A particulate polymer composite material was prepared by reinforcing with the Aluminum Oxide (Al₂O₃) or Aluminum (Al) metallic particles with a particle size of (30) µm to an unsaturated Polyester Resin with a weight fraction of (5%, 10%, 15%, 20%).

Tensile test results showed the maximum value of elastic modulus reached (2400MPa.)  in the case of reinforcing with (Al) particles with weight fraction (20%) and (1500 MPa.)  in the case of reinforcing with (Al₂O₃) particles of the same weight fraction.

  When the impact and the flexural strength tests were done, the results showed that flexural strength (F.S), maximum shear stress (τ_max), impact strength

     In this study, oxidative desulfurization of dibenzothiophene (DBT) with H2O2 as an oxidant was studied, whereas the catalyst used was zirconium oxide supported on Activated carbon (AC). Zirconium oxide (ZrO2) was impregnated over prepared activated carbon (AC) and characterized by various techniques such as XRD, FTIR, BET, SEM, and EDX. This composite was used as a heterogeneous catalyst for oxidation desulfurization of simulated oil. The results of this study showed that ZrO2/AC composite exhibited significant catalytic activity and stability, effectively lowering sulfur content under mild conditions. Factors such as reaction temperature (30, 40, 50, 60°C), time (5, 10, 15,20,30,60, 80 100 min), catalyst dose (0.3, 0.5,

Background: Poly (methylmethacrylate) is not ideal in every aspect and has disadvantages such as insufficient surface hardness, increase water sorption and poor impact resistance and the latter being the primary cause of fracture of denture base resins. The aim of this study was to evaluate the effect of addition of silanized nano- hydroxyapatite (HA) on some properties of heat cured acrylic denture base material. Materials and methods: HA nano particles were first silanized with MPS (tri methacryloxypropyletrimethoxy silane coupling agent) then ultrasonicated with methylmethacrylate (monomer) to disperse agglomerated nano particles and mixed with polymer. 2% by wt of HA nano particles was selected as the best concentration that add

This study was conducted in the Faculty of Agricultural Engineering Sciences - University of Baghdad in the field of sheep and goats in the Department of Animal Production. Effect of different concentrations of bovine albumin on some semen characteristics of frozen rams. Used in this experiment, 3 rams and their ages ranging from 2.5-3 years. The sample of the semen was diluted with Tris dilution with the addition of 10 ml of egg yolk per 100 ml, the sample by 1:1 with the tris and then the collection of sperm samples (Pooling) after the semen was divided into four treatments Control and bovine albumin at concentrations of 5, 7.5 and 10% and then complete dilution 10: 1, at 5C, dilution 20: 1, containing 5% glycerol per 100 ml. The results

Background: with the advent of new postmaterial in dentistry, it has become important to measure fitness of post restoration along the horizontal plane of the root space.This study aimed to measure and compare, the cement film thickness of conventional zinc phosphate cement in micrometer between the post and root dentin along horizontal plane at different post space regions (coronal, middle and apical) of four types of posts, by using stereomicroscopy. Material and methods: Thirty-two extracted human maxillary canines, mandibular canines and maxillary central incisors (n=32) were instrumented with ProTaper system files (hand use) and obturated with gutta-percha for ProTaper and AH26® root canal sealer. After 24hrs of incubation at 37ºC, p

This paper focused on the stone matrix asphalt (SMA) technology that was developed essentially to guard against rutting distress. For this procedure, fibers play a racy role in stabilizing and preventing the drain down problem caused by the necessity of high binder content coupled with their strengthening effect. A set of specimens with cylindrical and slab shapes were fabricated by inclusions jute, polyester, and carbon fibers. For each type, three contents of 0.25%, 0.5%, and 0.75% by weight of mixture were added by lengths of 5, 7.5, and 10 mm. The prepared mixtures were tested to gain the essential pertained parameters discriminated by the values of drain down, Marshall quotient, rut depth, and dynamic stability. It

Methotrexate (MTX) is widely used chemotherapeutic agent with different side effects including germ cells toxicities. Silibinin is one of the structural isomers of silymarin, with different phytotherapeutic applications, and its possible protective effects against MTX induced germ cells damage were investigated in this work. Twenty five male mice were divided into five groups (n=5) allocated as follows: Group 1 received buffer for five days given by single intraperitoneal (IP) injection per day; Group 2 in addition to buffer for five days, animals received at day five single dose of 20mg/kg of MTX IP. Groups (3, 4, and 5) received respectively, (50, 100, or 150mg/kg body weight) of silibinin IP single daily dose for five days then at day fi

The study was reflection of the impact of the widespread use of polymer Novolak composite reinforced  Glass fiber and Asbestos fiber once again with weight fraction 60% on the physical properties, which included (Hardness, Compressive deformation, compressive modulus of elasticity, Flexural modulus of elasticity, Resilience modulus, the maximum of Flexural strength, Flexural strain energy and Shear strength inner layers); it is known how much important the media as a source of bacterial contamination, which contributes directly or indirectly in the process of aging of these materials. These Novolak composite reinforced,  prepared by weight fraction of (10%) and (14%) of the Hexamethylene-tetraamine (HMTA) hardener material. It

In this research, the use of natural materials like wool and cannabis as intermediate reinforcement for prosthetic limbs due to their comfort, affordability, and local availability was discussed. As part of this study on below-the-knee (BK) prosthetic sockets, two sets of samples were made using a vacuum method. These sets were made of natural fiber-reinforced polymer composites with lamination 80:20: group (Y) had 4 perlon, 1 wool 4 perlon, and group (G) had 4 perlon, 1 cannabis 4 perlon. The two groups were compared with a socket made of polypropylene. Tensile testing was used to determine the mechanical characteristics of the socket materials. The Y group has a yield stress of 17 MPs, an ultimate strength of 18.75 MPa, and an elastic