The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burnt under (1200)°C temperatures according to a burning program which raised the temperature (5)°C per minute and then the soaking interval. Some tests such as the physical, mechanical and thermal test were connected on the testing results for the specimens indicated that the raw materials with fine size range and high temperature gave specimens a thermal phase with higher percent of Mullit in comparison with coarse size. Bulk density values, coefficient of longitudinal and hardness increase with porosity and ratio of water absorption values decrease. Also, results show that Alumina with Bauxite gives it stiffens because of the increase of the mullite phase which is characterized by high mechanical and thermal properties especially thermal conductivity. Results show that the best thermal and mechanical properties are found in the fifth mixture (X5) which contains a ratio of about (10) % of Al2O3 .
In this work, varying compositions of SiO2 micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO2/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.
This research aims to understand complexity management and its impact on the use of the dynamic capabilities of a sample of private colleges. Private colleges are currently facing many crises, changes, unrest and high competitive pressures. Which is sometimes difficult or even impossible to predict. The recruitment of dynamic capabilities is also one of the challenges facing senior management at private colleges to help them survive and survive. Thus, the problem of research was (there is a clear insufficiency of interest in Complexity Management and trying to employ it in improving the dynamic capabilities of Colleges that have been discussed?). A group of private colleges was selected as a
... Show More
The effect of micro-and nano silica particles (silica SiO2 (100 μm), Fused silica (12nm)) on some mechanical properties of epoxy resin was investigated (Young's modulus, Flexural strength). The micro-and nano composites were prepared by using three steps process with different volume fraction of micro-and nano particles (1, 2, 3, 4, 5, 7, 10, 15, and 20 vol. %). Flexural strength and Young's modulus of nano composites were increased at low volume fraction (max. enhancement at 4 vol.% ). However at higher volume fraction both Young's modulus and flexural strength decrease. Moreover, above, the mechanical properties are enhanced more than that of neat epoxy resin. The flexural strength decreases with increasing the volume fraction of micr
... Show More
(6)
(5)
the structrual and mechanical properties of thin Ni films of different thicknesses deposited on coring glass substrate using lonbeam sputtering(IBS) technique under vacuum torr have been studied the TEM and electron
Nanoparticles of copper sulfide have been prepared by simple reaction between using copper nitrate with different concentrations ratio 0.1, 0.3, and 0.5 mM, thiourea by a simple chemical route. The prepared Nano powders have been deposited onto glass substrates by casting method at 60°C. The structure of the product Nano- films has been studied by x-ray diffraction, where the patterns showed that all the samples have a hexagonal structure of covellite copper sulfide with the average crystalline sizes 14.07- 16.51 nm. The morphology has been examined by atomic force microscopy, and field emission scan electron microscopy. The AFM images showed particles with almost spherical and rod shapes with average diameter sizes of 49.11- 90.64 nm.
... Show More
(10)
The rental activity receives "significant" interest from accounting organizations interested in issuing accounting standards worldwide, such as the Financial Accounting Standards Board (FASB), the International Accounting Standards Board (IASB). As leases represents an important source of finance for economic units as an alternative to financing assets through purchase or borrowing. Professional organizations have focused on addressing the situation of extra-budgetary funding through which the lessee hides many leases that are classified as financing without It shows in the budget, which gives an incorrect picture of the reality of the financial situation of economic unity, IASB has issued IFRS 16, which terminates off- Balance s
... Show More
(24)
(20)
(31)
An Investigation of estimated Mechanical Properties of AL-Alloys 2024-T3, which is the most commonly used in industrial applications, been established experimentally. A new novel Plasma Peening techniques had applied for the whole surfaces of the material by CNC-Plasma machine for 48 specimen, and then a new investigation were toke over to figure the amount of change in mechanical properties and estimated fatigue life. It found that improvement was showing a nonlinear behavior according to peening duration time, speed, peening distance, peening number, and amount of effected power on the depth of the material thickness. The major improvement was at medium speed long duration time normal peening distance. Which shows up t
... Show More