Fiber reinforced polymer composite is an important material for structural application. The diversified application of FRP composite has taken center of attraction for interdisciplinary research. However, improvements on mechanical properties of this class of materials are still under research for different applications. In this paper we have modified the epoxy matrix by Al₂O₃, SiO₂ and TiO₂ nano particles in glass fiber/epoxy composite to improve the mechanical and physical properties. The composites are fabricated by hand lay-up method. It is observed that mechanical properties like flexural strength, hardness are more in case of SiO₂ modified epoxy composite compare to other nano

The physical, the thermal and the mechanical properties of Nano-composites, that consisted of Polyprime EP epoxy that reinforced by multi-walled carbon nanotubes (MWCNTs), have been studied. Various loading ratios, 0.1, 0.5, and 1 wt. %of MWCNT shave been infused into epoxy by a magnetic stirrer and then the hardener mixed with the mthat supplied with the epoxy. All sample shave been cutting using CNC machine. Tensile test, three-point bending, hardness tests, lee's disk, differential scanning calorimetry, water absorption and dielectric and electrical conductivity test were utilized on unfilled, MWCNT-filled epoxy to identify the loading effect on the properties of materials. Scanning electron microscopy (SEM) was used to determine the

 In the current study, the definition of mapping of fuzzy neutrosophic generalized semi-continuous and fuzzy neutrosophic alpha has generalized mapping as continuous. The study confirmed some theorems regarding such a concept. In the following, it has been found relationships among fuzzy neutrosophic alpha generalized mapping as continuous, fuzzy neutrosophic mapping as continuous, fuzzy neutrosophic alpha mapping as continuous, fuzzy neutrosophic generalized semi mapping as continuous, fuzzy neutrosophic pre mapping as continuous and fuzzy neutrosophic γ mapping as continuous.

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed re

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed reactor

This research studies the effect of addition of some nanoparticles
(MgO, CuO) and grain size (30,40nm) on some physical properties
(impact strength, hardness and thermal conductivity) for a matrix
blend of epoxy resin with SBR rubber. Hand –Lay up method was
used to prepare the samples. All samples were immersed in water for
9 weeks.
The Results showed decreased in the values of impact strength and
hardness but increased the coefficient of thermal conductivity.

In the present study, composites were prepared by Hand lay-up molding and investigated. The composites constituents were epoxy resin as the matrix, 6% volume fractions of Glass Fibers (G.F) as reinforcement and 3%, 6% of industrial powder (Calcium Carbonate CaCO₃, Potassium Carbonate K₂CO₃ and Sodium Carbonate Na₂CO₃) as filler. Density, water absorption, hardness test, flexural strength, shear stress measurements and tests were conducted to reveal their values for each type of composite material. The results showed that the non – reinforced epoxy have lower properties than composites material. Measured density results had show an incremental increase with volume fraction increase