The composites were manufactured and study the effect of addition of filler (nanoparticles SiO2 treated with silane) at different weight ratios (1, 2, 3, 4 and 5) %, on electrical, mechanical and thermal properties. Materials were mixed with each other using an ultrasound, and then pour the mixture into the molds to suit all measurements. The electrical characteristics were studied within a range of frequencies (50-1M) Hz at room temperature, where the best results were shown at the fill ratio (1%), and thermal properties at (X=3 %), the mechanical properties at the filler ratio (2%).

An effective two-body density operator for point nucleon system folded with two-body correlation functions, which take account of the effect of the strong short range repulsion and the strong tensor force in the nucleon-nucleon forces, is produced and used to derive an explicit form for ground state two-body charge density distributions (2BCDD's) and elastic electron scattering form factors F (q) for 19F, 27Al and 25Mg nuclei. It is found that the inclusion of the two-body short range correlations (SRC) has the feature of reducing the central part of the 2BCDD's significantly and increasing the tail part of them slightly, i.e. it tends to increase the probability of transferring the protons from the central region of the nucleus towards

Background: Leukemia is a broad term given to a group of malignant diseases characterized by diffuse replacement of bone marrow with proliferating leukocyte precursors. Chemotherapy has been increasingly used to treat malignant conditions. The systemic sequelae as a result of these immunosuppressive techniques induce many oral and dental complications. This study was conducted to evaluate the effect of chemotherapy on oral health status and activity of salivary alkaline phosphates enzyme in patients with acute lymphocytic leukemia. Materials and methods: The study groups included 28 patients with acute lymphocytic leukemia; they were under chemotherapy, aged 20-25 year old. The control group includes healthy subjects matching with study

Glass Fiber Reinforced Polymer (GFRP) beams have gained attention due to their promising mechanical properties and potential for structural applications. Combining GFRP core and encasing materials creates a composite beam with superior mechanical properties. This paper describes the testing encased GFRP beams as composite Reinforced Concrete (RC) beams under low-velocity impact load. Theoretical analysis was used with practical results to simulate the tested beams' behavior and predict the generated energies during the impact loading. The impact response was investigated using repeated drops of 42.5 kg falling mass from various heights. An analysis was performed using accelerometer readings to calculate the generalized inertial load. The in

New N2O2 donor kind Schiff basehas been destined and structured by reaction Ampyrone with O-hydroxyacetophenone and Anthranilic acid. The metal complexes of the Schiff base with Mn(II), Hg(II), Ni(II), Cu(II), and Co(II) metal ions were designed and characterized by magnetic susceptibility, elemental analyses, molar conduction, IR, and 1H NMR,UV-Vis spectral metrics.The UV-Vis. and magnetic susceptibility data of the complexes suggest a square-planar, tetrahedraland octahedral geometries around the central metal ions. All elaborations were accomplished after determination the optimum molar concentration and pH which followed law of Lambert-Beer's in the researches pH scopes. The composition of these complexes were conclude dapprobating to t

Nanostructure of chromium oxide (Cr₂O₃-NPs) with rhombohedral structure were successfully prepared by spray pyrolysis technique using Aqueous solution of Chromium (III) chloride CrCl₃ as solution. The films were deposited on glass substrates heated to 450°C using X-ray diffraction (XRD) shows the nature of polycrystalline samples. The calculated lattice constant value for the grown Cr₂O₃ nanostructures is a = b = 4.959 Å & c = 13.594 Å and the average crystallize size (46.3-55.6) nm calculated from diffraction peaks, Spectral analysis revealed FTIR peak characteristic vibrations of Cr-O Extended and Two sharp peaks present at 630 and 578 cm-1 attributed to Cr-O “stretching

Background: Isoxazoles are an important class of five-membered unsaturated heterocyclic compounds. They show several applications in diverse areas such as pharmaceuticals, agrochemistry and industry. Isoxazoles are also found in natural sources showing insecticidal, plant growth regulation and pigment functions. Current study was conducted for synthesis of twenty five new Isoxazole derivatives and to evaluate the in vitro antibacterial activities of these derivatives. Methods: Benzaldoxime and their substituted [I] ae were prepared via addition-elimination reactions between aromatic aldehyde and hydroxylamine hydrochloride. In a second step, para-or meta-substituted benzaldoximes [I] ae were reacted with N-chlorosucceinimide in DMF to yield

This thesis aims to study the effect of addition polymer materials on mechanical properties of self-compacting concrete, and also to assess the influence of petroleum products (kerosene and gas oil) on mechanical properties of polymer modified self-compacting concrete (PMSCC) after different exposure periods of (30 ,60 ,90 ,and 180 days).

Two type of curing are used; 28 days in water for SCC and 2 days in water followed 26 days in air for PMSCC.

The test results show that the PMSCC (15% P/C ratio) which is exposed to oil products recorded a lower deterioration in compressive strength's values than reference concrete. The percentages of reduction in compressive strength values of PMSCC (15% P/C ratio) was

The temperature influence on the fluorescence lifetime, quantum yields and non-radiative rate parameter or coumarin 460 dye dissolved in methanol was investigated in the temperature range (160-300 k). A single photon counting technique was used or measuring the fluorescence decay curves. A noticeable decrease of the fluorescence lifetime with increasing the temperature was observed. The non-radiative activation energy of 10.57 K.J. mole-1 was measured by the help of Arrhenius plot.

In the present work, the behavior of thick-walled cylinder of elasto-plastic material (polymeric material) has been studied analytically. The study is based on modified Von-Mises yield criterion (for non metallic material). The equations of stress distribution are obtained for the cylinder under general cases of elastic expansion, plastic initiation and elastic-plastic expansion.

        A computer program is developed for evaluating the stress distribution. The solution is carried out for worst boundary conditions when the cylinder is subjected to the combination of pressure load, inertia load, and temperature gradient.

        The results are presente