Chemical bath deposition was used to synthesize ZnO nanorods (NRs) on glass and fluorine^_doped tin oxide (FTO) substrates. X-ray diffraction was performed to examine the crystallinity of ZnO nanorod. Results showed that ZnO NRs had a wurtzite crystal structure. Field emission scanning electron microscopy images showed that glass sample had rod-like structure distribution with (50 nm) diameter and average length of approximately (700 nm), whereas the FTO-coated glass sample had 25 nm diameter and average length of approximately 950 nm. The direct optical transition band gaps of the glass and FTO^_coated glass samples were( 4 and 4.43 eV), respectively. The structural and optical properties of the synthesized ZnO p

Thin films of pure and doped nano titanium dioxide (TiO2) were prepared using a chemical pyrolysis technique (CPS), with different nanosize graphene oxide (GO) concentrations in the range (3-9)wt%. The structural, morphological andoptical characteristics of these films were investigated. X-ray diffraction (XRD) technique measurements revealed that the structure properties of TiO2have polycrystalline structure with anatase phase. AFM analysis showed the grain size of TiO2 films with different concentrations was decreased after doping with high concentration of GO ratio. Roughness of these films decreased too after adding of GO impurity for all films from (7.65-5.6)nm except 5wt% percentage where increased to 13.7nm. Optical

The new organic reagent 2-[Benzo thiazolyl azo]-4,5-diphenyl imidazole was prepared and used as complexing agent for separation and spectrophotometric determination of Cu2+ ion in some samples include plants, soil, water and human blood serum. Initially determined all factors effect on extraction method and the results show optimum pH was (pHex=9), optimum concentration was 40?g/5mLCu2+ and optimum shaking time was (15min.), as well stoichiometry study appears the complex structure was 1:1 Cu2+: BTADPI. Interferences effect of cations were studied. Synergism effect shows MIBK gave increasing in distribution ratio (D). Organic solvent effect appears there is no any linear relation between dielectric constant for organic solvent used and dis

Recently, a great rise in the population and fast manufacturing processes were noticed. These processes release significant magnitudes of waste. These wastes occupied a notable ground region, generating big issues for the earth and the environment. To enhance the geotechnical properties of fine-grained soil, a sequence of research projects in the lab were conducted to analyze the impacts of adding sludge waste (SW). The tests were done on both natural and mixed soil with SW at various proportions (2%, 4%, 6%, 8%, and 10%) based on the dry mass of the soil used. The experiments conducted focused on consistency, compaction, and shear strength. With the addition of 10% of SW, the values of LL and PI decreased by 29.7% and 3

Introduction: Nitrofurantoin (NFT) is abroad spectrum bactericidal antibiotic. The bioavailability of NFT is affected by many factors. Samafurantin® tablets containing 50 mg NFT were manufactured by Samarra drug industry. Urinary excretion studies were employed since; the urinary tract is the main site of NFT action and excretion. Objective: The objective of the study was to investigate the effect of Uricol® and food on secondary pharmacokinetic parameters of Samafurantin® tablets with different doses by applying urinary data. Methods: Twelve healthy male volunteers participated in this study. Urine samples were collected from each volunteer after overnight fasting at a specified time intervals which considered as a blank sample for meas

In the present work, HgBa2Can-1CunO2n+2+δ superconducting thin films with (100) nm thickness were (n=1, 2 and 3) prepared by Pulsed Laser Deposition technique on glass substrate at R.T (300) K, have been synthesize. The effect of Cu content on the structural, surface morphology, optical and electrical properties of HgBa2Can-1CunO2n+2+δ films were investigated and analyzed. The results of XRD analysis show that all samples are polycrystalline structure with orthorhombic phase, the change of Cu concentration in samples produce changes in the mass density, lattice parameter and the ratio (c/a). AFM techniques were used to examine the surface morphology of HgBa2Can-1CunO2n+2+δ superconducting films, the study showed the values of surface rou

This study was design to investigate the dimensional stability of heat-activated acrylic resin with different methods of flask cooling (15 minutes rapid cooling, one hour bench cooling, four hours delayed deflasking, and 24 hours delayed deflasking) at different time intervals (immediately, two days, seven days, 30 days) after deflasking. Heat-activated acrylic resin was used to prepare acrylic samples. Then, measurement of the distances where achieved between the centers of selected marks in the acrylic samples. They were measured at different time intervals for different methods of flask cooling. The results showed that the group samples of the four hours and 24 hours of delayed deflasking was insignificantly different from the control an