The current study aimed to investigate the viability of biofilm formation klebsilla pneumoniae and Staphylococcus aureus. 440 urine samples were collected from patients suffering from urinary tract infection (UTI) from those who were admitted and visitors to Al-Ramadi Teaching Hospital, Al-Yarmouk Teaching Hospital, Al-Ramadi Teaching Hospital for women and children and , Teaching Laboratories in the Medical City for both genders for a period extended from 5 July, 2017 to 10 October, 2017. Samples were diagnosed by culturing them on a selective media and by biochemical testes , also, diagnosis was ensured by using VITEK-2 compact system. Results showed that K.pneumoniae isolation ratio was 17.1%(68) and S.aureus ratio was 13.1%(52). Thei

Silver/polyvinyl alcohol (Ag/PVA) nanocomposite films were synthesized via solution casting with varying concentrations of Ag nanoparticles (1–5 wt%). A comprehensive investigation was conducted to understand the influence of Ag content on the structural, optical, mechanical, thermal, electrical, and antibacterial properties of the composites. UV-Vis spectroscopy revealed a red shift in absorption peaks and a reduction in the optical band gap, which decreased from 3.78 eV for pure PVA to 3.37 eV for the 5 wt% Ag composite. FTIR and SEM analyses confirmed successful nanoparticle incorporation and morphological changes. The nanocomposites exhibited enhanced tensile strength, elongation at break, Young’s modulus, and hardness due t

Brainstorming is considered as one of the manners that develop learners' mental abilities. Besides, it can help learners get a lot of ideas and thoughts. And by following applied steps to answer the problem concerned, the researcher carried out this practical study aimed at:Developing the ideas of design of third year students/Institute of Fine Arts/Evening Studies- Baghdad/First Rusafa by employing Brainstorming mechanism to develop the ideas of design of institute students in designing the technical advertisement and to achieve the authenticity of the goal of the research, Department of Plastic Arts/Institute of Fine Arts/Evening Studies/Baghdad-First Rusafa was chosen as a case study for the research. It embraced (20) students who rep

Preparation of superposed thin film (CdTe)1-xSex / ZnS) with concentration of (x= 0.1, 0.3, 0.5) at a temperature of substrate (Ts= 80 0C) by using Thermal Vacuum Evaporation System. The measurement of X-ray diffraction shows that the compounds CdTe, ZnS, (CdTe)1-xSex and (CdTe)1-xSex / ZnS have a polycrystalline structure, the C-V characteristic shows that the capacitance degrease by increasing the concentration (x) in reverse bias, while the I-V characteristic shows the current dark (Id) increase in forward and reverse bias by increasing (x) and the photocurrent (Iph) increase in reverse bias by increasing the concentration (x), the values of photocurrent are greater than from the values of the dark current for all concentrations

High temperature superconductors materials with composition Bi1.6-xSbxPb0.4Sr2Ca2-yCdyCu3OZ (x = 0, 0.1, 0.2 and 0.3) and (y = 0.01 and 0.02), were prepared by using the chemical reaction in solid-state ways, and test influence of partial replacement of Bi and Ca with Sb and Cd respectively on the superconducting properties, all samples were sintered at the same temperature (850 oC) and for the same time (195 h). The structural analysis of the prepared samples was carried out using X-ray diffraction (XRD) measurements performed at room temperature, scanning electron microscope (SEM) and dc electrical resistivity was measured as a function of temperature. It was found that the sample prepared by partial substitution of Sb at ratio (x= 0.2

      Spray pyrolysis technique was subjected to synthesized (SnO2)1-x (TiO2: CuO) x Thin films on different substrates like glass and single crystal silicon using. The structure of the deposited films was studied using x-ray diffraction. A more pronounced diffraction peaks of SnO2 while no peaks of (CuO , TiO2 ) phase appear in the X-ray profiles by increasing of the content of (TiO2 , CuO) in the sprayed films. Mixing concentration (TiO2 , CuO) influences on the size of the crystallites of the SnO2 films ,the size of crystallites of the spray paralyzed oxide films change in regular manner by increasing of (TiO2 , CuO) amount. The effect of mixing concentration on the optical properties of the films was also investigated. The

      Spray pyrolysis technique was subjected to synthesized (SnO₂)_1-x (TiO₂: CuO) _x Thin films on different substrates like glass and single crystal silicon using. The structure of the deposited films was studied using x-ray diffraction. A more pronounced diffraction peaks of SnO₂ while no peaks of (CuO , TiO₂ ) phase appear in the X-ray profiles by increasing of the content of (TiO₂ , CuO) in the sprayed films. Mixing concentration (TiO₂ , CuO) influences on the size of the crystallites of the SnO₂ films ,the size of crystallites of the spray paralyzed oxide films change in regular manner by increasing of (TiO