The effect of micro-and nano silica particles (silica SiO2 (100 μm), Fused silica (12nm)) on some mechanical properties of epoxy resin was investigated (Young's modulus, Flexural strength). The micro-and nano composites were prepared by using three steps process with different volume fraction of micro-and nano particles (1, 2, 3, 4, 5, 7, 10, 15, and 20 vol. %). Flexural strength and Young's modulus of nano composites were increased at low volume fraction (max. enhancement at 4 vol.% ). However at higher volume fraction both Young's modulus and flexural strength decrease. Moreover, above, the mechanical properties are enhanced more than that of neat epoxy resin. The flexural strength decreases with increasing the volume fraction of micr

In this paper, a polymer-based composite material was prepared by hand Lay-up method consisting of epoxy resin as a base material reinforced by magnesium oxide powder once and silicon dioxide powder again and with different weight ratios (3, 6, 9 and 12) wt %. The three-point bending test was performed in normal conditions and after immersion in sulfuric acid. The results showed that the bending value decreased with the increase of the weighted ratio of the reinforcement material (MgO, SiO2). The Bending of samples reinforced by SiO2 was found to be less than the bending of samples reinforced by particles (MgO). For example, the bending of the SiO2 sample (0.32 mm) at the weighted ratio (3%) and for the MgO (0.18mm) sample at the weight

Hedera helix L. plant belongs to the family Araliaceae that provide a host of bioactive compounds (mainly saponins) of important biological activities, like spasmolytic, secretolytic, anti-inflammatory, and antibacterial activities. Literature survey revealed that there was no previously study concerning H. helix L. which is cultivated in Iraq, so we decided to carry out this study which include extraction, isolation, purification and identification of biologically important triterpenoid saponin hederacoside C from leaves of H. helix L. Extraction of hederacoside C was carried out using two methods; in the first method maceration  was done with methanol 99.8% and in the second method soxhlet extraction wit

The continuous pressure of work and daily life and the increasing financial and social stress that Iraqi women are experiencing (both inside and outside Iraq) is one of the main causes of anxiety, particularly in those of working class women. This group of women carry the burden of carrying out multiple roles and responsibilities at the same time. All this collectively make them more prone to developing anxiety compared to men. In addition, the physiological and psychological nature of women, as females, on top of the other roles in life, like being a wife or mother or daughter or sister, all add extra pressure on women especially for those who are considered as productive working individuals in the society. In order to study the relatio

     The polyaniline powder was chemically manufactured by direct oxidation of aniline. The resulting polymer was characterized by the results of optical, measurements by (FT-IR) spectroscopy, we have detected some of the absorption peaks located at 3498, 2858 cm^-1, which correspond N-H vibrations, and C-H expansion of the aromatic ring respectively as well as stretching vibrations of quinoid ring have been observed. Structural properties, such as the surface topography using an atomic force microscope (AFM), and Surface composition by (SEM) have been studied. The structure of some pellets of polyaniline powder have been examined by using analytical X-ray diffraction technique, the pattern of obse

In this research we prepared shiff bases unilateral claw( benzyl imine aniline ) and Bilateral claw ( benzayal-2-imine phenol ) in high purity reach to 98% , which it's prepared from aromatic amine with aldehydes, it's solid,thermosetting, not dissolved in water in general. Diagnosed prepared article by using infra red spectroscopy (IR) which shows azomethen grop at 1640cm-1 At this diagnosis we suggest tetra headral mechanism in this Circumstances For a reaction.

The magnetic properties of a pure Nickel metal and Nickel-Zinc-Manganese ferrites having the chemical formula Ni_0.1(Zn_0.4Mn_0.6)_0.9Fe₂O₄ were studied. The phase formation and crystal structure was studied by using x-ray diffraction which confirmed the formation of pure single spinel cubic phase with space group (Fd3m) in the ferrite. The samples microstructure was studied with scanning electron microstructure and EDX. The magnetic properties of the ferrite and nickel metal were characterized by using a laboratory setup with a magnetic field in the range from 0-500 G. The ferrite showed perfect soft spinel phase behavior while the nickel sample showed higher magnetic loss an

Thin films of pure tin mono-sulfide SnS and tin mono-sulfide for (1,2,3,4)% fluorine SnS:F with Thicknesses of (0.85 ±0.05) ?m and (0.45±0.05) ?m respectively were prepared by chemical spray pyrolysis technique. the effect of doping of F on structural and optical properties has been studied. X-Ray diffraction analysis showed that the prepared films were polycrystalline with orthorhombic structure. It was found that doping increased the intensity of diffraction peaks. Optical properties of all samples were studied by recording the absorption and transmission spectrum in range of wave lengths (300-900) nm. The optical energy gap for direct forbidden transi