Thin films of CdS:Cu were deposited onto glass substrate temperature 400 °c. The optieal properties have been studied for Cds doped with (1,3, 8) wt% of Cu before and after Gamma irradiation. It was found that the irradiation caused an ( Frenkel defects) where the atom is displaced from its original site leaving vacancy and forming on interstitial atom. It was found the irradiation caused an absorption edge shifting towards long wavelength as a result of the increasing of Cu concentration.

Porous silicon (P-Si) has been produced in this work by photoelectrochemical (PEC) etching process. The irradiation has been achieved using diode laser of (2 W) power and 810 nm wavelength. The influence of various irradiation times on the properties of P-Si material such as P-Si layer thickness, surface aspect, pore diameter and the thickness of walls between pores as well as porosity and etching rate was investigated by depending on the scanning electron micrograph (SEM) technique and gravimetric measurements.

Research in Iraq has expanded in the field of material technology involving the properties of the lightweight concrete using natural aggregate. The use of the porcelinate aggregate in the production of structural light concrete has a wide objective
and requires a lot of research to become suitable for practical application. In this work metakaolin was used to improve compressive strength of lightweight porcelinate concrete which usually have a low compressive strength about 17 MPa . The effect of metakaolin on compressive, splitting tensile, flexure strengths and modulus of elasticity of lightweight porcelinate concrete have been investigated. Many experiments were carried out by replacing cement with different percentages of
met

Pure nano Ferro fluid was synthesized by chemical co-precipitation method. The composite of polyaniline with nano sized Ferro fluid was prepared by In-situ–chemical oxidation polymerization method with ammonium per sulphate as an oxidant in aqueous hydrochloric acid under constant stirring at room temperature. The optical properties, absorption, transmission, optical energy gap (Eg) and optical constant refractive index (n) have been investigated. The value of the Eg decreased with increasing Ferro fluid concentration.

A field experiment was conducted at Abu-Ghrib during 2013- 2014 season to study the effect of harrowing systems on the decomposition and fermentation on organic matter(OM) when added and mixed with the soil under special technology, as well as its effect on the growth parameters and productivity of (Zea mays L. 5018). The experiment was laid out using factorial randomized complete block design (RCBD) in split-split design with three replications in SCL bare soil with a percent of moisture ranged from 16 – 18 %. The main plots were designated to the two systems of harrowing (Rotary Harrowand Disc Harrow ). The sub main plots were specified for two organic matters ( Sheep manure ,cow manure ) . Data were statistically analyzed, and

Semi-empirical methods were applied for calculating the vibration frequencies and IR absorption intensities for normal coordinates of the {mono (C₅₆H₂₈), di (C₈₄H₂₈), tri (C₁₁₂H₂₈) and tetra (C₁₄₀H₂₈)} -rings layer for (7,7) armchair single wall carbon nanotube at their equilibrium geometries which were all found to have D₇d symmetry point group.

Assignment of the modes of vibration (3N-6) was done depending on the pictures of their modes by applying (Gaussian 03) program. Comparison of the vibration frequencies of (mono, di, tri and tetra) rings layer which are active in IR, and inactive in Ramman spectra. For C-H stretching vibrat

Thin films of Mn2O3 doped with Cu have been fabricated using the simplest and cheapest chemical spray pyrolysis technique onto a glass substrate heated up to 250 oC. Transmittance and absorptance spectra were studied in the wavelength range (300 -1100) nm. The average transmittance at low energy was about 60% and decrease with Cu doping, Optical constants like refractive index, extinction coefficient and dielectric constants (εr), (εi) are calculated and correlated with doping process.

Using photo electrochemical etching technique (PEC), porous silicon (PS) layers were produced on n-type silicon (Si) wafers to generate porous silicon for n-type with an orientation of (111) The results of etching time were investigated at: (5,10,15 min). X-ray diffraction experiments revealed differences between the surface of the sample sheet and the synthesized porous silicon. The largest crystal size is (30 nm) and the lowest crystal size is (28.6 nm) The analysis of Atomic Force Microscopy (AFM) and Field Emission Scanning Electron Microscope (FESEM) were used to research the morphology of porous silicon layer. As etching time increased, AFM findings showed that root mean square (RMS) of roughness and po