Microstructural Characterization and Mechanical Properties of Similar and Dissimilar Al Alloys Joined using Friction Stir Welding
...Show More Authors

The influence of pre- shot peening and welding parameters on mechanical and metallurgical properties of dissimilar and similar aluminum alloys AA2024-T3 and AA6061-T6 joints using friction stir welding have been studied. In this work, numbers of plates were equipped from sheet alloys in dimensions (150*50*6) mm then some of them were exposed to shot peening process before friction stir welding using steel ball having diameter 1.25 mm for period of 15 minutes. FSW joints were manufactured from plates at three welding speeds (28, 40, 56 mm/min) and welding speed 40mm/min was chosen at a rotating speed of 1400 rpm for welding the dissimilar pre- shot plates. Tow joints were made at rotational speed of 1000 rpm and welding speed of 40m/min from shot and without shot peening plats. Welding temperature was measured in three zones using thermocouple. Micro hardness (HV) and tensile tests were performed to evaluate the mechanical characteristic of the joints. The results show a decay in mechanical qualities when the welding speed was increased and the best result was at (28) mm/min and the opposite result was obtained when rotational speed increased and pre-shot contributed in improving of this decay at 88% of welding speed (40) mm/min and 98%  at the rotational speed of 1000 rpm.

 

 

 

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Wed Apr 19 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Study the Effect of Zn Doping in the Structural and Electrical Properties of CdTe Thin Films
...Show More Authors

Some of structural ,and electrical properties of pure and zinc (Zn) doped cadmium telluride thin films with impurity percentages (0.5, 1, 1.5)%, deposited on hot glass substrate (temperature equals to 423K) of  thickness of 300nm and rate deposition of 0.5 nm.s-1  by thermal co-evaporation technique under vacuum of (2×10-5)Torr have been investigates. The structural properties for the prepared films were studied before and after. doping process by analysis of the X-ray diffraction, and it appeared that pure and dopant  CdTe thin films are polycrystalline and have the cubic structure with preferential orientation in the [111] direction, and the crystal structure of the films were improved due to doping process. From d.c

... Show More
View Publication Preview PDF
Publication Date
Tue Nov 01 2016
Journal Name
Journal Of Hazardous Materials
Impacts of compound properties and sediment characteristics on the sorption behaviour of pharmaceuticals in aquatic systems
...Show More Authors

View Publication
Scopus (71)
Crossref (70)
Scopus Clarivate Crossref
Publication Date
Wed Jan 25 2023
Journal Name
Journal Of Umm Al-qura University For Applied Sciences
Investigating CO2 storage properties of Pd(II) and Co(II) chelates of a Schiff's base ligand
...Show More Authors
Abstract<p>A new metal complexes are made from the ligands derived from amoxicillin based Schiff's base coordinated with Pd(II) and Co(II) have been synthesized and characterized via different spectroscopic methods. FT-IR spectroscopy have shown a formation of tetrahedral and square planar geometry for Co(II) and Pd(II) complexes, respectively. Surface morphology was inspected via field emission scanning electron microscopy (FESEM) and atomic force microscopy (AFM). The Brunauer–Emmett–Teller surface area of the metal complexes samples is about 6.63 to 8.71 m<sup>2</sup>/g, with pore diameters and volume of 0.030–0.0501 cm<sup>3</sup>/g and 18.39–22.98 nm, respectively. The quadrupo</p> ... Show More
View Publication Preview PDF
Scopus (2)
Crossref (1)
Scopus Crossref
Publication Date
Fri Dec 22 2023
Journal Name
Journal Of Optics
Studying the effect of adding Mo on the optical and structural properties of the CoFe2O4 compound
...Show More Authors

View Publication
Scopus Clarivate Crossref
Publication Date
Sun Sep 07 2008
Journal Name
Baghdad Science Journal
Study the effect of thickness and annealing temperature on the Electrical Properties of CdTe thin Films
...Show More Authors

The electrical properties of polycrystalline cadmium telluride thin films of different thickness (200,300,400)nm deposited by thermal evaporation onto glass substrates at room temperature and treated at different annealing temperature (373, 423, 473) K are reported. Conductivity measurements have been showed that the conductivity increases from 5.69X10-5 to 0.0011, 0.0001 (?.cm)-1 when the film thickness and annealing temperature increase respectively. This increasing in ?d.c due to increasing the carrier concentration which result from the excess free Te in these films.

View Publication Preview PDF
Crossref
Publication Date
Thu Jun 30 2022
Journal Name
Iraqi Geological Journal
Integrating Petrophysical and Geomechanical Rock Properties for Determination of Fracability of the Iraqi Tight Oil Reservoir
...Show More Authors

Tight oil reservoirs have been a concerned of the oil industry due to their substantial influence on oil production. Due to their poor permeability, numerous problems are encountered while producing from tight reservoirs. Petrophysical and geomechanical rock properties are essential for understanding and assessing the fracability of reservoirs, especially tight reservoirs, to enhance permeability. In this study, Saadi B reservoir in Halfaya Iraqi oil field is considered as the main tight reservoir. Petrophysical and geomechanical properties have been estimated using full-set well logs for a vertical well that penetrates Saadi reservoir and validated with support of diagnostic fracture injection test data employing standard equations

... Show More
View Publication
Scopus (7)
Scopus Crossref
Publication Date
Fri Jul 22 2022
Journal Name
Journal Of Biomimetics, Biomaterials And Biomedical Engineering
Influence of Bioactive and Bio Inert Ceramic Powders on Tribology Properties of PMMA Composite Denture Base
...Show More Authors

Polymer matrix composites are suitable materials for medical applications, such as denture base resin polymethyl methacrylate (PMMA). This includes light weight and high strength. This paper describes the effect of selected weight fractions (1, 2, 3, 4 & 5) % wt of nano(Alumina AL2O3, Zirconia ZrO2, Hydroxyapatite HA and Halloysite nanoClay) reinforcements on the biopolymer matrix (PMMA). Some tribology tests were used to evaluate the prepared system (impact strength, hardness surface, and wear rate) tests. The samples were fabricated by (Hand Lay-Up) with different particle reinforcement percentages. All tests were accomplished at room temperature, and samples were developed according to the ASTM standard. The weight fraction o

... Show More
View Publication
Scopus (1)
Crossref (2)
Scopus Clarivate Crossref
Publication Date
Fri Jan 01 2016
Journal Name
World Scientific News
Effect of annealing temperature on the structural and optical properties of CdSe: 1% Ag thin films
...Show More Authors

Publication Date
Fri Jul 01 2022
Journal Name
Journal Of Biomimetics, Biomaterials And Biomedical Engineering
Influence of Bioactive and Bio Inert Ceramic Powders on Tribology Properties of PMMA Composite Denture Base
...Show More Authors

Polymer matrix composites are suitable materials for medical applications, such as denture base resin polymethyl methacrylate (PMMA). This includes light weight and high strength. This paper describes the effect of selected weight fractions (1, 2, 3, 4 & 5) % wt of nano(Alumina AL2O3, Zirconia ZrO2, Hydroxyapatite HA and Halloysite nanoClay) reinforcements on the biopolymer matrix (PMMA). Some tribology tests were used to evaluate the prepared system (impact strength, hardness surface, and wear rate) tests. The samples were fabricated by (Hand Lay-Up) with different particle reinforcement percentages. All tests were accomplished at room temperature, and samples were developed according to the ASTM standard. The weight fraction of (4% for AL

... Show More
Scopus (1)
Scopus
Publication Date
Thu Jan 04 2018
Journal Name
International Journal Of Science And Research (ijsr)
Effect of Doping on Properties of the Hall Effect and Electrical Conductivity for AgInTe2 Thin Films
...Show More Authors

The effect of different doping ratio (0.3, 0.5, and 0.7) with thickness in the range 300nmand annealed at different temp.(Ta=RT, 473, 573, 673) K on the electrical conductivity and hall effect measurements of AgInTe2thin film have and been investigated AgAlxIn(1-x) Te2 (AAIT) at RT, using thermal evaporation technique all the films were prepared on glass substrates from the alloy of the compound. Electrical conductivity (σ), the activation energies (Ea1, Ea2), Hall mobility and the carrier concentration are investigated as a function of doping. All films consist of two types of transport mechanisms for free carriers. The activation energy (Ea) decreased whereas electrical conductivity increases with increased doping. Results of Hall Effect

... Show More
Preview PDF