In this work, studying the effect of ethylenediamine as a corrosion inhibitor was investigated for carbon steel in aerated HCl solution in range of 0.1-1N under dynamic conditions, i.e., rotational velocity of 400–1200 rpm in the temperature range 35 – 65 ºC.  Weight loss method was employed in absence and presence of the inhibitor as an adsorption type in concentration range 1000 – 5000 ppm using rotating cylinder specimens. The experimental results showed that corrosion rate in absence and presence of inhibitor is increased with increasing temperature, rotational velocity and concentration of acid. It is decreased with increasing inhibitor concentration for the whole range of temperature, rotational velocity and concentrati

The study of the dynamic behavior of packed distillation column was studied by frequency response analysis using Matlab program. A packed distillation column (80 mm diameter) (2000 mm height) filled with glass packing (Raschig Rings 10mm), packing height (1500 mm) has been modified for separation of methanol-water mixture (60 vol%). The column dynamic behavior was studied experimentally under different step changes in, feed rate (±30%), reflux rate (±22%), and reboiler heat duty (±150%), the top and bottom concentration of methanol were measured. A frequency response analysis for the above step response was carried out using Bode diagram, the log modulus and the phase angle were  used to analyze the process model. A Matlab progra

The photodynamic inactivation against Methicillin-resistant Staphylococcus aureus using two different lasers, 532 nm diode pumped solid state laser (DPSS) in combination with safranin O and 650 nm diode laser in combination with methylene blue was investigated in the present work. A hundred swab samples were collected from patients with burn and wound infections admitted to two hospitals in Baghdad (Specialized Burns Hospital in Medical City and Al Imamein Al Jwadein Medical City Hospital) from December 2015 to February 2016 Antimicrobial susceptibility was performed by using Kirby- Bauer method. The irradiation experiments included four groups; a control group, a photosensitizer only group, a laser irradiation only group and a laser irr

content Analysis for Some Type of Pillows used in Iraqi houses

تحديدات مفاهيمية في التحليل السياسي

The composites were manufactured and study the effect of addition of filler (nanoparticles SiO2 treated with silane) at different weight ratios (1, 2, 3, 4 and 5) %, on electrical, mechanical and thermal properties. Materials were mixed with each other using an ultrasound, and then pour the mixture into the molds to suit all measurements. The electrical characteristics were studied within a range of frequencies (50-1M) Hz at room temperature, where the best results were shown at the fill ratio (1%), and thermal properties at (X=3 %), the mechanical properties at the filler ratio (2%).

In this research a study of the effect of quality, sequential and directional layers for three types of fibers are:(Kevlar fibers-49 woven roving and E- glass fiber woven roving and random) on the fatigue property using epoxy as matrix. The test specimens were prepared by hand lay-up method the epoxy resin used as a matrix type (Quick mast 105) in prepared material composit . Sinusoidal wave which is formed of variable stress amplitudes at 15 Hz cycles was employed in the fatigue test ( 10 mm )and (15mm) value 0f deflection arrival to numbers of cycle failure limit, by rotary bending method by ( S-N) curves this curves has been determined ( life , limit and fa

ABSTRACT: Thin film of CdS has been deposited onto clean glass substrate by using Spray pyrolysis technique. Results of Morphological (AFM) studied; electrical properties and optical conductivity studied are analysis. AFM results show a crystalline nature of the films. From the conductivity measurement at different temperatures, the activation energy of the films was calculated and found to be between 0.188 - 0.124 eV for low temperature regions, and between 1.67-1.19eV for high temperature regions. Hall measurements of electrical properties at room temperature show that the resistivity and mobility of CdS polycrystalline films deposited at 400 C0, were 3.878x103 . cm and 1.302x104cm2/ (V.s), respectively. The electrical conductivity of th

In this work Nano crystalline (Cu2S) thin films pure and doped 3% Al with a thickness of 400±20 nm was precipitated by thermic steaming technicality on glass substrate beneath a vacuum of ~ 2 × 10− 6 mbar at R.T to survey the influence of doping and annealing after doping at 573 K for one hour on its structural, electrical and visual properties. Structural properties of these movies are attainment using X-ray variation (XRD) which showed Cu2S phase with polycrystalline in nature and forming hexagonal temple ,with the distinguish trend along the (220) grade, varying crystallites size from (42.1-62.06) nm after doping and annealing. AFM investigations of these films show that increase average grain size from 105.05 nm to 146.54 nm