Effect of nano and micro SiO2 particles with different weight percent (2,4,6,8 and 10) %wt on the Interlaminar fracture toughness (GIc) of 16-plies of woven roving glass fiber /epoxy composites prepared by hand lay – up technique were investigated. The specimens were tested using DCB test (mode I).
Area method was used to compute the interlaminar fracture toughness. The results show that, GIc would increase with the increasing in the filler content, the main failure in microcomposites and nanocomposites was delamination in the layers, the delamination reduced with increasing in the filler content.

This research studies the effect of adding micro, nano and hybrid by ratio (1:1) of (Al2O3,TiO2) to epoxy resin on thermal conductivity before and after immersion in HCl acid for (14 day) with normality (0.3 N) at weight fraction (0.02, 0.04, 0.06, 0.08) and thickness (6mm). The results of thermal conductivity reveled that epoxy reinforced by (Al2O3) and mixture (TiO2+Al2O3) increases with increasing the weight fraction, but the thermal conductivity (k) a values for micro and Nano (TiO2) decrease with increasing the weight fraction of reinforced, while the immersion in acidic solution (HCl) that the (k) values after immersion more than the value in before immersion.

Due to the broad range uses of chromium for industrial purposes, besides its carcinogenic effect, an efficient, cost effective removal method should be obtained. In this study, cow bones as a cheap raw material were utilized to produce active carbon (CBAC) by physiochemical activation, which was characterized using: SEM to investigate surface morphology and BET to estimate the specific surface area. The best surface area of CBAC was 595.9 m²/gm which was prepared at 600 ^ᵒC activation temperature and impregnation ratio of 1:1.5. CBAC was used in aqueous chromium ions adsorption. The investigated factors and their ranges are: initial concentration (10-50 mg/L), adsorption time (30-300 min), temperature (20-50

Traditional programs and the tedious and financially costly processes they require are no longer the best choice for content makers. The continuous development and development have led to the emergence of competitive software that offers capabilities that are more suitable for aesthetic needs, as it breaks down stereotypical frameworks from the familiar to the unfamiliar to be more suitable for graphic subjects in terms of dealing with the requirements of the digital content industry. Video for communication platforms, as it has more advantages than traditional software and the flexibility and high quality it offers at the level of the final product, All of this contributed to supplementing the image with aesthetic employments with data

Abstract

   Mitoxantrone is an antitumor agent used in the treatment of breast and prostate cancer, acute leukemia, lymphoma, and also in the treatment of multiple sclerosis due to its immunosuppressive properties. The mitoxantrone's cardiotoxicity is irreversible, dose-dependent, and it may occur years after treatment. Zinc is considered as an essential mineral for cell division and the synthesis of DNA and protein; furthermore, such mineral has an important role in states of cardiovascular diseases; and may have protective effects in coronary artery disease and cardiomyopathy.

Objective: The current study is designed to investigate effects of two different doses of zinc sulfat

The research aims to know the extent of the impact of the risks of foreign exchange centers represented in commitment risks, liquidity risks, and exchange rate risks on the continuity of the economic unit. The research in the light of its presentation of the intellectual, cognitive and applied contributions about the risks of foreign currency centers and the continuity of the economic unit, and represented the research community in the banking sector, and the sample included nine private commercial banks listed in the Iraq Stock Exchange, and they relied on the research on a time series consisting of four years that extended from one year 2017 to 2020. The research problem was the impact of the risks associated with foreign currency cent

The excellent specifications of electrodes coated with lead dioxide material make it of great importance in the industry. So it was suggested this study, which includes electrodeposition of lead dioxide on graphite substrate, knowing that the electrodeposition of lead dioxide on graphite studied earlier in different ways.

In this work the deposition process for lead dioxide conducted using electrolytic solution containing lead nitrate concentration 0.72 M with the addition of some other material to the solution, such as copper nitrate, nickel nitrate, sodium fluoride and cetyl trimethyl ammonium bromide, but only in very small concentrations. As for the operating conditions, the effect of change potential and temperature as well

Hydrate dissociation equilibrium conditions for carbon dioxide + methane with water, nitrogen + methane with water and carbon dioxide + nitrogen with water were measured using cryogenic sapphire cell. Measurements were performed in the temperature range of 275.75 K–293.95 K and for pressures ranging from 5 MPa to 25 MPa. The resulting data indicate that as the carbon dioxide concentration is increased in the gas mixture, the gas hydrate equilibrium temperature increases. In contrast, by increasing the nitrogen concentration in the gas mixtures containing methane or carbon dioxide decreased the gas hydrate equilibrium temperatures. Furthermore, the cage occupancies for the carbon dioxide + methane system were evaluated using the Van der Wa

Nanoparticles of copper sulfide have been prepared by simple reaction between using copper nitrate with different concentrations ratio 0.1, 0.3, and 0.5 mM, thiourea by a simple chemical route. The prepared Nano powders have been deposited onto glass substrates by casting method at 60°C. The structure of the product Nano- films has been studied by x-ray diffraction, where the patterns showed that all the samples have a hexagonal structure of covellite copper sulfide with the average crystalline sizes 14.07- 16.51 nm. The morphology has been examined by atomic force microscopy, and field emission scan electron microscopy. The AFM images showed particles with almost spherical and rod shapes with average diameter sizes of 49.11- 90.64 nm.