This thesis aims to study the effect of addition polymer materials on mechanical properties of self-compacting concrete, and also to assess the influence of petroleum products (kerosene and gas oil) on mechanical properties of polymer modified self-compacting concrete (PMSCC) after different exposure periods of (30 ,60 ,90 ,and 180 days).

Two type of curing are used; 28 days in water for SCC and 2 days in water followed 26 days in air for PMSCC.

The test results show that the PMSCC (15% P/C ratio) which is exposed to oil products recorded a lower deterioration in compressive strength's values than reference concrete. The percentages of reduction in compressive strength values of PMSCC (15% P/C ratio) was

solation of candida spp. From cancer patients who suffered oral candidiasis due to immunodeficiency

An experimental program was conducted to determine the residual of composite Steel Beams-Reinforced Concrete (SB-RC) deck floors fabricated from a rolled steel beam topped with a reinforced concrete slab, exposed to high temperatures (fire flame) of 300, 500, and 700ºC for 1 hour, and then allowed to cool down by leaving them in the lab condition to return to the ambient temperature. The burning results showed that, by exposing them to a fire flame of up to 300ºC, no serious permanent deflection occurred. It was also noticed that the specimen recovered 93% of 19.2 mm of the deflection caused by burning. The recovered deflection of burned composite SB-RC deck floor at 500ºC was 40% of 77.9 mm of the deflection caused by burning with a res

The numerical analysis was conducted to studying the influence of length to diameter ratio (L/D) on the behavior of the soil treated with sand columns treated with 8% sodium silicate for both floating and end bearing type by using finite element method (Plaxis 3D Foundation ) for isolated foundation of real dimensions. The analysis’s study indicate that in the floating type the best improvement ratio was achieved at (L/D=8) when using columns with a diameter of (0.5, 0.7), but when using columns with a diameter of 0.3 m, it was noticed that the bearing improvement ratio increases with increasing (L/d). While the results of the analysis for end bearing type show that the higher improvement ratio was achieved at (L/D=4) when using columns w

Background: Bloody diarrhea plays a major role in
morbidity and mortality especially in developing
countries, it is usually a sign of invasive enteric
infection, there is a thought that amoebic dysentery is
more common than bacillary dysentery in Iraq, and
from 1989 to 1997 amoebic dysentery increase from
20000to 550000 patients.
Objectives: This study aims to:
1. Outline the incidence of various infectious causes of
bloody diarrhea in Erbil district.
2. Assess the effect of multiple factors like age, sex,
source of water supply, etc... On the incidence of
amebic and bacillary dysentery.
3. To provide baseline data for making strategic plan to
reduce the diarrhoeal mortality and morbidity.
Met

This research presents and discuss the results of experimental investigation carried out on geogrids model to study the behavior of geogrid in the loose sandy soil. The effect of location eccentricity, depth of first layer of reinforcement, vertical spacing, number and type of reinforcement layers have been investigated. The results indicated that the percentage of bearing improvement a bout (22 %) at number of reinforced layers N=1 and about (47.5%) at number of reinforced layers N=2 for different Eccentricity values when depth ratio and vertical spacing between layers are (0.5B and 0.75B) respectively

ABSTRACT : Fifteenth isolates of C. sakazakii were obtained from previous studies of the sample (infant formula, cerebrospinal fluid and blood). All isolates C. sakazakii identification based on microscopic, biochemical test and confirmed by 16SrRNA. We studied the movement of all isolates and study adhesion to polystyrene plate, adhesion and invasion to Esophageal adenocarcinoma (SKG-GT-4) for four isolates [Cerebrospinal fluid (CSF5), Bloods (B 1), Dialak (A1c), Novolac Allernova (C1)] and its cytotoxicity. Results showed that all isolates can move after 4 hours of incubation and increased after 8 hours, the isolates moved to different distances strong, medium, and weak. The results showed that the number of C. sakazakii colony adherent t

Static loads exposing to mechanical components can cause cracks, which are lead to form stress concentration regions causing the failure of structure. Generally, from 80% to 90% of structure failure is due to initiation of the cracks. Therefore, it is necessary to repair the crack and reduce its effect on the structure where the effect of the crack is modelled as an additional flexibility to the structure. In the last few years, piezoelectric materials have been considered as one of the most favourable repairing techniques. The piezoelectric material converts the applied voltage on it to a bending moment to counter the bending moment caused by the external load on the beam at the crack location. In this study, the design of the piez