The objectives of this paper was the development of a novel ligand, L, which was achieved in two stages: ligand is synthesised by reducing the result of the reaction between cyclohexane-1,2-diamine and 4-hydroxy-3,5-dimethoxycy clohexane-1-carbaldehyde, followed by the production of the 4,4’-((1E,1’E)-(1,2 phenylenebis(azanylylidene))bis(methanylylidene))bis(2,6-dimethoxyphenol) precursor (P). While studying corrosion inhibition (copper alloy) in acid solution by weight loss, compounds were characterised using 1H, 13CNMR (for ligand (L) and (P)), FT-IR and UV spectra, melting point, molar conductivity, %C, %H and %N, %M, and magnetic susceptibility. The complex’s octahedral structure is inferred from the bidentate coordination of the metal ion. The molar ratio of type [Pt(L)Cl2 (H2 O)2 ] seemed to be 1:1(M:L). Using the weight loss method, the corrosion inhibitory ef fects of the platinum complex on copper alloy in a nitric acid solution (0.5 M HNO3 ) were studied. Adsorption of inhibitor molecules onto the surface of the copper alloy was the primary mechanism by which corrosion activity was reduced and active sites were blocked. The results demonstrated that the efficacy of inhibition was improved with increasing inhibitor concentrations. The inhibitor had its maximum inhibitory effectiveness of 97.5% at a concentration of 700 ppm. Calculated values of the Gibbs free energy corroborated with the results of adsorption investigations, which showed that the process mostly included physical adsorption and Langmuir adsorption iso therm. The development of protective coatings was validated by scanning electron microscopy analyses of surface morphology.
A new tool geometry was used to achieve friction stir spot welding (FSSW) in which the shoulder was designed separately from the rotating pin, and in order to examine weldment strength through the modified tool, a lap joints of AA2024 aluminum alloy plate 1 mm thick were welded successfully by using 6 mm pin diameter and varying process parameters (rotational speeds, tool nose geometry, and depth of tool penetration in the lower welded plate). Experimental tests indicate that the maximum average tensile shear load was 3100 N at the best selected condition. Microstructure examination and micro hardness test along the spot zones were investigated as well as measuring pin penetration load. Visual inspection of the welded spot surface shows a g
... Show More
(6)
(3)
(2)
(1)
Schiff base derived from PVA and Erythroascorbic acid derivative (pentulosono-ɣ-lactone-2, 3-enedianisoate) was synthesized and characterized by Thin Layer Chromatography (TLC) and FTIR spectra, aldehyde was also characterized by (U.V-Vis), 1HNMR, 13CNMR and mass spectra. The inhibitory effect of prepared polymer on the activity of human serum Cholinesrerase has been studied in vitro. The polymer showed a remarkable activity at low concentration (4.5*10-3 – 4.5*10-8 M).
(8)
(4)
(29)
(26)
The main factors that make it possible to get the corrosion of reinforcing steel in concrete are chloride ions and the absorption of carbon dioxide from the environment, and each of them works with a mechanism which destroys the stable immunity of rebar in the concrete. In this work the effect of carbon dioxide content in the artificial concrete solution on the corrosion behavior of carbon steel reinforcing bar (CSRB) was studied, potentiostatically using CO2 stream gas at 6 level of concentrations; 0.03 to 2.0 weight percent, and the effect of rising electrolyte temperature was also followed in the range 20 to 50ᴼ C. Tafel plots and cyclic polarization procedures were obeyed to investigate the c
... Show More
(14)
(2)
(3)
(2)
Background: The high reactivity of hydrogen peroxide used in bleaching agents have raised important questions on their potential adverse effects on physical properties of restorative materials. The purpose of this in vitro study was to evaluate the effect of in-office bleaching agents on the microhardness of a new Silorane-based restorative material in comparison to methacrylate-based restorative material. Materials and method: Forty specimens of Filtek™ P90 (3M ESPE,USA) and Filtek™ Supreme XT (3M ESPE, USA) of (8mm diameter and 3m height) were prepared. All specimens were polished with Sof-Lex disks (3M ESPE, USA). All samples were rinsed and stored in incubator 37˚C for 24 hours in DDW. Ten sample of each material were subjected to
... Show MoreBackground: Separation and deboning of artificial teeth from denture bases present a major clinical and labortory problem which affect both the patient and the dentist. The optimal bond strength of artificial teeth with denture base reinforced with nanofillers and flexible denture bases and the effect of thermo cycling should be evaluated. This study was conducted to evaluate and compare the shear bond strength of artificial teeth (acrylic and porcelain) with denture bases reinforced by 5% Zirconium oxide nanofillers and flexible bases under the effect of different surface treatments and thermo cycling and comparing the results with conventional water bath cured denture bases. Material and methods: Two types of artificial teeth; acrylic and
... Show More