In this paper, the behavior of spliced steel girders under static loading is investigated. A group of seven steel I-girders were tested experimentally. Two concentrated loads were applied to each specimen at third points and the load was increased incrementally up to the yield of the specimen. Two types of splices were considered; the bearing type and the friction-grip type splices. For comparison, an analytical study was made for the tested girders in which the finite element analysis program (Abaqus) was used for analysis. It was found that the maximum test load for spliced girders with bearing type splices was in the range of (34%) to (67%) of the maximum test load for the reference girder. For girders spliced by using friction-grip t

The polymeric hydrogels composed of poly vinyl alcohol (m.wt 72000) and glutaraldehyde(5%,8% and 10%) , have been thermally prepared for the purpose of studying their swelling and drug release behavior . The swelling ratio was measured for all the hydrogel samples at 37°C, in three different media pH (1.2, 4.7 and 6.8) as a function of time. The results show that the maximum swelling ratios were arranged as follows :pH =6.8 > pH =4.7 > pH =1.2 hydrogels cross linked PVA showed a typical pH responsive behavior such as high pH has maximum swelling while low pH shows minimum swelling.

All the stiffened and unstiffened elastic constants for lead germanate (Pb5Ge3O11) single
crystal have been measured from room temperature 298 K up to 513K by using ultrasonic
pulse superposition technique. The correction of piezoelectric stiffening has been used to
obtain the unstiffened elastic constants. Elastic moduli of lead germanate (C11, C33, C12, C13,
C44 and C66) decrease with the increase of temperature. C11, C33, C
12 and C13 suffered a dip at
transition temperature but they increase with the increase of temperature just above Curie
temperature between 453 and 473 K because of their positive temperature coefficients in this
range, and then decrease slightly (except C12 increases) in the

             The polymeric hydrogels composed of poly vinyl alcohol (m.wt 72000) and glutaraldehyde(5%,8% and 10%) , have been thermally prepared for the purpose of studying their swelling and drug  release behavior .      The swelling ratio was measured for all the hydrogel samples at 37°C, in three different media pH (1.2, 4.7 and 6.8) as a function of time. The results show  that the maximum swelling ratios were arranged as follows :pH =6.8 >  pH =4.7 > pH =1.2 hydrogels cross linked PVA showed a typical pH  responsive behavior such as high pH has maximum swelling while low  pH  shows minimum swelling.

This paper is an attempt to demonstrate the syntactic behavior of -ly adverbs and -ly adjectives. It mainly deals with -ly as an inflectional suffix that forms adverbs and adjectives It is hypothesized that there are differences between adjective-forming –ly and adverb-forming –ly.The researcher first made general and specific observations about the morphological processes of -ly adverbs and -ly adjectives. Since the study focuses on a linguistic phenomenon, its data is a set of -ly adverbs and -ly adjectives used as examples to support the hypothesis. The importance of studying the syntactic behavior of -ly stems from the fact that thousands of English adjectives and adverbs are created by adding the suffix "-ly" to their roots

Six proposed simply supported high strength-steel fiber reinforced concrete (HS-SFRC) beams reinforced with FRP (fiber reinforced polymer) rebars were numerically tested by finite element method using ABAQUS software to investigate their behavior under the flexural failure. The beams were divided into two groups depending on their cross sectional shape. Group A consisted of four trapezoidal beams with dimensions of (height 200 mm, top width 250 mm, and bottom width 125 mm), while group B consisted of two rectangular beams with dimensions of (125 ×200) mm. All specimens have same total length of 1500 mm, and they were also considered to be made of same high strength concrete designed material with 1% volume fraction of steel fiber.

Improving the accuracy of load-deformation behavior, failure mode, and ultimate load capacity for reinforced concrete members subjected to in-plane loadings such as corbels, wall to foundation connections and panels need shear strength behavior to be included. Shear design in reinforced concrete structures depends on crack width, crack slippage and roughness of the surface of cracks.

This paper illustrates results of an experimental investigation conducted to investigate the direct shear strength of fiber normal strength concrete (NSC) and reactive powder concrete (RPC). The tests were performed along a pre-selected shear plane in concrete members named push-off specimens. The effectiveness of concrete compressiv

The study's objective is to produce Nano Graphene Oxide (GO) before using it for batch adsorption to remove heavy metals (Cadmium Cd⁺², Nickel Ni⁺², and Vanadium V⁺⁵) ions from industrial wastewater. The temperature effect (20-50) °C and initial concentration effect (100-800) mg L^-1 on the adsorption process were studied. A simulation aqueous solution of the ions was used to identify the adsorption isotherms, and after the experimental data was collected, the sorption process was studied kinetically and thermodynamically. The Langmuir, Freundlich, and Temkin isotherm models were used to fit the data. The results showed that Cd, Ni, and V ions on the GO adsorbing surface matched the Langmuir mo