Silver selenide telluride Semiconducting (Ag2Se0.8Te0.2) thin films were by thermal evaporation at RT with thickness350 nm at annealing temperatures (300, 348, 398, and 448) °K for 1 hour on glass substrates .using X-ray diffraction, the structural characteristics were calculated as a function of annealing temperatures with no preferential orientation along any plane. Atomic force microscopy (AFM) and X-ray techniques are used to analyze the Ag2SeTe thin films' physical makeup and properties. AFM techniques were used to analyze the surface morphology of the Ag2SeTe films, and the results showed that the values for average diameter, surface roughness, and grain size mutation increased with annealing temperature (116.36-171.02) nm The transmittance and absorbance spectra are also analyzed and published in accordance with the wavelength range of (400-1100) nm, The results show that the sample's maximum absorbance value was obtained at a temperature treatment of 448 K, The findings show that the thin films under study are particular of direct transitions at optical energies of 2.05& 1.7& 1.65 and 1.6 ev.
The LiCoMnO4 spinel compound was prepared by a sol–gel method. Structural measurements were utilized to investigate the characteristics of LCMO powder. The powder crystallizes in the space group Rd-3m, with a trigonal crystallinity structure, according to XRD analysis (hexagonal axes). SEM images showed that the crystalline grains sizes were about 200 nm - 350 nm, which provides large surface area. The sample had soft magnetic characteristics, according to hysteresis behaviour analysis in the Vibrating Sample Magnetometer (VSM). The prepared material is thought to be a candidate for the applications of energy storage in lithium-ion batteries.
In this study, crop residues from rice husks were used to enhance the properties of the prepared
wood-plastic composites (W.P.C) are made from epoxy (EP) and unsaturated polyester (UPE) at
a ratio of (50:50) and reinforced with scales in different proportions, both types are fine
(300μm≤) and coarse (300μm>). These blends were undergoing (wear, impact, hardness,
differential scanning calorimetry (DSC), and thermal conductivity) tests and the results showed
the best weight fraction. is the fine particle weight fraction at 25% and coarse at 15%, depending
on the studied tribological characteristics. The results showed by thermal properties of glass
transition temperatures (Tg). For each of the (EP,
In this research four steps of the new derivatives of Naproxen drug have been made which are known as a high medicinal effectiveness; the first step involved converting Naproxen into the corresponding ester (A) by reaction Naproxen with methanol absolute in presence H2SO4. While the second step involved treatment methyl Naproxen ester (A) with hydrazine hydrate 80% in presence of ethanol .The third reaction requires synthesis of Schiff bases (C1-C10) by condensation. of Naproxen hydrazide (B) with many substituted aromatic aldehydes . Finally, the fourth step synthesized new tetrazole derivatives ( D1- D10) by the reaction of the prepared Schiff bases (in the third step) with Sodium azide in THF as a solvent .The prepared compounds wer
... Show More
(2)
The research is concerned about studying the absorption spectrum of the solution coumarin dye C47. The chloroform solvent was used with C47 dye in three different concentrations 10-4, 10-5 and 10-6 M. The laser dye solution was prepared by dissolving the required amount of dye in chloroform alcohol, while studying absorption spectrum before and after irradiation with gamma ray by cobalt-60 source 60Co at exposure time, which are 0, 4, 6 and 18 hours with different absorbed doses 0, 136, 204 and 612 Gy. The results show that red shift in the absorption spectrum was increased by increasing the concentration of laser dye solutions , while the increase of gamma dose led to increase the red shift after irradiation, as the exposure period and irr
... Show More
(2)
This study was undertaken to provide more insight on the optimum injection temperature used for the production of PE crates, thereby saving time and money, and improving part quality. The work included processing trails of HDPE crates in an injection
molding machine at five temperatures ranged from 220 to 300°C. Both Rheological and mechanical characterization was conducted in order to understand the effect of injection temperature on the properties of crates. Oven aging was also applied for (4 weeks) to evaluate the long-term thermal stability. The results revealed that producing the crates at a temperature range of (260-280 °C) gives the best rheological and mechanical result. The lowest drop in thermal stability has been observed
The problem of soil contamination is increased recently due to increasing the industrial wastes such as petroleum hydrocarbon, organic solvents, and heavy metals as well as maximizing the use of agricultural fertilizers. During this period, wide development of data collection methods, using remote sensing techniques in the field of soil and environment applications appear and state the suitable technique for remediation. This study deals with the application of remote sensing techniques in geoenvironmental engineering through a field spectral reflectance measurements at nine spots of naturally hydrocarbons contaminated soil in Al-Daura Refinery Company site which is located to the south west of Baghdad using radiometer device to get stan
... Show More
(4)
Poly ethylene oxide PEO / Poly vinyl alcohol PVA blends were prepared by cast method at different ratios of (25%PEO/75%PVA, 30%PEO/70%PVA, 35%PEO/65%PVA, 40%PEO/60%PVA, and 50%PEO/505PVA). Samples miscibility ,and thermal stability were studied by using differential scanning calorimetry(DSC),and thermo gravimetric analysis (TGA) analysis. The results proved that there was one glass transition temperature (Tg=160°C) at 25%PEO\PVA ratio
)that was attributed to its miscibility. This miscibility associated with (Hydrogen bonds) between (Hydroxyl group) in PVA, and PEO, whereas there were two glass transition temperature for the blends ratio more than 30%PEO,that was due its immisc
(9)
Purepolyaniline and doped with hydrochloric acid was prepared in different molarities at room temperature. The a.c electrical properties were stadied.AC conductivityσac (ω), is found to vary as ωS in the frequency range (100Hz-10MH), S< 1and decreases indicating a dominate hopping process. Thedielectric constant ε1and dielectric loss ε2 have been determined for bulk polyaniline. ε1 decrease with the increase frequency. Electrical conductivity measurements increase with the increases both of the amount of HCl and the dose of radiation. The dielectric investigations show decrease with dose radiation.
ABSTRACT
The controversy is currently revolving around industrial additives, including antioxidants, their negative effects on consumer health and the emergence of various and various diseases, which led scientists and researchers to intensify most studies on natural antioxidants and their synthesis from medicinal plants mentioned in ancient medicine and in divine books as potential antioxidants of increasing importance. Therefore, this study was designed to synthesize silver nitrate particles from plant leaf extracts (Figs, Olives, and Moringa) and study their effect on bacterial inhibition of each of the undesirable Coliform bacteria (E-Coli,
... Show More