Background: Denture relining is the process of resurfacing of the tissue side of the ill fitting denture, the bond strength at the relining-denture base interface is most important for denture durability.The aim of present study was to evaluate the shear bond strength between the thermosens as relining material and different denture base materials that bonded by thermo fusing liquid. As this corrective procedureis the common chair side procedure in the dental clinic. Material and method: Sixty samples were prepared and divided into three main groups according to the type of denture base materials.Group (A) referred to the heat cure acrylic samples which consisted of 20 samples. Group (B) referred to the high impact acrylic samples which con

PMMA (Poly methyl methacrylate) is considered one of the most commonly used materials in denture base fabrication due to its ideal properties. Although, a major problem with this resin is the frequent fractures due to heavy chewing forces which lead to early crack and fracture in clinical use. The addition of nanoparticles as filler performed in this study to enhance its selected mechanical properties. The Nano-additive effect investigated in normal circumstances and under a different temperature during water exposure. First, tests applied on the prepared samples at room temperature and then after exposure to water bath at (20, 40, 60) C^° respectively. SEM, PSD, EDX were utilized for samples evaluation in this study. Flexural

The development of new cephalosporins with improved activity against resistant microbes, such as, MRSA (methicillin resistant Staph. aureus), P. aeruginosa, is of high potential. Chemical synthesis of two new series of thiadiazole linked to cysteine (series 1) and cephalosporins containing thiadiazole linked to cysteine through disulfide bond (series 2) were achieved. The chemical structures of the synthesized compounds were confirmed using spectral (FT-IR, ¹H-NMR) and elemental microanalysis. The incorporation of privileged chemical moieties, such as, thiadiazole, Schiff base, cysteine and sulfonamide, has been found to have great contribution to the antimicrobial activities. Compounds of series 1 (1

Zerumbone is a well-known compound having anti-cancer, anti-ulcer, anti-inflammatory and anti-hyperglycemic effects. During its use for the disease treatment, the membrane of erythrocyte can be affected by consumption of this bioactive compound. The current study was the first report of investigation of the hemolytic activities on human erythrocytes and cytotoxic profile of zerumbone. The toxicity of zerumbone on human erythrocytes was determined by in vitro hemolytic assay. Brine shrimp lethality assay was used to evaluate the cytotoxic effect of zerumbone at concentrations 10, 100 and 1000 μg/mL. The human erythrocyte test showed no significant toxicity at low concentrations, whereas hemolytic effect was amplified up to 17.5 % at

Zerumbone is a well-known compound having anti-cancer, anti-ulcer, anti-inflammatory and anti-hyperglycemic effects. During its use for the disease treatment, the membrane of erythrocyte can be affected by consumption of this bioactive compound. The current study was the first report of investigation of the hemolytic activities on human erythrocytes and cytotoxic profile of zerumbone. The toxicity of zerumbone on human erythrocytes was determined by in vitro hemolytic assay. Brine shrimp lethality assay was used to evaluate the cytotoxic effect of zerumbone at concentrations 10, 100 and 1000 μg/mL. The human erythrocyte test showed no significant toxicity at low concentrations, whereas hemolytic effect was amplified up to 17.5

Background: Tooth extraction is one of the most commonly performed procedures in dentistry. It is usually a traumatic process often resulting in immediate destruction and loss of alveolar bone and surrounding soft tissues. Various instruments have been described to perform atraumatic extractions which can prevent damage to the paradental structures. The physics forceps is one of those innovations in dental extraction technologies that claim to provide an efficient means for atraumatic dental extractions. Materials and method: A randomized clinical trial was conducted to compare the physics forceps with the conventional forceps for the removal of 28 mandibular single rooted teeth under the following parameters: incidence of crown, root, b

The adhesion strength between Polyethylene (PE) film and Aluminum surface by using the adhesive material (Cyanoacrylate) has been studied. Aluminum (Al) was used as a substrate, and polyethylene (PE) was used as a film adhered to the Al surface. Standard specimens were prepared to use in the peeling test in dry condition, other specimens were immersed in water for 12 days at room temperature. the results for the specimens in the dry condition had shown that high value in the peel force and the peel energy, the peel force was 0.38*103 N/m and the peel energy was 0.605*103 N/m, peeling the film from Al surface leaves a residual of the adhesive material on both adherend, the failure for this specimen were combination of adhesive and cohesive f

Background: acrylic resin denture base consider a common denture base material for its acceptable cost, aesthetic and easy processing but still has disadvantages including easy of fracture and low impact strength. Material and method: The experimental group was prepared by addition of 15% phosphoric acid 2-hydroxyethyl methacrylate ester (PA2HEME) with polymethyl methacrylate monomer; the experimental groups was compared with the control one. The specimens were prepared according to ADA specification No. 12 with dimension 65 mm x 10 mm x2.5 mm (length x width x thickness respectively). The prepared specimens were tested by three-point flexural strength utilizing Instron Universal Testing Machine (WDW, Layree Technology Co.), Shore D hard

Previously many properties of graphene oxide in the field of medicine, biological environment and in the field of energy have been studied. This diversity in properties is due to the possibility of modification on the composition of this Nano compound, where the Graphene oxide is capable of more modification via addition other functional groups on its surface or at the edges of the sheet. The reason for this modification possibility is that the Sp3 hybridization (tetrahedral structure) of the carbon atoms in graphene oxide, and it contains many oxygenic functional groups that are able to reac with other groups. In this research the effect of addition of some amine compounds on electrical properties of graphene oxide has been studied by the