Aluminum doped zinc selenide ZnSe/n-Si thin films of (250∓20 nm) thickness with (0.01, 0.02 and 0.03), are depositing on the two type of substrate (glass and n-Si) to manufacture (ZnSe/n-Si) solar cell through using thermal vacuum evaporation procedure. physical and optoelectronic properties were examined for the samples. X-Ray and AFM techniques are using to study the structure properties. The energy band gap of as-deposited ZnSe thin films for changed dopant ratio were ranging from (2.6-2.68 eV). The results of Hall effect show that pure and doping films were (p-type), and the concentration carriers and the carriers mobility increases with increase Al-dopant ratio. The (C-V) have shown that the heterojunction were of abrupt type. In add

In this work Study effect of annealing temperature on the Structure
of a-Se and electrical properties of a-Se/c-Si hetrojunction have been
studied.The hetrojunction fabricated by deposition of a-Se film on c-
Si using thermal evaporation.
Electrical properties of a-Se/ c-Si heterojunction include I-V
characteristics, in dark at different annealing temperature and C-V
characteristics are considered in the present work.
C-V characteristics suggested that the fabricated diode was
abrupt type, built in potential determined by extrapolation from
1/C2-V curve. The built - in potential (Vbi) for the Se/ Si System
was found to be increase from 1.21 to 1.62eV with increasing of
annealing temperature

Visible-light photodetectors constructed Fe2O3 were manufactured effectively concluded chemical precipitation technique, films deposited on glass substrate and Si wafer below diverse dopant (0,2,4,6)% of Cl, enhancement in intensity with X-ray diffraction analysis was showed through favored orientation along the (110) plane, the optical measurement presented direct allowed with reduced band gap energies thru variation doping ratio , current–voltage characteristics Fe2O3 /p-Si heterojunction revealed respectable correcting performance in dark, amplified by way of intensity of incident light, moreover good photodetector properties with enhancement in responsivity occurred at wavelength between 400 nm and 470 nm.

Background: It may be an important prospective clinical use of manufacturing of porous implant for clinical situations, such as cases of limitation in bone height, low bone density .The small segment of porous implant an effective osseointegration allows increasing in contact area provided for small segmented porous provided by its surface configuration. This study was done to Fabricate porous titanium implants by powder technology, as well as the observation of removal torque values of porous titanium implants compared to smooth titanium implants. Materials and methods: Twenty porous titanium implants (3.2mm in diameter and 8mm in length) were manufactured by powder technology using commercially pure titanium powder of ≤75um part

New metal complexes of the ligands 2-benzamido benzothiazole(B1), and 2-actamido benzothiazole(B2) with metal ions Ni(II),and Co(II) were prepared in alcoholic medium. The prepared complexes were characterized by FT-IR and electronic spectroscopy, Magnetic susceptibility, Flame Atomic Absorption technique as well as elemental analysis and conductivity measurement. From the spectral studies, an octahedral monomer structure proposed for Ni(II) complexes, and a tetrahedral monomer structure for Co(II)complexes.Semi-empirical methods (PM3,and ZINDO/1)were carried out to evaluate the heat formation( ?H?f)binding energy(?Eb) and dipole moment(µ)for all metal complexes. Also vibration frequencies, Electrostatic potential, HOMO and LUMO

An environmentally friendly technique was used to prepare titanium dioxide@ silver (core shell) (TiO₂@Ag NPs) using chard leaf extract, a natural stabilizer and reductant. A nanocomposite (NCs) of TiO₂@Ag supported by halloysite nanotubes (HNTs), TiO2@Ag/HNT NCs, was prepared under microwave irradiation. The microwave technique is used to accelerate the reaction and enhance the homogeneity of nanoparticle distribution. Spectroscopic and structural analyses were performed on the resulting nanocomposite. X-ray diffraction (XRD) revealed a clear crystalline structure with grain sizes ranging from 7 to 15 nm, with an average of ~11 nm, the transmission electron microscope (TEM) revealed that the size of nanoparticles in the TiO₂@Ag/HNT N