In this work, magnesium aluminate spinel (MA) (MgO 28 wt%, Al2O3 72 wt%) stoichiometric compound , were synthesized via solid state reaction (SSR) Single firing stage, and the impact of sintering on the physical properties and thermal properties as well as the fine structure and morphology of the ceramic product were examined. The Spinel samples were pressed at of (14 MPa) and sintering soaking time (2h). The effect of adding oxide titania (TiO2) was studied. The obtained powders were calcined at a temperature range of 1200 and 1400 °C. The calcined samples spinel were characterized by XRD, it showed the presence of developed spinel phase end also showed that the best catalyst is titania. The SEM image showed the high sintering temperat

This study was carried out to find out the effect of germination of broad beans and chickpeas seeds for different periods on their antinutritional factors content ( Trypsin inhibitor and Phytic acid ) and the chemical constituents of germination seeds compared with the control samples (ungerminated seeds) . The results indicated asignificant increase (P<0.05) in crude protein content as germination period proceeded.The highest values of 28.0% and 24.0% were reached on the sixth and fourth day for germinated broad beans and chickpeas respectively, The intial values were 25.6% and 23.5% for control samples, respectively. The content of raffinose,stachyose and verbascose were reduced as germination period proceeded, Stachyose and verbascose we

The experiment was conducted using Potato( Solanum tuberosum L.) at the eastern Radwaniyah at private field during fall season 2020/2021 and spring 2021 to study the effect of nitrogen levels to 350, 275, 200 kg N h-1 ( N1, N2, N3) and phosphorous to 100, 180, 360 kg P2O5 h-1 ( P1, P2, P3) and potassium to 100, 200, 300 kg K2O h-1 ( K1, K2, K3) to vegetative growth and yield of industrial potato, The seeds of the hybrid potato Sinora, Class A, were planted in the fall season on 15/9/2020 and Elite in the spring season on 31/1/2021. The experimental fertilizers were added in four batches and in proportions according to the stages of plant age, Factorial experiment with RCBD using three replications. The results showed that changing t

This study has been conducted to examin the effect of sodium propionate at different level of 0.03,0.06,0.10% on the number of bacteria and mold and to extend the storage life of laboratory processed biscuit. The results indicated that the use of 0.10% sodium propionate prolonged the storage peroid until the third month, while the use of 0.20% sodium propionate showed no growth of bacteria up to six month of storage, three types of bacteria has been isolated from processed biscuit, namely, Staphylococcus aureus, Bacillus cereus, Esherichia coli. using 0.10% sodium propionate showed no growth of mold up to three month of storage ,while using of 0.15 % and 0.20% sodium propionate prevent the growth

An isolate of Leishmania major was grown on the semisolid medium and incubated at 26ºC. The isolate was irradiated by He: Ne laser (632.8 nm, 10 mW) at exposure times (5, 10, 15, 20, 25, 30) minutes in their respective order. The unirradiated groups represent control group. Growth rate and percentage of viability were examined during six days after irradiation. The change in these two parameters reflects the effect of irradiation on the parasite. The results refers that the general growth effected by irradiation in comparison with un irradiation group, The growth rate of parasite decrease with increasing the exposure time in comparison with control group. Parasite viability decrease with irradiation and the percentage of living cell dec

     This work compares the changes in optical and structural properties of cerium oxide (CeO2) when doped with different concentrations (3%,5%,7%, and 9%) of two oxides, In2O3 and Eu2O3. X-ray diffraction and spectrophotometry were employed in the visible, ultraviolet, and near-infrared regions. The findings demonstrated that CeO2 doped with In2O3 and Eu2O3 thin films were polycrystalline and had a cubic structure. The crystal size increased from 20.5 to 32.15 when Eu2O3 doping ratio increased from 0% to 7% and then decreased to 28.46 nm at 9%. While the crystal size showed an increase from 20.5 to 21.42 nm with the increase of the In2O3 doping ratio, while the lattice constant measured for cubic CeO2 changed opposite to that