The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burn

  

To evaluate and compare serum Leptin hormone level between Iraqi male & female and the relation between this hormone & BMI in these two groups.

A total of 44 normal male & female subjects were included in this study

{Group 1 : 22 female } , { Group 2 : 22 male}.

Serum Leptin hormone ,BMI &fasting blood glucose were measured for both groups.

   Serum Leptin level in group 1 was (8.82 + 2.9 μg/L) where as in group 2 it was (4.65 + 3.2 μg/L) . These changes were statistically significant. Fasting blood glucose levels were technically within the normal value (

Ovarian cancer has a high mortality and delayed diagnosis. Several immunological alterations take place during ovarian carcinogenesis, and can be of value in the surveillance of the diseases. This research was conducted to evaluate serum immunoglobulin levels in women with ovarian cancer and to assess their role in disease process. The present study is composed of 85 women (mean age = 62.03±12.4 yrs) with clinically and pathologically confirmed ovarian cancer and 65 healthy females as a control group (mean age = 61±12.1 yrs). ELISA test was achieved for the determination of serum [IgG, IgA, IgM]. The findings of current study illustrated significant (P=0.001) increase in serum IgG, IgA, and IgM levels as compared to co

          The research aims to determine the impact of Human Resources Accounting (HRA) on employee’s performance. The research’s problem was embodied in the lack of interest in HRA, which was reflected on the performance of employees in the Ministry of Education; the research adopted the descriptive-analytical approach, and the research community included the directors of departments and people at the headquarters of the Ministry of Education. The sample size was (224) individuals from the total community of 533. The questionnaire was adopted as the main tool for collecting data and information, as well as the interviews that were conducted by the researcher. In order to analyze t

Light naphtha treatment was achieved over 0.3wt%Pt loaded-alumina, HY-zeolite and Zr/W/HY-zeolite catalysts at temperature rang of 240-370°C, hydrogen to hydrocarbon mole ratio of 1-4 0.75-3 wt/wt/hr, liquid hourly space velocity (LHSV) and at atmospheric pressure. The hydroconversion of light naphtha over Pt loaded catalyst shows two main reactions; hydrocracking and hydroisomerization reactions. The catalytic conversion of a light naphtha is greatly influenced by reaction temperature, LHSV, and catalyst function. Naphtha transformation (hyroisomerization, cracking and aromatization) increases with decreasing LHSV and increasing temperature except hydroisomerization activity increases with increasing of temperature till 300°C then began

This paper aims to investigate the flexural behavior of reinforced concrete beams considering fire resistance by adding Lightweight Expanded Clay Aggregates (LECA) to the concrete mix as partial coarse aggregate replacement. LECA is a type of porous clay with a uniform pore structure with fine, closed cells and hard, tightly sintered skin. The experimental work comprised four reinforced self-compacted concrete beams. All the specimens were identical in their geometrical layout of 1600×240×200 mm, reinforcement details, and support condition (simply supported). For all the beams, the main reinforcement was provided by two bars, each having a diameter of 12 mm, while a bar of 6 mm diameter was employed for the top and shear reinforc