Background: Pit and fissure sealant have been considered an outstanding adjunct to oral health care in the decrease of occlusal caries onset and low progression. The aims of this in vitro study were to evaluate the marginal microleakage of three different types of fissure sealants (SDI, Tg and tetric N-flow) by time interval, one day and 45 days, in the presence or absence of bonding agent among maxillary and mandibular teeth. Materials and methods: Seventy two sound human maxillary and mandibular first premolar teeth were collected which were free from obvious carious lesions. The teeth were randomly divided into two main equal groups, group (1) and group (2), each group consists of (36) teeth involving equal numbers of maxillary and mandi

This study was carried out to evaluate the hepato-protective property of (Arachis hypogea L.) peanut skin extracts in CCl4 induced hepatotoxicity in mice. The antioxidant activity was measured utilizing 2, 2-diphenyl-1-1 picrylhydrazyl (DPPH) radical scavenging capacity. The results showed that the methanolic extract was the highest free radical scavenging activity than the aqueous extract with values (92.34 ± 0.45 and 87.62 ± 0.44) respectively in 12 mg/mL compared to 89.61 ± 0.34 for Butylated hydroxytoluene (BHT) and 93.25 ± 0.06 for vitamin C, which means that the methanolic extract of peanut skin is superior to BHT. Furthermore, the total phenolic content was analyzed by using Folin-Ciocalteu method, the amount of total phenol in a

This study included preparation for the unsaturated polyester samples before and after reinforced by Alumina oxide powder and copper oxide powder of different volume fraction amounting (3%,5%,8%). And this reearch included study of some of mechanical properties such as (hardness,compressive and wear).The results showed that increase of the hardness and compressive strength after the reinforced and increase with the volume fraction increase.As the wear test show that the wear rate increases with applied load from the different load(5,10,15)N,and the wear rate decreases with the volume fraction increase.

In this research, the effect of each of the concentrations ( Nd⁺³) was studied (N) the thickness of the thin disk (d) the number of times that the pumping beam passes through the effective medium of this laser (M_p) the reflectivity of the laser output mirror (R ₂₎ The losses of the effective medium (L) and the pumping power used in achieving the reverse qualification (P_P) on each of the pumping threshold capacities (P_p.th) and the output power of the laser (P_out) and the efficiency (ŋ) in Nd³⁺ thin-disk lasers (TDLs) pumping quasi-three-level With continuous operation (cw), at room temperature, and in the Gaussian mode (TEM00),

We found under these opera

Background: The bond strength of root canal sealers to dentin was important for maintaining the integrity of the seal in root canal filling in both static and dynamic situations. In a static situation, it should eliminate any space that allowed the percolation of fluids between the filling and the wall while in a dynamic situation; it was needed to resist dislodgement of the filling during subsequent manipulation. Materials and Methods: Forty mandibular premolars were selected for this study. All canals were instrumented using ProTaper rotary instruments. Instrumentation was done with copious irrigation of 5.25% sodium hypochlorite. Roots were randomly divided into four groups according to the type of cleaning and method of root canal irrig

Background: Implant stability is a mandatory factor for dental implant (DI) osseointegration and long-term success. The aim of this study was to evaluate the effect of implant length, diameter, and recipient jaw on the pre- and post-functional loading stability. Materials and methods: This study included 17 healthy patients with an age range of 24-61 years. Twenty-two DI were inserted into healed extraction sockets to replace missing tooth/ teeth in premolar and molar regions in upper and lower jaws. Implant stability was measured for each implant and was recorded as implant stability quotient (ISQ) immediately (ISQ0), and at 8 (ISQ8) and 12 (ISQ12) weeks postoperatively, as well as post-functional loading (ISQPFL). The pattern of implant

The emergence of mixed matrix membranes (MMMs) or nanocomposite membranes embedded with inorganic nanoparticles (NPs) has opened up a possibility for developing different polymeric membranes with improved physicochemical properties, mechanical properties and performance for resolving environmental and energy-effective water purification. This paper presents an overview of the effects of different hydrophilic nanomaterials, including mineral nanomaterials (e.g., silicon dioxide (SiO2) and zeolite), metals oxide (e.g., copper oxide (CuO), zirconium dioxide (ZrO2), zinc oxide (ZnO), antimony tin oxide (ATO), iron (III) oxide (Fe2O3) and tungsten oxide (WOX)), two-dimensional transition (e.g., MXene), metal–organic framework (MOFs), c

A hand lay-up method was used to prepare Epoxy/ metal composites. Epoxy resin (EP) was used as a matrix with metal particles (Al, Cu, and Fe) as fillers.
The preparation method includes preparing square panels of composites with different weight percentage of fillers (10, 20, 30, 40, and 50%). Standard specimens (88mm in diameter) for thermal conductivity tests were prepared to measure thermal conductivity kexp.The result of experimental thermal conductivity kexp, for EP/metal composites show that, kexp increase with increasing weight percentage, For EP/ Al and EP/Cu composites, and it have have maximum values of 0.33 and 0.35 W/m.K, respectively. While kexp for EP/ Fe composite show slight increase with maximum value of 0.186 W/m.K.

The study concern with the preparation of three type of mixtures; which are prepared from different percentage of polyvenil Butyral, Di-n-butyl phathalate and paraffin wax pastillated. The solvent used is Xylolzul analyses. After washing, Drying and milling the kaolin Dukhla, as a matrix in this study, and by using sieving Tech. The range of particle size used is less than and less than as a mesh batch. The added percentage from prepared mixture were 5% and 10% to 95% and 90% of the matrix respectively. Then disk samples were prepared by using a compaction pressure with heating. After cooling and drying the samples were undergo heat treatment in the range of (1250 – 1350) oC. The measurement of shrinkage and Dielectric properties sho