Potentiostatic polarization and weight loss methods have been used to investigate the corrosion behavior of carbon steel in sodium chloride solution at different concentrations (0.1, 0.4 and 0.6) M under the influence of temperatures ( 293, 298, 303, 308 and 313) K. The inhibition efficiency of the amoxicillin drug on carbon steel in 0.6 M NaCl has also been studied based on concentration and temperature. The corrosion rate showed that all salt concentrations ( NaCl solution) resulted in corrosion of carbon steel in varying ratio and 0.6 M of salt solution  was the highest rate (50.46 g/m².d). The results also indicate that the rate of corrosion increases at a temperature of 313 K.. Potentiodynamic polarization studi

             The centers of cities and historical quarter are exposed to a severe threat to the values of the physical and legal urban environment as a result of the value deterioration and the emergence, emergence and spread of new values on the intellectual and urban context, which generates the loss of the urban environment for its spatio-temporal continuity, flexibility, adaptation and continuity, and thus urban obsolescence, Hence the problem of the research in “the lack of comprehensiveness of studies on the phenomenon of urban obsolescence and its impact on the decline in the values of the quality of the built environment in historic

The purpose of present work is to study the relationship of the deformed shape of the nucleus with the radioactivity of nuclei for (Uranium-238 and Thorium-232) series. To achieve our purposes we have been calculated the quadruple deformation parameter (β2) and the eccentricity (e) and compare the radioactive series with the change of the and (e) as indicator for the changing in the nucleus shape with the radioactivity. To obtain the value of quadruple deformation parameter (β2), the adopted value of quadruple transition probability B (E2; 0+ → 2+) was calculated from Global Best fit equation. While the eccentricity (e) was calculated from the values of the minor and major ellipsoid axis’s (a & b). From the results, it is obvi

In this study, composite materials were prepared using unsaturated polyester resin as binder with two types of fillers (sawdust and chopped reeds). The molding method is used to prepare sheets of UPE / sawdust composite and UPE / chopped reeds composite. The mechanical properties were studied including flexural strength and Young's modulus for the samples at normal conditions (N.C). The Commercial wood, UPE and its composite samples were immersed in water for about 30 days to find the weight gain (Mt%) of water for the samples, also to find the effect of water on their flexural strength and Young's modulus. The results showed that the samples of UPE / chopped reeds composite gained highest values of flexural strength (24.

Background : It has been suggested that pretreatment with a statin agent prior to
myocardial infarction limits myocardial
creatine kinase release, and thus may act to
limit myocardial infarct size in humans.
Objective : To examine the effect of very
early statin initiation for acute myocardial
infarction (AMI), to the extent of
myonecrosis as manifested by peak serum
creatine kinase levels.
Methods : Patients with AMI admitted to AlKindy teaching hospital cardiac care unit
from 1st February 2007 to 28th February
2008, who fulfilled the inclusion criteria
cited in the present study, were randomly
assigned into two study groups. The statin
group patients have received a single oral
dose of 40 mg

The compressive residual stresses generated by shot peening, is increased in a direct proportional way with shot peening time (SPT). For each metal, there is an optimum shot peening time (O.S.T) which gives the optimum fatigue life. This paper experimentally studied to optimize shot peening time of aluminium alloy 6061-T651 as well as using of and analysis of variance (ANOVA).

Two types of fatigue test specimens’ configuration were used, one without notch (smooth) and the other with a notch radius (1,25mm), each type was shot peened at different time. The (O.S.T) was experimentally estimated  to be 8 minutes reaching the surface stresses at maximum peak of -184.94 MPa.

A response surface methodology (RSM) is presen

Objective: The aim of this study is to detect the effect of continuous exposure to Sodium Nitrite on 8-oxoguanine
DNA glycosylase (OGG1) gene which responsible on DNA repairs. DNA repair play a major role in maintaining
genomic stability when DNA exposure to damage. Genomic stability is very important for keeping body cells
healthy and to prevent many types of tumor development. Many genes are responsible for this job; one of them is
OGG1 gene.
Methodology: In current study two groups of mice were chronically exposed to sodium nitrite for six months and
eighteen months while third group was used as a control. Then sizes of OGG1 were estimated.
Results: The results exhibited in the unexposed (control) mice had two dif