In this paper we study the effect of adding Zinc Oxide powder (ZnO) at different ratios (10%,20%,30%,40%,50%) as particles and organic dyes rhodamine B(RhB), rohdamine 6G(Rh6G) and eosin(EO) are added at different doping ratios to polystyrene (PS), to form photosensitized(PS/ZnO/dye) composites, for samples were prepared as films by spin method. Photoconductive properties are investigated.     For I-V characteristic measurements, the photocurrent (Iph) and dark current (Id) are generally increased in non linear behavior with increasing light intensity and applied voltage for all composites. The photocurrent goes decrease through its maximum value at high white light intensities or high voltage for 2.4*10-

Thin films of vanadium oxide nanoparticles doped with different concentrations of europium oxide (2, 4, 6, and 8) wt % are deposited on glass and Si substrates with orientation (111) utilizing by pulsed laser deposition technique using Nd:YAG laser that has a wavelength of 1064 nm, average frequency of 6 Hz and pulse duration of 10 ns. The films were annealed in air at 300 °C for two hours, then the structural, morphological and optical properties are characterized using x-ray diffraction (XRD), Field emission scanning electron microscopy (FESEM) and UV-Vis spectroscopy respectively. The X-ray diffraction results of V2O5:Eu2O3 exhibit that the film has apolycrystalline monoclinic V2O5 and triclinic V4O7 phases. The FESEM image shows a h

A hybrid nanoparticles light emitting diode (NPs-LED) was fabricated as layers of ITO/TPD:PMMA/ Eu₂O₃ / Alq₃ / Al, by phase segregation method using spin coating technique. The NPs-LED hybrid device emitted light and consisted of three layers in a definite order placed on the transparent conducting oxide as an ITO substrate; the first layer was made of (N, N'-bis (3-methylphenyl) -N, N'-bis (phenyl) benzidine) (TPD) and polymethyl methacrylate (PMMA) polymers combined together. The second layer consisted of Europium (III) oxide (Eu₂O₃), while the third  layer was Alq₃, one of the most frequently-used electron transport layers.

The electroluminescence (EL) of N

Atherosclerosis is a condition of the hardening of a blood vessel via the development of plaques around the artery wall which causes the artery to narrow, leading to severe complications. Toxoplasmosis is an opportunistic parasitic infection that causes pathological complications in immunocompromised patients, which lead to increase the burden on the immune system in these patients. This study aims to assess the incidence rate of toxoplasmosis in atherosclerosis patients and its potential to change C - reactive protein (C-RP) and vitamin D3 levels. Serum samples (150) were tested for the positivity of anti-Toxoplasma IgG and IgM antibodies by means of Enzyme-linked immunosorbent assay (ELISA). In addition, C-RP was assessed in a

 The gas sensing properties of undoped Co₃O₄ and doped with Y₂O₃ nanostructures were investigated. The films were synthesized using the hydrothermal method on a seeded layer. The XRD, SEM analysis and gas sensing properties were investigated for the prepared thin films. XRD analysis showed that all films were polycrystalline, of a cubic structure with crystallite size of (12.6) nm for cobalt oxide and (12.3) nm for the Co₃O₄:6% Y₂O₃. The SEM analysis of thin films indicated that all films undoped Co₃O₄ and doped possessed a nanosphere-like structure.

The sensi

To determine the role of Epstien barr virus (EBV) in the pathogenesis of Rheumatoid arthritis (RA) , Reactive arthritis (ReA) and Ankylosing spondylitis (AS) patients, sixty-two patients (52 patients with RA ,five patients with ReA and five patients with AS) have been investigated. The mean age (47.3, 47.7, 34.5) of RA, ReA , AS respectively and compared to 24 apparently healthy individuals with the mean age 28.3. All the study groups were carried out to measure antibodies of EBV (VCA) IgG and IgM by enzyme-linked immunosorbent assay (ELISA) technique. The result showed that there was a highly significant elevation ( p< 0.01) in the concentration of EBV (VCA) IgG Ab compared to control group, while there was no significant different (

This paper studied the behaviour of reinforced reactive powder concrete (RPC) two-way slabs under static load. The experimental program included testing three simply supported slabs of 1000 mm length, 1000 mm width, and 70 mm thickness. Tested specimens were of identical properties except their steel fibers volume ratio (0.5 %, 1 %, and 1.5 %). Static test results revealed that, increasing steel fibers volume ratio from 0.5% to 1% and from 1% to 1.5%, led to an increase in: first crack load by (32.2 % and 52.3 %), ultimate load by (36.1 % and 17.0 %), ultimate deflection by (33.6 % and 3.4 %), absorbed energy by (128 % and 20.2 %), and the ultimate strain by (1.1 % and 6.73 %). The stiffness and ductility of the specimens also increased. A

This research foxed on the effect of fire flame of different burning temperatures (300, 400 and 500)oC on the compressive strength of reactive powder concrete (RPC).The steady state duration of the burning test was (60)min. Local consuming material were used to mixed a RPC of compressive strength around (100) MPa. The tested specimens were reinforced by (3.0) cm hooked end steel fiber of (1100) MPa yield strength. Three steel fiber volume fraction were adopted in this study (0, 1.0and 1.5)% and two cooling process were included, gradual and sudden. It was concluding that increasing burning temperature decreases the residual compressive strength for RPC specimens of(0%) steel fiber volume fraction by (12.16, 19.46&24.49) and (18.20, 27.77 &3

The construction of highly safe and durable buildings that can bear accident damage risks including fire, earthquake, impact, and more, can be considered to be the most important goal in civil engineering technology. An experimental investigation was prepared to study the influence of adding various percentages 0%, 1.0%, and 1.5% of micro steel fiber volume fraction (Vf) to reactive powder concrete (RPC)—whose properties are compressive strength, splitting tensile strength, flexural strength, and absorbed energy—after the exposure to fire flame of various burning temperatures 300, 400, and 500 °C using gradual-, foam-, and sudden-cooling methods. The outcomes of this research proved that the maximum reduction in mechanical prop