A.C electrical conductivity and dielectric properties for poly
(vinyl alcohol) (PVA) /poly (ethylene oxide) (PEO) blends undoped
and doped with multi-walled carbon nanotube (MWCNTs) with
different concentrations (1, and 3 wt %) in the frequency range
(25x103 - 5x106 Hz) were investigated. Samples of (PVA/PEO)
blends undoped and doped with MWCNTs were prepared using
casting technique. The electrical conductivity measurements showed
that σA.C is frequency dependent and obey the relation σA.C =Aωs for
undoped and doped blends with 1% MWCNTs, while it is frequency
independent with increases of MWCNTs content to 3%. The
exponent s showed proceeding increase with the increase of PEO
ratio (≥50%) for undope

This research deals with increasing the hardening and insulating the petroleum pipes against the conditions and erosion of different environments. So, basic material of epoxy has been mixed with Ceramic Nano Zirconia reinforcement material 35 nm with the percentages  (0,1,2,3,4,5) %, whereas the paint basis of broken petroleum pipes was used  to paint on it, then it was cut into dimensions (2 cm. × 2 cm.) and 0.3cm high. After the paint and percentages are completed, the samples were immersed into the paint. Then, the micro-hardness was checked according to Vickers method and thermal inspection of paint, which contained (Thermal conduction, thermal flux and Thermal diffusivity), the density of the painted samples was calculate

Objective: The present study was aimed to develop a pH-triggered in situ gel for local release of lidocaine hydrochloride (lidocaine HCL) in the buccal cavity to improve the anesthetic effect of this amino amide drug which has very high water solubility. The formulations were introduced to the oral cavity as a spray to improve compliance and for easier administration.Methods: In this work, two grades of carbopol (934 and 940)-based in situ gel spray were designed. The formulations containing lidocaine HCl 5% were prepared by mixing different concentrations of carbopol with xanthan gum. Eight formulations were investigated and evaluated for gelation capacity, spray angle, volume of solution delivered per each actuation, rheological p

Over the last few years, there has been a worldwide increase in the use of composite materials for rehabilitation of deficient reinforced concrete structures. One important application of this technology is the use of Carbon Fiber Reinforced Polymer (CFRP) jacket to provide external confinement of reinforced concrete columns. Square concrete column specimens 100×100×1000 mm with concrete
compressive strength of about 30 and 50 MPa, steel fiber volume fraction 0%, 0.5%, 0.75%, and percentage of longitudinal reinforcement 2.01%, 3.14% and 4.52% were tested until failure in previous research. In this research seven tested columns were repaired and rehabilitated using one layer of CFRP flexible wraps and tested to determine their ultim

In wide range of chemical, petrochemical and energy processes, it is not possible to manage without slurry bubble column reactors. In this investigation, time average local gas holdup was recorded for three different height to diameter (H/D) ratios 3, 4 and 5 in 18" diameter slurry bubble column. Air-water-glass beads system was used with superficial velocity up to 0.24 m/s. the gas holdup was measured using 4-tips optical fiber probe technique. The results show that the axial gas holdup increases almost linearly with the superficial gas velocity in 0.08 m/s and levels off with a further increase of velocity. A comparison of the present data with those reported for other slurry bubble column having diameters larger than

In the present research synthesis and study of biological activity a series of new polymers modified of chitosan with compounds containing azo group. Beginning diazonium salt produced from 3,3'-dimethyl-[1,1'-biphenyl]-4,4'-diamine reacted with concentrated HCl acid and sodium nitrite. The coupling reaction between diazonium salt with substituted aromatic aldehyde to produce Azo derivatives )1-6(. Azo Schiff bases Chitosan )7-12( were synthesized by condensation of Chitosan with Azo derivatives )1-6( in ethanol with some drops of glacial acetic acid. The structural modifications of Chitosan ring (linked to a bioactive azo moiety) were expected to give new derivatives )7-12( with a diverse range of biological functions. These compounds' st

 في البحث الحالي تم تحضير ودراسة النشاط الحيوي لسلسلة من البوليمرات الجديدة المحورة  من الكيتوسان مع مركبات تحتوي على مجموعة الآزو. في البداية تم تحضير ملح الديازونيوم من  تفاعل  3,3'-dimethyl-[1,1'-biphenyl]-4,4'-diamine مع حامض الهيدروكلوريك المركز ونتريت الصوديوم .ثم تفاعل  الازدواج بين ملح  الديازونيوم مع الديهايدات اروماتية معوضة  لإنتاج مشتقات الازو (1-6). ازو شف بيس كيتوسان((12-7 والتي حضرت من تفاعل الكيتوسان مع مشتقات