In the present work, pulsed laser deposition (PLD) technique was applied to a pellet of Chromium Oxide (99.999% pure) with 2.5 cm diameter and 3 mm thickness at a pressure of 5 Tons using a Hydraulic piston. The films were deposited using Nd: YAG laser λ= (4664) nm at 600 mJ and 400 number of shot on a glass substrate, The thickness of the film was (107 nm). Structural and morphological analysis showed that the films started to crystallize at annealing temperature greater than 400 oC. Absorbance and transmittance spectra were recorded in the wavelength range (300-
4400) nm before and after annealing. The effects of annealing temperature on absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of d

This paper aims to investigate the flexural behavior of reinforced concrete beams considering fire resistance by adding Lightweight Expanded Clay Aggregates (LECA) to the concrete mix as partial coarse aggregate replacement. LECA is a type of porous clay with a uniform pore structure with fine, closed cells and hard, tightly sintered skin. The experimental work comprised four reinforced self-compacted concrete beams. All the specimens were identical in their geometrical layout of 1600×240×200 mm, reinforcement details, and support condition (simply supported). For all the beams, the main reinforcement was provided by two bars, each having a diameter of 12 mm, while a bar of 6 mm diameter was employed for the top and shear reinforc

Symmetric cryptography forms the backbone of secure data communication and storage by relying on the strength and randomness of cryptographic keys. This increases complexity, enhances cryptographic systems' overall robustness, and is immune to various attacks. The present work proposes a hybrid model based on the Latin square matrix (LSM) and subtractive random number generator (SRNG) algorithms for producing random keys. The hybrid model enhances the security of the cipher key against different attacks and increases the degree of diffusion. Different key lengths can also be generated based on the algorithm without compromising security. It comprises two phases. The first phase generates a seed value that depends on producing a rand

Objective Advantageous properties of silicone elastomer made it one of the favorable materials in maxillofacial prosthesis construction, but these properties may change after months of usage or after pigments addition. This study aimed to define the optimum concentration for a mixture of two types of intrinsic pigments that added to VST-50 maxillofacial silicone material and study their effects on mechanical properties before and after artificial aging. Methods After the pilot study was conducted, 0.1% by weight of rayon flocking and 0. 2% by weight of burnt sienna intrinsic pigment concentration was selected because of improvement in tested mechanical properties of VST-50 maxillofacial silicone. A total of one hundred and eighty samples we

   This study, which is considered the first of its kind in the world and the Arab homeland, was carried out in the laboratory of mushroom production belonging to the Medicinal Plant Unit/ College Of Agricultural Engineering Sciences/ University of  Baghdad during the period from July 21, 2016, to December 30, 2018, aiming to isolate and purify the mycelium of the wild isolation in addition to the genetic and morphological identification of the mushroom Agaricus bellaniae. The obtained pure isolation was tagged in the American National Center for Biotechnology Information (NCBI) with symbol MF987843.1, thus Iraq would be the second country in the world in which the mushroom is grown following the United States of America. The

      Using three-point bending experiments,  the effect of the particle size of SiO₂ on the flexural properties of epoxy composites was investigated. Young modulus and flexural strength were studied for different weight percentage of filler  (2,4,6,8 and 10) wt%.The size of SiO₂ particles varied from micro (100um) to nano (12nm) .

Flexural strength and  Young modul were found to increase with the filler content, but when the particle size decreased to the nanoscale, the  Young module  increased. Flexural strength was higher for microcomposites than nanocomposites.

In this study, polyester composites reinforced with pistachio shells powder (P.) with an average
diameter (150 – 200 μm) with different weight ratios (0.5%, 1%, 1.5%, 2%, and 2.5%) were
prepared to the resin. The Shore D hardness, thermal conductivity (K), and the glass transition
temperature (Tg) of the samples were examined. The results showed that the Shore D hardness
increases with the increase of the reinforcement ratio and its maximum value is (87.55) at (2.5%
P.) While the value of hardness at (0%) is (86.5). The thermal conductivity increases slightly with
the increase in the percentage of reinforcement and its maximum value is (0.213253 W/ m. K) at
(2.5% P.), while the value of K at (0% P.)

Polycaprolactone polymer is widely used in medical applications due to its biocompatibility. Electro spinning was used to create poly (ε- caprolactone) (PCL) nanocomposite fiber mats containing hydroxyapatite (HA) at concentrations ranging from 0.05 to 0.4% wt. The chemical properties of the fabricated bio composite fibers were evaluated using FTIR and morphologically using field-emission scanning-electron microscopy (FESEM), Porosity, contact angle, as well as mechanical testing(Young Modulus and Tensile strength) of the nanofibers were also studied. The FTIR results showed that all the bonds appeared for the pure PCL fiber and the PCL/HA nano fibers. The FESEM nano fiber showed that the fiber diameter increased from 54.13 to 155.79 (n