Objectives: The purpose of this in vitro study was to compare the effect of adding a poloxamer surfactant to the irrigant solutions on its cleaning efficiency. Design: In this study the roots of extracted permanent premolar teeth were used and evaluated by using Scanning Electronic Microscopy (SEM). Materials and Method: 72 human single tooth of permanent premolar (8 for each group) were used in this in vitro study. Roots after sectioning at cervical area to get 15 mm were embedded in a plastic container filled with impression silicon, then instrumented with ProTaper rotary instruments till size F4. Each group (8 root) were irrigated with one of the nine solutions used in study: three concentrations of NaOH [5% (A1), 2.5%(A2), 0.5%(A3)], th

The anatomic characteristics of the leaves of 22 taxa of Stachys L. representing seven of the currently recognized sections distributed in northern Iraq, were examined. The study did not found any variations in the characteristics of the stomata system of the leaves.Therewere variations with a good taxonomic value in other anatomic characteristics.Thevariations in characters of the mesophyll tissue in S.kurdica var.brevidens Bom ex Bhattacharjeewas bifacial but in S.kurdica var.kurdica Boiss. & Hohen.was unifacial .The study also found that the taxa S.benthamiana Bioss., S.lanigera (Bornm.) Rech.f. andS.kotscyi Bioss. with 3 vascular bundles in the middle vein while the taxa S.ballotiformis Vatke., S.megalodonta Hausskn. &Bornm.exP.H.Davis

An effort is made to study the effect of composite nanocoating using aluminum-9%wt silicon alloys reinforced with different percentage (0.5,1,2,4)wt.% of carbon nanotubes (CNTs) using  plasma spraying. The effect of this composite on corrosion behavior for AA6061-T6 by extrapolation Tafel test in sea water 3.5wt% NaCl was invested. Many specimens where prepared from AA6061-T6 by the dimension (15x15x3)mm as this first set up and other steps include coating process, X-ray diffraction and SEM examination .The results show the CNTs increase the corrosion rate of the nanocomposite coatings with increasing the weight percentage of CNTs within the Al-Si matrix. Al-9wt%Si coating layer itself has less corrosion rate if compared with both n

Abstract Twenty Bacillus isolated were obtained from different sample food and water. Bacillus B1 isolated was the highest asparaginase producer, it was identified as a strain of B. subtilis. The highest production of asparaginase was observed when mineral salt medium containing 0.3% asparagen, pH 8 and incubated at 40°c for 24 hrs. B. subtilis B1 cells were immobilized by entrapment methods (calcium alginate and agar), and by adsorption on solid surface such as sawdust and cotton. The result showed that the immobilized cells by adsorption on sawdust was the best, the immobilized cell retained 88% of asparginase activity after 48h while free cell retained 65%. Cells immobilized by adsorption on sawdust was incubated at different temperatu

The aim of this study is to understand the effect of addition carbon types on aluminum electrical conductivity which used three fillers of carbon reinforced aluminum at different weight fractions. The experimental results showed that electrical conductivity of aluminum was decreased by the addition all carbon types, also at low weight fraction of carbon black; it reached (4.53S/cm), whereas it was appeared highly increasing for each carbon fiber and synthetic graphite. At (45%) weight fraction the electrical conductivity was decreased to (4.36Scm) and (4.27Scm) for each carbon fiber and synthetic graphite, respectively. While it was reached to maximum value with carbon black. Hybrid composites were investigated also; the results exhibit tha

Background: Failure of resin bases were a major disadvantage recorded in the constructed dentures. Reinforcements of the repair joint with nano fillers represent an attempt to enhance the strength and durability. The purpose of the research was to estimate the influence of nano fillers reinforcement with (ZrO2 and Al2O3) on impact and transverse strength of denture bases repaired with either cold or hot processing acrylic resin. Materials and methods: A hundred and forty (140) samples were processed with hot cured resin and organized in subgroups depending on the repair materials and condition (without repair (control), repair with hot cure, cold cure, hot and cold cure reinforced with either (5% Zr2O or 0.5% Al2O3). The samples in these

Alginate from Large brown seaweeds act as natural polymer has been investigated as polymer and has been added to concrete in different percentages ( 0% , 0.5% , 1% and 1.5% ) by the cement weight and the study show the effect of using alginate biopolymer admixtures on  some of the fresh properties of the concrete (slump &  the density  fresh) also in the hardened state (  Compressive strength , Splitting tensile strength  and Flexural strength ) at 28 days. The mix proportion was (1:2.26:2.26) (cement: sand: gravel) respectively and at constant w/c equal to 0.47. The results indicate that the use of alginate as a percent of the cement weight possess a positive effect on fresh properties of co