The aim of this study is to evaluate the levels of trace elements Magnesium (Mg), Zinc (Zn), Copper (Cu), and Selenium (Se) in blood sera of asthmatic patients by Atomic Absorption Spectrophotometry (AAS). The concentrations of Mg, Cu, and Zn have been determined by Flame Atomic Absorption spectrophotometry (FAAS), and Se with flameless Graphite Furnace Atomic Absorption Spectrophotometry (GFAAS). The study involves (55) asthmatic patients as study group and (28) subjects as control from both genders. Serum levels of Mg, Cu, and Se were significantly higher (p<0.001 for all) in patients when compared with healthy subjects, while Zn level was relatively significant (p<0.05). Our observations confirm the efficacy and applicability of (AAS) in

In this research, Mn-doped TiO2 thin films were grown on glass, Si and OIT/glass substrates by R.F magnetron sputtering technique with thicknesses (250 nm) using TiO2:Mn target under Ar gas pressure and power of 100 Watt. Through the results of X-ray diffraction, the prepared thin films are of the polycrystallization type after the process of annealing at 600°C for two hour The average crystalline size were 145.32, 280.97 and 261.23 nm for (TiO2:Mn) thin film on glass, Si and OIT/glass substrates respectively, while the measured surface roughness is between 0.981nm and 1.14 nm. The fabricated (TiO2:Mn) thin film on glass sensors have high sensitivity for hydrogen( H2 reducing gas) compared to the sensitivity for hydrogen gas on Si and OIT/

A rapid high performance liquid chromatography method for the determination of sphinganine (Sa) and sphingosine (So) in urine samples by employing a silica-based monolithic column is described. The samples were first extracted using ethyl acetate and derivatized using ortho-phthaldialdehyde in the presence of 2-mercaptoethanol. C20 sphinganine was used as internal standard. Under the optimized conditions, separation was achieved using a mixture of methanol:water (93:7, v/v), column temperature at 30°C, flow rate of 1 mL min−1, and an injection volume of 10 μL. Good linearity was obtained for Sa and So over the concentration range 20–500 ng mL−1(correlation coefficients ≥0.9978). The detection limits were 0.45 ng mL−1 for Sa and

The investment however "was its description and meaning, it remains a resident" in the composition of capital assets located in the forefront of the creation of productive assets, and this means that the investment in the productive sectors is a priority in achieving capital accumulation, on any other investment that takes place with the stages of advanced development of formation , not forgetting "to humans and investment humans as head of real money product, the source of the economic surplus and accumulation, and the source of producing values, and if human labor was the source of value, and the human was the source of work, therefore humanitarian work on different levels and skills presents capital", so the investment in huma

The aim of this research is to employ starch as a stabilizing and reducing agent in the production of CdS nanoparticles with less environmental risk, easy scaling, stability, economical feasibility, and suitability for large-scale production. Nanoparticles of CdS have been successfully produced by employing starch as a reducing agent in a simple green synthesis technique and then doped with Sn in certain proportions (1%, 2%, 3%, 4%, and 5%).According to the XRD data, the samples were crystallized in a hexagonal pattern, because the average crystal size of pure CdS is 5.6nm and fluctuates in response to the changes in doping concentration 1, 2, 3, 4, 5 %wt Sn, to become   4.8, 3.9, 11.5, 13.1, 9.3 nm respectively. An increase in crystal

In this research tri metal oxides were fabricated by simple chemical spray pyrolysis technique from (Sn(NO₃)₂.20 H₂O, Zn(NO₃)₂.6 H₂O, Cd(NO₃)₂.4 H₂O) salts at concentration 0.1M with mixing weight ratio 50:50 were fabricated on silicon substrate n-type (111). (with & without the presence of grooves by the following diemensions (20μm width, 7.5μm depth) with thickness was about ( 0.1 ±0.05 µm) using water soluble as precursors at a substrate temperature 550 ºC±5, with spray distance (15 cm) and their gas sensing properties toward H₂S gas at different concentrations (10,50,100,500 ppmv) in air were investigated at room te

Leinamycin is a thiol dependent DNA alkylating agent which shows very potent activity against various cancer cell lines. This natural compound forms guanine adducts (N7) in DNA which are converted into a basic sites and simultaneously generates Reactive Oxygen Species (ROS), to produce DNA strand breaks in human cancer cells. In present study, eight different strains isolated from Iraqi soils were taxonomically assigned as Streptomyces.atroolivaceous. Remarkably the strain named as THS-44 was distinguished in productivity in comparison with other strains; the amount of leinamycin was 50.98 mg/l. In this study, we assessed the cytotoxic activity of leinamycin against RD and ANM3 cancer cell line in compare with REF cell line as a normal cont

   In the present research the flame retardancy to  buildings and industrial foundations which are manufacturing from advanced polymeric  composite material was increased by coating it with surface layer included flame retardant material.  A(3mm) thick antimony tetroxide was used as a coated layer to retard and prevent the flame spread to the coating surface of polyester resin (SIROPOL 8340-PI) reinforced with hybrid fibers as a woven roving (°45-°0) consist of carbon and kevlar (49) fibers, and exposed it to direct flame generated from gas torch at temperature of (2000ºC), at  different exposed distance (10,15,20mm)and study the rang of resistance for this layer and its ability to protec

Positron annihilation lifetime (PAL) technique has been employed to
study the microstructural changes of polyurethane (PU), EUXIT 101
and epoxy risen (EP), EUXIT 60 by Gamma-ray irradiation with the
dose range (95.76 - 957.6) kGy. The size of the free volume hole and
their fraction in PU and EP were determined from ortho-positronium
lifetime component and its intensity in the measured lifetime spectra.
The results show that the irradiation causes significant changes in the
free volume hole size (V_h) and the fractional free volume (F_h), and
thereby the microstructure of PU and EP. The results indicate that
the γ-dose increases the crystallinity in the amorphous regions of PU
and increas