This study aimed to see how allicin (45mg/kg BW) affected diabetic Mellitus in male rats (DM). Forty male rats were utilized, and they were split into four groups at random for 42 days. T2 was treated with 45 mg/kg B.W of allicin dissolved in 1 ml of D.W daily and injected with a single dose of sodium citrate buffer (0.5ml Intra-Peritoneal IP), DM was induced in T1 and T2 by injection of a single dose of streptozotocin 50 mg/kg B.W IP, T1 was assigned as a positive control, T3 received 45 mg/kg B.W. of allicin dissolved in 1 ml D.W. every day, and a single dose of sodium citrate buffer was injected (0.5ml IP). When diabetic rats treated with allicin in T2 were compared to diabetic rats in T1, the findings indicated a significant increase (P0.05) in body weight growth, insulin, total protein, and albumin, better lipid profile, and reduced glucose concentration. Histological investigations revealed that the island of Langerhans had atrophy and necrosis in the exocrine tissue in the T1 group, whereas the T2 group had a large island of Langerhans. The findings in the T3 group marked hyperplasia of the island of Langerhans. The 45mg/kg, B.W. of allicin, has a hypoglycemic effect and elevates the expression level of insulin and pancreas tissue protection effect when used orally in adult rats at the given dose for forty-two days.
بهذا البحث نقارن معاييرالمعلومات التقليدية (AIC , SIC, HQ , FPE ) مع معيارمعلومات الانحراف المحور (MDIC) المستعملة لتحديد رتبة انموذج الانحدارالذاتي (AR) للعملية التي تولد البيانات,باستعمال المحاكاة وذلك بتوليد بيانات من عدة نماذج للأنحدارالذاتي,عندما خضوع حد الخطأ للتوزيع الطبيعي بقيم مختلفة لمعلماته
... Show More
The photonconductor detectors CdSe:Cu was fabricated as a thin film of (1 μm) in thickness using vacuum evaporation technique. doping with copper was made using vacuum annealing at 350oC under argon atmosphere . The spectral responsivity and spectral detectivity of the detector were determined as a function of incident wavelength on the sample. A remarkable improvement in performance was absorbed for the specimen, which doping with (1-5 wt%) Cu.
The spectral response increases with increasing of wavelength for incident radiation to maximum value, after that , it reduced sharply . There is a shifting for peak responsivity indirect of higher wavelength. The detectivity was increased with doping but its decreased as the concentration in
Investigation of the adsorption of acid fuchsin dye (AFD) on Zeolite 5A is carried out using batch scale experiments according to statistical design. Adsorption isotherms, kinetics and thermodynamics were demonstrated. Results showed that the maximum removal efficiency was using zeolite at a temperature of 93.68751 mg/g. Experimental data was found to fit the Langmuir isotherm and pseudo second order kinetics with maximum removal of about 95%. Thermodynamic analysis showed an endothermic adsorption. Optimization was made for the most affecting operating variables and a model equation for the predicted efficiency was suggested.
Two grades of paving asphalt with penetration of 46 and 65 are studied for determining changes in their physical and chemical properties caused by ageing.
The ageing process has been conducted on two petroleum paving asphalt cement using thin film oven test at 150, 163 and 175 C, and ageing time 5, 10,15, 20, 25 and 30 hours. The effect of ageing time and temperature on penetration, kinematic viscosity, softening point, solubility in trichloroethylene, heat loss and changes in chemical composition are investigated. The results of thin film oven test process indicte that the asphaltenes concentration of all aged asphalt increases with increasing ageing time, while the opposite was observed for polar-aromatic and naphthene-aromatic. The
The electrical properties of the AlNiCo thin films with thickness (1000oA) deposited on glass substrates using Ion – Beam sputtering (IBS) technique under vacuum <10-6 torr have been studied . Also it studied the effect of annealing temperature from this films , It is found that the effective energy decrease with increase of temperature and the conductivity decrease with increase temperature 323oK but after this degree the conductivity increasing .