Gypseous soils represented one of the most complex salty soils that faced the geotechnical engineers. Structures that built on gypsum soil will undergo unexpected distortions that will eventually contribute to catastrophic failure. The purpose of this article is to understand the durability of gypsum soil against wetting drying cycles after improvement with polyurethane polymer especially investigate the effect of the wetting-drying cycle on collapsibility. The soil was brought from Sawa lake in AL-Muthanna Governorate in Iraq, with gypsum content 65.5%, A set of Odometer tests were performed to determine the collapsibility potential (CP) for treated and untreated gypsum soil. The result shows that adding a different percentage of polyurethane polymer (PP) gave a significant improvement in collapse potential (CP) and durability against wetting and drying cycles with different curing times. Whereas reduction in (CP) for the three percentages (3%, 6%, 10%) of polyurethane polymer was (53%,82%,93.2%) respectively after the specimens subjected to one cycle, while the three percentages (3%, 6%, 10%) of polyurethane polymer gave about (85%, 87%,94.6%) reduction in (CP) respectively after the specimens subjected to four cycles. the result showed that polyurethane can be used successfully as a chemical additive to stabilize the mechanical characteristic of gypseous soil with a high percentage of gypsum content.
The aim of this paper is to demonstrate the effect of Na2[Fe(CN)5.NO].2H2O impurity (0.1 M) concentration on the dielectrical properties of poly (P-Aminobenzaldehyde) terminated by pheneylenediamine in the frequency and temperature ranges (1-100)KHz and (283-348) K respectively.These properties include dissipation factor, series and parallel resistance, series and parallel capacitance, real and imaginary part of the dielectric constant, a.c conductivity and impedance (real and imaginary) part, that have been deduced from equivalent circuit. The investigation shows that adding Na2[Fe(CN)5.NO].2H2O as additive to the polymer lead to increase of the dielectric constant with increasing temperature and it is decreasing with increasing the freq
... Show MoreAbstract
In this study, the effect of carboxylic methyl cellulose (CMC), and sodium dodcyl benzene sulfonate (SDBS) as an aqueous solution on the drag reduction was investigated. Different concentrations of (CMC) and (SDBS) such as (50, 100, 150, 200, 250, 300, 350, 400, 450, and 500 ppm) were used to analyze the aqueous solution properties, including surface tension, conductivity, and shear viscosity. The optimum four concentrations (i.e., 50, 100, 200, and 300 ppm) of fluid properties were utilized to find their effect on the drag reduction. Two different PVC pipe diameters (i.e., 1" and 3/4") were used in this work. The results showed that blending CMC with SDBS gives
... Show MoreFrom the sustainability point of view a combination of using water absorption polymer balls in concrete mix produce from Portland limestone cement (IL) is worth to be perceived. Compressive strength and drying shrinkage behavior for the mixes of concrete prepared by Ordinary Portland Cement (O.P.C) and Portland limestone cement (IL) were investigated in this research. Water absorbent polymer balls (WAPB) are innovative module in producing building materials due to the internal curing which eliminates autogenous shrinkage, enhances the strength at early age, improve the durability, give higher compressive strength at early age, and reduce the effect of insufficient external curing. Polymer balls (WAPB) had been used in the mixes of thi
... Show More4, 4s (pyridine 2, 6 diylbis (1, 3, 4 oxadiazole 5, 2 diyl)) bisphenol monomer (3) was synthesized from cyclization of Ns2, Ns6 bis (4 hydroxybenzylidene) pyridine 2, 6 dicarbohydrazide (2) in the presence of bromine in glacialacetic acid. Newly five polymers (P1P5) were synthesized from reaction bis 1, 3, 4 oxadiazole bisphenolmonomer with five different di acid chloride. The antibacterial activity of the synthesized polymers was screened against gram positive and gram negative bacteria. Polymers P4 and P5 exhibited significant antibacterial against all microorganisms, as well these polymers showed highest antifungal activity.
In situ gel can be defined as a polymer solution administered as a liquid and when exposed to some physiologic condition such as thepH, ionic, temperature modulation or solvent and UV induced gelation undergo to phase transition to a semisolid gel. Ketotifenfumarate belongs to the histamine H1 receptor antagonists, and Ketotifen fumarate is used in the treatment of allergic conditions likeconjunctivitis and rhinitis. This work aims to study the natural polymer effects (xanthan gum,gellan gum) on the properties of pH-trigger in situ ocular gel, then compared the drug-releasing rate of optimized formula with the market ketotifen eye drop. Eightformulations (F1-F8) were prepared using different concentrations of xanthan gum, gellan gum with ca
... Show MoreThe twelve samples of agricultural soils from four regions in Al-Najaf governorate with sampling plant with soil. Physical properties of the soil where studied, such as electrical conductivity ranged from (136.33-1070.00)μS/cm-3, and moisture which ranged between the values (0.39-36.48)%. The chemical analysis of the soil have included the proportion of calcium carbonate the ratio between (44.00-48.00%) has been observed increasing amounts of calcium carbonate in surface models. The pH where results indicate that pH values were close to study models ranged between (6.88-7.42) these values generally within the normal range for the measured pH values of the Iraqi soil. The amount of gypsum ranged betwe
... Show MoreThis study offers the elastic response of the variable thickness functionally graded (FG) by single walled carbon nanotubes reinforced composite (CNTRC) moderately thick cylindrical panels under rotating and transverse mechanical loadings. It’s considered that, three kinds of distributions of carbon nanotubes which are uniaxial aligned in the longitudinal direction and two functionally graded in the transverse direction of the cylindrical panels. Depending on first order shear deformation theory (FSDT), the governing equations can be derived. The partial differential equations are solved by utilizing the technique of finite element method (FEM) with a program has been built by using FORTRAN 95. The results are calculat
... Show More