Abstract-Industrial and urban development has resulted in the spread of plastic waste and the increase in the emissions of carbon dioxide resulting from the cement manufacturing process. The current research aims to produce green (environmentally friendly) concrete by using plastic waste as coarse aggregates in different proportions (10% and 20%) and nano silica sand powder as an alternative to cement in different proportions (5% and 10% by weight). The results showed that compressive strength decreased by 12.10% and 19.23% for 10% and 20% plastic waste replacement and increased by 12.89% and 20.39% for 5% and 10% silica sand replacement respectively at 28 days. Flexural strength decreased by 12.95% and 19.64% for 10% and 20% plastic waste

Membrane manufacturing system was operated using dry/wet phase inversion process. A sample of hollow fiber membrane was prepared using (17% wt PVC) polyvinyl chloride as membrane material and N, N Dimethylacetamide (DMAC) as solvent in the first run and the second run was made using (DMAC/Acetone) of ratio 3.4 w/w. Scanning electron microscope (SEM) was used to predict the structure and dimensions of hollow fiber membranes prepared. The ultrafiltration experiments were performed using soluble polymeric solute poly ethylene glycol (PEG) of molecular weight (20000 Dalton) 800 ppm solution 25 °C temperature and 1 bar pressure. The experimental results show that pure water permeation increased from 25.7 to 32.2 (L/m2.h.bar) by adding aceton

Forward osmosis (FO) process was applied to concentrate the orange juice. FO relies on the driving force generating from osmotic pressure difference that result from concentration difference between the draw solution (DS) and orange juice as feed solution (FS). This driving force makes the water to transport from orange juice across a semi-permeable membrane to the DS without any energy applied. Thermal and pressure-driven dewatering methods are widely used, but they are prohibitively energy intensive and hence, expensive. Effects of various operating conditions on flux have been investigated. Four types of salts were used in the DS, (NaCl, CaCl2, KCl, and MgSO4) as osmotic agent and the experiments were performed at the concentration of

Membrane manufacturing system was operated using dry/wet phase inversion process. A sample of hollow fiber membrane was prepared using (17% wt PVC) polyvinyl chloride as membrane material and N, N Dimethylacetamide (DMAC) as solvent in the first run and the second run was made using (DMAC/Acetone) of ratio 3.4 w/w. Scanning electron microscope (SEM) was used to predict the structure and dimensions of hollow fiber membranes prepared. The ultrafiltration experiments were performed using soluble polymeric solute poly ethylene glycol (PEG) of molecular weight (20000 Dalton) 800 ppm solution 25 °C temperature and 1 bar pressure. The experimental results show that pure water permeation increased from 25.7 to 32.2 (L/m2.h.bar) by adding a

A lab-scale packed Bio film reactor was used for ethanol production by fermentation of sugar solution using a local
isolated yeast saccharomyces cerevisia and glutaraldelryde on gelating as a covalent bounding agent. In this study four
types of packing in the reactor were used. They are; polypropylene mesh, glass rashig rings, ceramic rashig rings and
glass beads. Glucose solutions were used as substrate with four concentrations; (5, I 0, I 5, 20 g/l). Results show that the
ethanol productivity was increase with increasing sugar concentration. Also it was found that polypropylene mesh
packing give the highest productivity while glass beads gives the lowest productivity. The experiments were conducted at
three temperatur

Reverse osmosis membrane desalination is one of the most significant water treatments that is used to offer freshwater. The aim of this research is to study the effect of controlling the value of the zeta potential on the suspended particles in the water and the proximity of the membrane surfaces in the colloidal solution, to keep the water stable electrically and disperse the colloidal particles. To achieve this aim, the experimental study was conducted in the Sanitary Engineering Laboratory, in the engineering college - University of Baghdad. Two systems were set up, one worked normally and the other worked by using the zeta rod placed before the reverse osmosis membrane. The results showed that the effect of the zeta rod increas