In this research ,Undoped Nio and 1%Li doped Nio thin films were deposited utilizing chemical spray pyrolysis on the glass substrates heated (450C). The effects of non-thermal plasma on the structural and optical properties were studied. XRD measurement shows that Nio and Nio:1%Li films were found to be polycrystalline and have cubic structure with a preferred orientation (111). Decreased crystal size after exposure especially at (7) sec. AFM data indicate that the surface roughness average and (RMS) values of the prepared doped films are increasing after exposure to plasma, the transmittance increases after doped samples exposure to plasma, it was found that the energy gap value decreased when doped samples exposure to plasma, also, thickn

      Spray pyrolysis technique was subjected to synthesized (SnO₂)_1-x (TiO₂: CuO) _x Thin films on different substrates like glass and single crystal silicon using. The structure of the deposited films was studied using x-ray diffraction. A more pronounced diffraction peaks of SnO₂ while no peaks of (CuO , TiO₂ ) phase appear in the X-ray profiles by increasing of the content of (TiO₂ , CuO) in the sprayed films. Mixing concentration (TiO₂ , CuO) influences on the size of the crystallites of the SnO₂ films ,the size of crystallites of the spray paralyzed oxide films change in regular manner by increasing of (TiO

In this work; copper oxide films (CuO) were fabricated by PLD. The films were analyzed by UV-VIS absorption spectra and their thickness by using profilometer. Pulsed Nd:YAG laser was used for prepared CuO thin films under O₂ gas environment with varying both pulse energy and annealing temperature. The optical properties of   as-grown film such as optical transmittance spectrum, refractive index and energy gap has been measured experimentally and the effects of laser pulse energy  and annealing temperature on it were studied. An inverse relationship between energy gap and both annealing temperature and pulse energy was observed.

A new compounds of 2,4-substituted-1,3- thiazole containing amines [I] and [II], Schiff bases [IV] and [V], amides [VI]-[X],esters [XI] - [XIII], thiazolidinones [XIV]-[XVIII] and 1,3-oxazepines [XIX]-[XXV] were Synthesized and characterized by melting points, FTIR spectroscopy, elemental analysis, 1HNMR,13CNMR, dept135and Mass spectroscopy. The liquid crystalline properties of the synthesized compounds were verified by using hot-stage polarizing optical microscopy (POM) and differential scanning calorimeter (DSC). The compound [I] was found to be nematic textures (N). The first series of this study [II]n display only enantiotropic nematic phase when n=1-5 while the compounds with n =6-8 display two mesophasese smectic C(SmC) and nematic ph

The aim of the research is the detection of heavy metals using (Inductively coupled Plasma ICP) for samples in Tigris river at intakes of water treatment plants Baghdad (Sharq dejla, Al-Wathba, Al-Wahda, and Al-Dora) and samples at Tigris banks near (Al-Adhamya, Al-Shuhda bridge and al-Jadrya).
All the recorded results were fitted with Iraqi standers No. 25 in 1967 for all samples with heavy metals (arsenic Ar, Cadmium Cd, Chromium Cr, Zinc Zn, Lead Pb, Copper Cu, Nickel Ni, Manganese Mn, Ferrous Fe) where all concentration were lower than standard values except Cadmium (0.01- 0.014) in plants intakes and (0.027- 0.048) in river samples while the standard value is (0.005).
Other tests such as chemical oxygen demand and oil &

This work is focused on studying the effect of liquid layer level (height above a target material) on zinc oxide nanoparticles (ZnO and ZnO₂) production using liquid-phase pulsed laser ablation (LP-PLA) technique. A plate of Zn metal inside different heights of an aqueous environment of cetyl trimethyl ammonium bromide (CTAB) with molarity (10^-3 M) was irradiated with femtosecond pulses. The effect of liquid layer height on the optical properties and structure of ZnO was studied and characterized through UV-visible absorption test at three peaks at 213 nm, 216 nm and 218 nm for three liquid heights 4, 6 and 8 mm respectively. The obtained results of UV–visible spectra test show a blue shift accomp