The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burnt under (1200)°C temperatures according to a burning program which raised the temperature (5)°C per minute and then the soaking interval. Some tests such as the physical, mechanical and thermal test were connected on the testing results for the specimens indicated that the raw materials with fine size range and high temperature gave specimens a thermal phase with higher percent of Mullit in comparison with coarse size. Bulk density values, coefficient of longitudinal and hardness increase with porosity and ratio of water absorption values decrease. Also, results show that Alumina with Bauxite gives it stiffens because of the increase of the mullite phase which is characterized by high mechanical and thermal properties especially thermal conductivity. Results show that the best thermal and mechanical properties are found in the fifth mixture (X5) which contains a ratio of about (10) % of Al2O3 .
In present work, new tetra-dentate ligand, titled 3,5-bis ((E)-5-Bromo-2-hydroxy benzylidene amino) benzoic acid (H3L), was prepared via an acid-catalyzed condensation process. New four metallic ligand complexes with Co(II), Ni(II), Cu(II) and Zn(II) ions, were also prepared from the refluxing of equivalent moles. Ligand's structure and its complexes; were confirmed by numerous characterization methods, including Ultraviolet-Visible, Infrared, Mass Spectrometer, 1H and 13C Nuclear Magnetic Resonance spectra, atomic absorption, magnetic moments, and molar conductivity measurements. The results of the spectroscopic analyzes proved that the prepared ligand acts as tetradentate bi-ionic ligand and it was bond
... Show More
(7)
(1)
Objectives: to compare health of mothers and neonatal among age groups, to find out the correlation between
age groups and mother and neonatal health.
Methodology: A descriptive study was carried out at delivery rooms of three teaching hospitals in Baghdad city
from Feb. 28th through May. 28th
, 2013. A purposive (non-probability) sample of 300 laboring women was selected
from delivery rooms categorized into three groups, group 1 (≤19) years, group 2 their age between (20-35) years
old and group 3 their age (≥35) years. The data were collected through the use of constructing questionnaire, an
interview technique with mothers and reviewing their medical records as means of data collection; The
questionnaire con
The current article focuses on studying the social organization reality of the Iraqi society; it aims to construct an Iraqi organized personality that believe in the principles of Islamic religion by making use of the sociology thoughts in explaining the strength of social organization, and the causes of social deviance in attempt of decreasing the deviance and strengthening the cohesion of Iraqi character.
The researchers put forward some questions: to what extent the western theoretical pattern can succeed in explaining the social organization of the Iraqi society? What is the more appropriate western theory for diagnosing the cohesion and deviance of the society? What is the s
... Show More
(15)
(12)
Nano gamma alumina was prepared by double hydrolysis process using aluminum nitrate nano hydrate and sodium aluminate as an aluminum source, hydroxyle poly acid and CTAB (cetyltrimethylammonium bromide) as templates. Different crystallization temperatures (120, 140, 160, and 180) 0C and calcinations temperatures (500, 550, 600, and 650) 0C were applied. All the batches were prepared at PH equals to 9. XRD diffraction technique and infrared Fourier transform spectroscopy were used to investigate the phase formation and the optical properties of the nano gamma alumina. N2 adsorption-desorption (BET) was used to measure the surface area and pore volume of the prepared nano alumina, the particle size and the
... Show MoreNano gamma alumina was prepared by double hydrolysis process using aluminum nitrate nano hydrate and sodium aluminate as an aluminum source, hydroxyle poly acid and CTAB (cetyltrimethylammonium bromide) as templates. Different crystallization temperatures (120, 140, 160, and 180) 0C and calcinations temperatures (500, 550, 600, and 650) 0C were applied. All the batches were prepared at PH equals to 9. XRD diffraction technique and infrared Fourier transform spectroscopy were used to investigate the phase formation and the optical properties of the nano gamma alumina. N2 adsorption-desorption (BET) was used to measure the surface area and pore volume of the prepared nano alumina, the particle size and the morphology of the surface of
... Show More
(3)
Ceramic to metal joining technique, which was used in this investigation includes the use of active filler alloy as a sandwich between the alumina and kovar alloy for brazing. High purity powdered metals of silver, copper, and additives of titanium were used to prepare the active filler alloy, through compacting the mixed powders and alloying in a furnace with argon atmosphere at the temperature of 800oC for 10 minutes. To use it as an active filler metal, it has been modified to a proper thickness. Two groups of alumina were prepared with different sintering temperatures (1450oC and 1650oC) and each group was tested under atmospheric pressure, vacuum furnace pressure of 2*10-4 torr and vacuum furnace pressure of 2*10-6 torr. All the pro
... Show More
(2)
(2)
In recent years, there has been a rapid development in research on high performance ceramics for mechanical, electrical and medical industries. This development will be shown for alumina as a representative for oxide ceramics powders.
Dry–pressing forming technique was used to prepare different ceramic compacts for alumina grafted by polymethacrylate polymers. All Alumina compact were fired firstly at 1200 ◌ْ C, then
at 1600 ◌ْ C.
Mechanical strength was examined in different means, some
depends on compression and other depends on impact. Hardness was
also measured .The results obtained were compared with that of
Alumina compact prepared under the same condition from Alumina
especially made for pressing .
the mental image is so important in human life as one of the major standers for his trends and behavior, and as the human nature requires to interest in things based on how much it’s close to and how much it effects on his interest, So the neighborhood countries was one of the topics that occupied the attention of the Iraqi individual and pushed him to form perceptions of them based on the cultural heritage and the historical relations of Iraq with these countries as well as the actions of neighboring countries on Iraq and the resulting effects on the course of events. the mental image is so important in human life as one of the major standers for his trends and behavior, and as the human nature requires to interest in things bas
... Show More