Abstract Background: The daily usage of maxillofacial prostheses causes them to mechanically deteriorate with time. This study was aimed to evaluate the reinforcement of VST50F maxillofacial silicone by using yttrium oxide (Y2O3) nanoparticles (NPs) to resist aging and mechanical deterioration. Materials and Method: Y2O3 NPs (30–45nm) were loaded into VST50F maxillofacial silicone in two weight percentages (1 and 1.5 wt%), which were predetermined in a pilot study as the best rates for improving tear strength with minimum increase in hardness values. A total of 120 specimens were prepared and divided into the control and experimental groups (with 1 and 1.5 wt% Y2O3 addition). Each group included 40 specimens, 10 specimens for each paramet

In the current study, gold nanoparticles were made using Acinetobacter baumannii broth culture. UV-vis, FTIR, XRD, FESEM, AMF, and zeta potential measurements were also used to study the properties of the Ab-AuNPs. The average was 66 nm, ranging from 20 to 90 nm. The examination results proved that the Ab-AuNPs are semi-spherical and varied from 20 to 90 nm, with an average of 66 nm. 

   MTT assay on the breast cancer cell line MCF-7 confirmed the anticancer activity in vitro. Cancer cells showed an important cytotoxic activity of Ab-AuNPs. The breast. Cancer cell. Line.MCF-7 but ineffective against the normal.cell line.MCF-10. The IC50 values of Ab-AuNPs were at 11.45 μg ml-1. The results proved that Ab-

Lithium–Manganese ferrites having the chemical formula (Li0.5-0.5x Mnx Fe2.5-0.5x O4), (0 ≤ x ≤ 1) were prepared by double sintering powder processing. The density of the ferrite increased with Mn content while the porosity was noticed to decrease. The dielectric constant was found to increase at high frequencies more rapidly than the low ones. The dielectric constant found to decrease with Mn content. The decrease in loss factor with frequency agreed with Deby’s type relaxation process. A maximum of dielectric loss factor was observed when the hopping frequency is equal to the external electric field frequency. Manganese substitution reduced the dielectric loss in ferrite. The variation of tanδ with frequency shows a similar na

1-[4-(2-Hydroxy-4, 6-dimethyl-phenylazo)-phenol]-ethanone (HL1) and 2-(4-methoxy-phenylazo)-3, 5- dimethyl-phenol (HL2) were produced by combination the diazonium salts of amines with 3, 5- dimethylphenol. The geometry of azo compounds was resolved on the basis of (C.H.N) analyses, 1H and 13CNMR, FT-IR and UV-Vis spectroscopic mechanisms. Complexes of La (III) and Rh (III) have been performed and depicted. The formation of complexes has been identified by using elemental analysis, FTIR and UV-Vis spectroscopic process as well, conductivity molar quantifications. Nature of complexes produced have been studied obeyed mole ratio and continuous alteration ways, Beer's law followed through a concentration scope (1×10-4 - 3×10-4 M). High molar

Oxidation of sulfur compounds in fuel followed by an adsorption process were studied using two modes of operation, batch mode and continuous mode (fixed bed). In batch experiment oxidation process of kerosene with sulfur content 2360 ppm was achieved to study the effect of amount of hydrogen peroxide(2.5, 4, 6 and 10) ml at different temperature(40, 60 and 70)°C. Also the effect of amount acetic acid was studied  at the optimal conditions of the oxidation step(4ml H₂O₂ and 60 °C).Besides, the role of acetic acid different temperatures(40, 60, 70) °C and 4ml H₂O₂, effect of reaction time(5, 30, 60, 120, 300) minutes at temperatures(40,60) °C, 4ml H₂O₂ and 1 mlHAC)&

The study aims to evaluate the removal of sulfur content from Iraqi light naphtha produced in Al-Dora refinery by adsorption desulfurization DS technique using modified activated carbon MAC loaded with nickel Ni and copper Cu as single binary metals. The experiments were carried in a batch unit with various operating parameters;  MAC dosage, agitation speed, and a contact time of 300 min at constant initial sulfur concentration 155 ppm and temperature. The results showed higher DS% by AC/Ni-Cu (66.45)% at 500 rpm and 1 g dosage than DS (29.03)% by activated carbon AC, increasing MAC dosage, agitation speed, and contact time led to increasing DS% values.  The adsorption capacity of MAC results was recorded (16, 15, and 20) mg sulfu

The study aims to evaluate the removal of sulfur content from Iraqi light naphtha produced in Al-Dora refinery by adsorption desulfurization DS technique using modified activated carbon MAC loaded with nickel Ni and copper Cu as single binary metals. The experiments were carried in a batch unit with various operating parameters;  MAC dosage, agitation speed, and a contact time of 300 min at constant initial sulfur concentration 155 ppm and temperature. The results showed higher DS% by AC/Ni-Cu (66.45)% at 500 rpm and 1 g dosage than DS (29.03)% by activated carbon AC, increasing MAC dosage, agitation speed, and contact time led to increasing DS% values.  The adsorption capacity of MAC results was recorded (16,

In this work, thiadiazole derivatives were prepared by taking advantage of active sites in (2-amino-5-mercapto-1, 3, 4-thiadiazole) as a starting material base. The main heterocyclic compounds (1, 3, 4-thiadiazole, oxazole) etc, 2-amino-5-mercapto-1,3,4-thiadiazole compound (1) was prepared by cyclic closure of thiosemicarbazide compound with anhydrous sodium carbonate and carbon disulfide. Oxidation of (1) via hydrogen peroxide, to have (2) which was treated with chloro acetyl chloride to get (3). Preparation of thiazole ring (4) was from reacting of (3) with thiourea. Synthesis of diazonium salts (5) from compound (4) using sodium nitrite and HCl. Compound (5) reacted with different ester compounds to prepare a new azo compounds (6–8).C

         Trace elements concentrations are frequently reported to be a good indicator for diagnosis and prognosis of some disease. The levels of copper, zinc, manganese, and magnesium were measured in serum of two group. Group one contains (52) newborn jaundice patients while the second group contains (20) healthy newborn used as controls.

          In this study the concentration of Cu, Zn, Mg, and Mn were measured using atomic absorption spectrophotometer (AAS). It has been found that zinc level is significantly lower in newborn jaundice patients compared with normal subjects at (p<0.05) , also the level of Cu, Mg, and Mn were significantly