The enhancement of ZnSe/Si Heterojunction by adding some elements (V, In and Cu) as impurities is the main goal because they contribute to the manufacturing of renewable energy equipment, such as solar cells. This paper describes the preparation of thin films ZnSe with V, In and Cu doped using thermal evaporation method with a vacuum of 10–5 Torr. The thin film was obtained from this work could be applied in heterojunction solar cell because of several advantages including high absorption coefficient value and direct band gap. The samples prepared on a glass and n-type Si wafer substrate. These films have been annealed for 1 h in 450 K. X-ray diffraction XRD results indicated that ZnSe thin film possesses poly-crystalline structure after

Ag-doped NiO thin films were fabricated by dip coating and subsequently annealed at 373, 473, 573, and 673 K to elucidate the influence of annealing temperature on their structural, morphological, optical, and NO2-sensing characteristics. X-ray diffraction confirmed the formation of polycrystalline Ag/NiO films, with progressively improved crystallinity and larger crystallite size at elevated annealing temperatures. Atomic force microscopy revealed a homogeneous surface morphology with grain growth, with the average grain diameter increasing from 26.40 to 34.2 nm. Optical analysis showed high visible-region transmittance (65–70%) and a gradual reduction in the optical band gap from 2.75 to 2.07 eV with increasing annealing temperature. Ga

􀀤􀁅􀁖􀁗􀁕􀁄􀁆􀁗􀀑􀀃􀀬􀁑􀀃􀁗􀁋􀁌􀁖􀀃􀁕􀁈􀁖􀁈􀁄􀁕􀁆􀁋􀀏􀀃􀀤􀁊􀀤􀁏􀀔􀀐􀁛􀀬􀁑􀁛􀀶􀁈􀀕􀀃􀀋􀀤􀀤􀀬􀀶􀀌􀀃􀁆􀁒􀁐􀁓􀁒􀁘􀁑􀁇􀀃􀁄􀁏􀁏􀁒􀁜􀁖􀀃􀁓􀁕􀁈􀁓􀁄􀁕􀁈􀁇􀀃􀁉􀁒􀁕􀀃􀁇􀁌􀁉􀁉􀁈􀁕􀁈􀁑􀁗􀀃􀁛􀀃􀀋􀀓􀀑􀀖􀀏􀀃􀀓􀀑􀀙􀀃􀁄􀁑􀁇􀀃􀀓􀀑􀀜􀀌􀀃􀁅􀁜􀀃􀁐􀁈􀁏􀁗􀁌􀁑􀁊􀀃 􀁗􀁋􀁈􀁐􀀃 􀁌􀁑􀀃 􀁄􀁑􀀃 􀁈􀁙􀁄􀁆􀁘􀁄􀁗􀁈􀁇􀀃 􀁔􀁘􀁄􀁕􀁗􀁝􀀃 􀁗􀁘􀁅􀁈􀀃 􀀋􀀕􀀑􀀘􀀍􀀔􀀓􀀐􀀖􀀃 􀁗􀁒􀁕􀁕􀀌􀀑􀀃 􀀤􀀤􀀬􀀶􀀃 􀁚􀁌􀁗􀁋􀀃 􀁇􀁌􀁉􀁉

ZnTe possesses the proper optoelectronic properties as a candidate for device development. The structure and optical properties of ZnTe semiconductor thin films of 500 nm were studied using thermal evaporation technique. The influence of annealing temperatures on ZnTe thin films in the range ( R.T - 473 K). XRD and surface morphological analyses are used to examine the films. The ZnTe films are comparatively polycrystalline and cubic in phase, according to the XRD analysis. with a lattice constant of 0.61 nm upon an (111) orientation. The intensities of all the peaks rapidly increase though they show the same tendencies; it shows the crystallinity of the films becomes higher crystal size diameters (from 8.41 to 12.18nm) both increas

Cadmium sulfide and Aluminum doped CdS thin films were prepared by thermal evaporation technique in vacuum on a heated glass substrates at 373K. A comparison between the optical properties of the pure and doped films was made through measuring and analyzing the transmittance curves, and the effect of the annealing temperature on these properties were estimated. All the films were found to exhibit high transmittance in the visible/ near infrared region from 500nm to 1100nm.The optical band gap energy was found to be in the range 2.68-2.60 eV and 2.65-2.44 eV for CdS and CdS:Al respectively , with changing the annealing temperature from room temperature to 423K.Optical constants such as refractive index, extinction coefficient, and complex di