The primary objective of this study was to identify the mechanisms for the development and propagation of longitudinal cracks that initiate at the surface of composite pavement. In this study the finite element program ANSYS version (5.4) was used and the model worked out using this program has the ability to analyze a composite pavement structure of different layer properties. Also, the aim of this study was modeling and analyzing of the composite pavement structure with the physical presence of crack induced in concrete underlying layer. The results obtained indicates that increasing the thickness of the asphalt layer tends to decrease the stress intensity factor, which may be attributed to the rapidly decrease of horizontal tensile stress in the asphalt layer. The cracks initiate at the surface due to high vertical stress and shear stress from wheel loads tends to propagate downward due tensile stress generated at the bottom of the asphalt layer or near crack tip, and the whole process occur at the same location of the existing cracks in underlying concrete layer rather than travel up from existing crack. As the load position varies from the crack zone, this result in tensile stresses or tension at the crack tip, leading to increase the stress intensity factor and intern result in crack propagation further into the depth of the pavement.
Aim: To evaluate the commercial pure titanium disks that structuring by laser in two design (dot and groove) each one with three different laser scan (5, 15 and 25) and comparing with titanium surface that not subjected to any surface structuring (control) through measuring the wettability test and surface roughness test. Materials and methods: Structuring on the surface of the commercial pure titanium (CP Ti) disks was performed via using fiber laser CNC machine in two design (dot and groove) in three different laser scans (5, 15 and 25), then the structuring disks analyzed with the control group by atomic force microscope and water contact angle test. Results: The results of this study showed that the surface roughness and the wettability
... Show MoreIn this work a flowsheet has been put for the recovery of uranium and plutonium from 2.5M nitric acid solutions using 17.5% tributyl phosphate (TBP) and 2.5% trioctylamine (TOA) in kerosene diluent . The fission products (resulting from irradiated of uranium samples in nuclear research reactor) were removed from the desired actinides U & Pu .The organic phase TBP/TOA/Kerosene, containing both actinides U&Pu were stripped using 0.1 M HNO3. Trioctylamine (2.5 volume ratio ) in mesitylene , has been used in conditions appropriate for the recovery of Pu . From the experiments done using mixer- settler , the concentration of uranium in the organic phase in such conditions was very low ,not exceeding parts of a million .
The actor has mechanisms that were applied in the performance، as it formed a style in the theatrical form (weird)، and the researcher deliberately studied these mechanisms and divided them into four chapters.
The researcher divided it into two sections، the first is the actor's performance requirements، and the second is the boring performance methods in the directors' theater، and then the researcher concluded the second chapter with the most important indicators.
As for the third chapter، the researcher determined the society of his research and the method of selecting the sample (strange) and analyzing the sample and concluded with the most important results of the sample analysis.
Objective: To determine the prevalence of Posttraumatic Stress Disorder (PTSD) among Iraqi repatriated
prisoners of Iran-Iraq war, and the relationship with demographic factors.
Methodology: A descriptive study was carried out from Oct. 18th, 2009 through Jan. 10th, 2010. A nonprobability
based snowball sampling technique was used to recruit 92 Iraqi repatriated prisoners of war
(IRPOWs) who had visited Ministry of Human Rights. A data collection instrument was constructed that
consisted of six demographic characteristics, and eight items to measure the level of PTSD in POWs. Data were
collected with the constructed instrument during a brief interview. Data were analyzed through the application of
descriptive statist
A novel demountable shear connector is proposed to link a concrete slab to steel sections in a way that resulting steel-concrete composite floor is demountable, i.e. it can be easily dismantled at the end of its service life. The proposed connectors consist of two parts: the first part is a hollow steel tube with internal threads at its lower end. The second part is a compatible partially threaded bolted stud. After linking the stud to the steel section, the hollow steel tube can be fastened over the threaded stud, which create a complete demountable shear connector. The connector is suitable for use in both composite bridges and buildings, and using cast in-situ slabs, precast solid slabs, or hollow-core precast slabs. A series of push-off
... Show More
(1)
(1)
To decrease the dependency of producing high octane number gasoline on the catalytic processes in petroleum refineries and to increase the gasoline pool, the effect of adding a suggested formula of composite blending octane number enhancer to motor gasoline composed of a mixture of oxygenated materials (ethanol and ether) and aromatic materials (toluene and xylene) was investigated by design of experiments made by Mini Tab 15 statistical software. The original gasoline before addition of the octane number blending enhancer has a value of (79) research octane number (RON). The design of experiments which study the optimum volumetric percentages of the four variables, ethanol, toluene, and ether and xylene materials leads
... Show More
(46)
(42)
The inhibitive action of polyvinyl alcohol –sodium nitrite (PVASN) composite on the corrosion of mild steel in simulated cooling water (SCW) has been investigated by weight loss and potentiodynamic polarization. The effect of composite concentration (PVA/SN) , pH, and exposure time on corrosion rate of mild steel were verified using 2 levels factorial design and surface response analysis through weight loss approach, while the electrochemical measurements were used to study the behavior of mild steel in (SCW) with pH between 6 and 8 and in absence and presence of (PVA) in solution containing different concentration of NaNO2. It was verified that all three main variables studied were statistically significant while their interaction is
... Show MoreAtmospheric residue fluid catalytic cracking was selected as a probe reaction to test the catalytic performance of modified NaY zeolites and prepared NaY zeolites. Modified NaY zeolites have been synthesized by simple ion exchange methods. Three samples of modified zeolite Y have been obtained by replacing the sodium ions in the original sample with lanthanum and the weight percent added are 0.28, 0.53, and 1.02 respectively. The effects of addition of lanthanum to zeolite Y in different weight percent on the cracking catalysts were investigated using an experimental laboratory plant scale of fluidized bed reactor.
The experiments have been performed with weight hourly space velocity (WHSV) range of 6 to 24 h
... Show MoreIn this work, an optical fiber biomedical sensor for detecting the ratio of the hemoglobin in the blood is presented. A surface plasmon resonance (SPR)-based coreless optical fiber was developed and implemented using single- and multi-mode optical fibers. The sensor is also utilized to evaluate refractive indices and concentrations of hemoglobin in blood samples, with 40 nm thickness of (20 nm Au and 20 nm Ag) to increase the sensitivity. It is found in practice that when the sensitive refractive index increases, the resonant wavelength increases due to the decrease in energy.
(6)
(5)