The Asphalt cement is produced as a by-product from the oil industry; the asphalt must practice further processing to control the percentage of its different ingredients so that it will be suitable for paving process. The objective of this work is to prepare different types of modified Asphalt cement using locally available additives, and subjecting the prepared modified Asphalt cement to testing procedures usually adopted for Asphalt cement, and compare the test results with the specification requirements for the modified Asphalt cement to fulfill the paving process requirements. An attempt was made to prepare the modified Asphalt cement for pavement construction in the laboratory by digesting each of the two penetration grade Asphalt c

Unsaturated polyester toughened Epoxy was developed. Epoxy resin had toughened by weight fraction of 10, 20, 30, and 40 wt. % unsaturated polyester. FTIR spectroscopy has been used to investigating the intermolecular hydrogen bonding. Unsaturated polyester–epoxy matrices were characterized for their thermal properties. The FTIR test detected a peak shift of the functional groups which can explain cross-linking occurs between the two resins. The crosslinking between epoxy and unsaturated polyester confirmed via the existence of the stretching asymmetrical C-C band and contraction of the  C-O band. The DSC test demonstrated that glass transition temperature value decreases with epoxy strengthening. The specific heat capacity and the

The effect of annealing temperature (Ta) on the electrical properties like ,D.C electrical conductivity (σ DC), activation energy (Ea),A.C conductivity σa.c ,real and imaginary (ε1,ε2) of dielectric constants ,relaxation time (τ) has been measured of ZnS thin films (350 nm) in thickness which were prepared at room temperature (R.T) using thermal evaporation under vacuum . The results showed that σD.C increases while the activation energy values(Ea) decreases with increasing of annealing temperature.(Ta) from 303- 423 K .
The density of charge carriers (nH) and Hall mobility (μH) increases also with increasing of annealing temperature Hall effect measurements showed that ZnS films were n-type converted to p-type at high annealin

Cadmium Oxide thin films were deposited on glass substrate by spray pyrolysis technique at different temperatures (300,350,400, 500)oC. The optical properties of the films were studied in this work. The optical band-gap was determined from absorption spectra, it was found that the optical band-gap was within the range of (2.5-2.56)eV also width of localized states and another optical properties.

High   Alumina   Glasses   "Alumina   Silicate   Glasses"   was prepared by utilizing powder technology technique. The starting materials are wasted soda-lime glass from an industrial site, Iraqi­ Duekhla raw kaolin and small amounts of potassium carbonates.

X-ray Diffraction and FTIR analysis show complete vitreous glasses are obtained. Increasing Alumina content plays an obvious role in improving physical and mechanical properties of the prepared high  alumina  glass.   In  addition,  the   increased  alumina  content enhanced the dielectric constant and reduced dielectric loss. These results may be interpreted as du

Chalcogenide glasses SeTe have been prepared from the high purity constituent elements .Thin films of SeTe compound have been deposited by thermal evaporation onto glass substrates for different values of film thickness . The effect of varying thickness on the value of the optical gap is reported . The resultant films were in amorphous nature . The transmittance spectra was measured for that films in the wavelength range (400-1100) nm . The energy gap for such films was determined .

The paper aims at investigating the content of particles and minerals of soft clay soil in the Mekong Delta coastal provinces, southern Vietnam, as well as improving soil stability using inorganic adhesives, i.e.lime and cement-based stabilization. To study the composition of soft clay soil, a series of different laboratory methods were carried out and revealed various characteristics related to mineral composition, pH value, soluble salt content, and grain particle composition of soft clay soils. The results demonstrated five soil subtypes, namely high – saline soil (S2), low-saline soil (S1), acid sulfate soil (A), acid sulfate - saline soil (S-A), soil without salt and
acid sulfate content (S0- A0). The soft clay soil (C) in

This study investigates the ionic conduction dependence on the size of alkaline cations in gel polymer electrolytes based on double iodide can enhance by incorporating a salt having a bulky cation.

Soil resistivity depends on many overlapping factors, which influence it in various ways. The aim of this study was to determine the effects of some physical and chemical factors on soil apparent resistivity. The results of field, laboratory, and statistical studies revealed a complex relationship between water content, pH, and salinity with soil apparent resistivity. The results showed that water content had a clear effect on apparent resistivity, as it increased significantly when water content value decreased to less than about 5%. The results also showed that increasing the salinity ratio at the expense of water content led to an increase in the apparent resistivity values. The apparent resistivity values also increased significantly

Cadmium oxide (CdO) thin films were deposited using the sequencing ion layer adsorption and reaction (SILAR) method. In this study, the effect of the pH value of an aqueous solution of cadmium acetate at a concentration of 0.2 mol of the cadmium oxide film was determined. The solution source for the cadmium oxide film was cadmium ions and an aqueous ammonia solution. The CdO films were deposited on glass substrates at a temperature of 90 ℃. The cadmium oxide film thickness was determined by the weight difference method at pH values ​​(7.2, 8.2). X-ray diffraction (XRD) and scanning electron microscopy (SEM) showed that the size of the crystals increased with the increase in the solution (pH). While the UV-visible spectra of the fil