Mechanical Properties of MIG Joints for Dissimilar Aluminum Alloys
...Show More Authors

The research aims to investigate the effects of GMAW or MIG welding process on the mechanical properties of dissimilar aluminum alloys 2024-T351 and AA 6061- T651. A series of experimental techniques have been conducted to evaluate mechanical properties of the alloys, by carrying out hardness, tensile and bending tests for welded and un-welded specimens.

Metal inert gas (MIG) has been carried out on sheet metal using ER- 4043(AlSi5) as a filler metal and argon as shielded gas. The welded joints were tested by X-ray radiography and Faulty pieces were excluded.

Welding joints without defects are subjected to heat treatment including heating the joints in furnace to 170 °C for half an hour then air cooling to relief welding stress.

Tensile test was implemented for all specimens which prepared in the dimensions according to ASTM 17500 by using Testing machine smart series with preload value 100 kN. Vickers hardness test and microstructure examination were made, the last test was bending test which implemented on the welded and un welded specimens which machined into standard test specimen dimensions.

Results of mechanical properties Using MIG welding process appear a general decay compared with un welded and in the dissimilar joint comparing with parent metal that is due to the microstructure change during the welding process. The location of the failure for welded specimens after all mechanical test was found predominantly along the heat affected zone ( HAZ ).but Unwedded specimens were failed near the center line of the specimen.  

View Publication Preview PDF
Quick Preview PDF
Publication Date
Thu Dec 31 2015
Journal Name
Al-khwarizmi Engineering Journal
Effect of Acetic Acid on Electrochemical Behavior of Sealed AA2319-T3 Al-Alloys Anodized in Phosphoric Acid Electrolytes
...Show More Authors

Abstract

      The present study investigates the effect of acetic acid on corrosion behavior and its potential of hydrothermally sealed anodized AA2319-Al-alloys. Anodizing treatment was performed in stagnant phosphoric acid electrolyte with or without addition of acetic acid. Hydrothermal sealing was carried out in boiling water for each anodized specimen. The open circuit potential of the unsealed and sealed anodized samples was examined using open circuit potential measurement for the purpose of starting in scanning polarization diagrams. The potentiostatic polarization technique measurements were performed to assess corrosion behavior and sealing quality (i.e., degree of sealing) of

... Show More
View Publication Preview PDF
Publication Date
Sat Oct 28 2023
Journal Name
Baghdad Science Journal
Effect of Green-biosynthesis Aluminum Nanoparticles (Al NPs) on Salmonella enterica Isolated from Baghdad City
...Show More Authors

This study is aimed to Green-synthesize and characterize Al NPs from Clove (Syzygium aromaticum
L.) buds plant extract and to investigate their effect on isolated and characterized Salmonella enterica growth.
S. aromaticum buds aqueous extract was prepared from local market clove, then mixed with Aluminum nitrate
Al(NO3)3. 9 H2O, 99.9% in ¼ ratio for green-synthesizing of Al NPs. Color change was a primary confirmation
of Al NPs biosynthesis. The biosynthesized nanoparticles were identified and characterized by AFM, SEM,
EDX and UV–Visible spectrophotometer. AFM data recorded 122nm particles size and the surface roughness
RMs) of the pure S. aromaticum buds aqueous extract recorded 17.5nm particles s

... Show More
View Publication Preview PDF
Scopus (2)
Crossref (1)
Scopus Crossref
Publication Date
Sat Jul 01 2023
Journal Name
Journal Of Taibah University Medical Sciences
Impact of nano-cellulose fiber addition on physico-mechanical properties of room temperature vulcanized maxillofacial silicone material
...Show More Authors

Objectives: Maxillofacial silicone is used to restore abnormalities due to congenital or acquired causes. However, the quality of silicone is far from ideal. This study was aimed at assessing the influence of the addition of cellulose nanofibers (CNFs; several nanometers wide and 2-5 micro m long) on the physical and mechanical characteristics of maxillofacial silicone elastomers. Methods: Two CNF weight percentages (0.5% and 1%) were tested, and 180 specimens were divided into one control and two experimental groups. Each group was subdivided into six subgroups. In each subgroup, ten specimens subjected to each of the following tests: tearing strength, Shore-A hardness, tensile strength, elongation percentage, surface roughness, and color

... Show More
View Publication
Scopus (1)
Crossref (1)
Scopus Clarivate Crossref
Publication Date
Fri Mar 30 2018
Journal Name
Journal Of Pure And Applied Microbiology
The Effect of Polyester Fibers Addition on Some Mechanical Properties of Room Temperature Vulcanized Maxillofacial Silicon Elastomers
...Show More Authors

View Publication
Scopus (1)
Crossref (1)
Scopus Crossref
Publication Date
Mon Nov 14 2022
Journal Name
Journal Of Reinforced Plastics And Composites
Effect of phosphoric acid molarity on the structural, thermal, mechanical, and electrical properties of polyimide/polyaniline nanocomposites
...Show More Authors

In this paper, we used two monomers, 3,3',4,4'-benzophenone tetracarboxylic dianhydride (BTDA) and m,m'-diaminobenzophenone (m, m’-DABP), to produce polyamide acid and then converted it to polyimide (PI). The effects of phosphoric acid (H3PO4) molarity (1, 2, and 3 M) on the structural, thermal, mechanical, and electrical characteristics of the polyimides/polyaniline (PI/PANI) nanocomposites were studied. Two sharp reflection peaks were developed by the addition of PANI to PI. When 3 M H3PO4 is added, the crystalline sharp peak loses some of its intensity. The complex formation of PI/PANI-H3PO4 was confi

... Show More
View Publication
Scopus (11)
Crossref (10)
Scopus Clarivate Crossref
Publication Date
Mon Apr 03 2023
Journal Name
Polymer Composites
Effect of silver nanoparticles on structural, thermal, electrical, and mechanical properties of poly(vinyl alcohol) polymer nanocomposites
...Show More Authors

View Publication
Scopus (24)
Crossref (26)
Scopus Clarivate Crossref
Publication Date
Tue Aug 06 2024
Journal Name
Fullerenes, Nanotubes And Carbon Nanostructures
Preparation and characterization of PVA/MWCNT nanocomposites: a composition dependence study of structural, optical and mechanical properties
...Show More Authors

View Publication
Scopus (1)
Crossref (2)
Scopus Clarivate Crossref
Publication Date
Wed Jun 01 2022
Journal Name
Iraqi Journal Of Physics
Enhanced Mechanical Property of Acrylic Polymer/Graphene/Carbon Fibers Hybrid for Water Proof Coating
...Show More Authors

In this work, some mechanical properties of the polymer coating were improved by preparing a hybrid system containing Graphene (GR) of different weight percentages (0.25, 0.5, 1, and 2wt%) with 5wt% carbon fibres (CF) and added to a polymer coating by using casting method. The properties were improved as GR was added with further improvement on adding 5wt% of CF. The impact strength of acrylic polymer with GR increases with increasing weight ratio‏‏ of GR; maximum value was obtained when the polymer coating was incorporated with 1wt% GR and 5wt% CF. The impact strength of acrylic polymer with GR and GR/CF composites incorporated with GR at 1wt% and CF at 5wt%. Hardness increase with increasing weight ratio of Gr and a significant imp

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Tue Jul 01 2025
Journal Name
South African Journal Of Chemical Engineering
Expired azithromycin and cephalexin as corrosion inhibitors for aluminum in saline-acidic solution
...Show More Authors

View Publication
Scopus Clarivate Crossref
Publication Date
Sat Jan 20 2024
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
The Effect of Partial Substitution of Ge-S-Cd Alloys on the Density of Energy States
...Show More Authors

Five samples of the ternary alloy Ge-S-Cd were created using the melting point method, and the effects of partially substituting cadmium for germanium were determined. and partial substitution of germanium by cadmium was used to study the change in electrical conductivity. Electrical experiments were performed on Ge35-xS65Cdxternary alloy with x = 0, 5, 10, 15, and 20. It was discovered that the conductivity (σdc) rises with rising temperature in all samples under experiment. This confirms that the samples have semiconductor behavior. It has been observed that there are three regions of electrical conductivity in the electrical conductivity curve at low, moderate, and high temperatures. The pr

... Show More
View Publication
Crossref