In this research the a-As flims have been prepared by thermal evaporation with thickness 250 nm and rata of deposition r_d(1.04nm/sec) as function to annealing temperature (373 and 473K), from XRD analysis we can see that the degree of crystalline increase with T_a, and I-V characteristic for dark and illumination shows that forward bias current varieties approximately exponentially with voltage bias. Also we found that the quality factor and saturation current dependence on annealing temperatures.

In this research the a-As flims have been prepared by thermal evaporation with thickness 250 nm and rata of deposition (1.04nm/sec) as function to annealing temperature (373 and 373K), from XRD analysis we can see that the degree of crystalline increase with , and I-V characteristic for dark and illumination shows that forward bias current varieties approximately exponentially with voltage bias. Also we found that the quality factor and saturation current dependence on annealing temperatures.

This work concerned on nanocrystalline NiAl2O4 and ZnAl2O4 having spinel structure prepared by Sol–gel technique. The structural and characterization properties for the obtained samples were examined using different measurements such as X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), finally, Field emission scanning electron microscope (FESEM).The Spinel-type for two prepared compound (NiAl2O4) and (ZnAl2O4) at different calcination temperature examined by XRD. Williamson-Hall Methods used to estimate crystallite size, Average distribution crystallite size of two compound were, 34.2 nm for NiAl2O4 and32.6 for ZnAl2O4, the increase in crystallite size affecting by increasing in calcination temperature for both comp

This contribution investigates the impact of adding transition metal of Ti to CeOy samples at various concentrations referring to 0, 15.84, 24.46, 34.46, 36.23, 38.46, 45.38% and pure TiOy, correspondingly. The samples were fabricated by the magnetron sputtering technique. X-ray diffraction (XRD) configurations demonstrate the presence of α-Ce2O3 and Ce2O3 phases with increased Ti contents in the systems. X-ray photoelectron spectroscopy (XPS) experimentation confirms the purity of the S1-sample (CeO2) and the purity of the S8-sample (TiO2). Further XPS analysis reveals that Ti incorporation in the doped systems functions as a reducing agent because of the existence of α-Ce2O3 and Ce2O3 phases. Moreover, based on UV–vis spectroscopy res

This contribution investigates the impact of adding transition metal of Ti to CeOy samples at various concentrations referring to 0, 15.84, 24.46, 34.46, 36.23, 38.46, 45.38% and pure TiOy, correspondingly. The samples were fabricated by the magnetron sputtering technique. X-ray diffraction (XRD) configurations demonstrate the presence of α-Ce2O3 and Ce2O3 phases with increased Ti contents in the systems. X-ray photoelectron spectroscopy (XPS) experimentation confirms the purity of the S1-sample (CeO2) and the purity of the S8-sample (TiO2). Further XPS analysis reveals that Ti incorporation in the doped systems functions as a reducing agent because of the existence of α-Ce2O3 and Ce2O3 phases. Moreover, based on UV–vis spectroscopy res

In this research, a detailed finite-element (FE) analysis of the combined influence of the drilled-hole position, the shape of the hole, and the fillet design on the structural and dynamic performance of spur gears is investigated. ANSYS R16.2 was used to create a three-dimensional numerical model that can be used to assess the bending stress distribution and vibration response under realistic loading conditions. A trochoidal fillet and four circular fillet radii (0.5, 1.0, 1.5 and 2.0 mm) were studied to determine their effect on the stress concentration behavior. FE-guided hole-suggestion process was introduced which is an automated process in which low-stress zones to be cut away are identified so as to allo

A new azo dye, 5,5-[1,2-phenylenebis(2,1-biazenediyl)]bis[8-quinolino], was synthesized by reacting the diazonium salt of o-phenylenediamine with 8-hydroxyquinoline. The ligand was subsequently used to prepare a series of metal complexes with V(IV), Fe(III), Cr(III), Mn(II), Mo(VI), and Ru(III). The ligand was characterized using 1H and 3C-NMR spectroscopy, while the metal complexes were analyzed using UV-Vis, FT-IR, and mass spectrometry, along with thermal analysis (TGA, DSC), (C.H.N.), conductivity measurements, magnetic susceptibility, and metal and chlorine content analysis, the results indicated that the ligand exhibits tetracoordination. The complexes predominantly formed octahedral geometries, except for the vanadium complex, which

PVC/Kaolinite composites were prepared by the melt intercalation method. Mechanical properties, thermal properties, flammability and water absorption percentage of prepared samples were tested. Mechanical characteristic such as tensile strength, elongation at break; hardness and impact strength (charpy type) were measured for all samples. It was found that the tensile strength and elongation at break of PVC composites decreased with increasing kaolinite loading. Also, the hardness of the composites increases with increase in filler content .The impact strength of the composites at the beginning increases at lower kaolinite loadings is due to the lack of kaolin adhesion to the matrix. However, at higher kaolin loadings. This severe agglom

One of the important objectives of the varistor is for a sustainable environment and reduce the pollution resulting from the frequent damage of the electrical devices and power station waste. In present work, the influence of Al2O3 additives on the non –linear electrical features of SnO2 varistors, has been investigated, where SnO2 ceramic powder doped with Al2O3 in three rates (0.005, 0.01, and 0.05), the XRD test improved that SnO2 is the primary phase, while CoCr2O4, and Al2O3 represent the secondary phases. The electrical tests of all prepared samples confirmed that the increasing of Al2O3 rates and sintering temperature improves and increase the electrical features, where the best results obtained at Al2O3 (0.05) and 1000℃, the non

The aim of the current research is to develop the social studies curriculum at the primary stage in light of the standards of the next generation, which was represented in three main dimensions (pivotal ideas, scientific practices, and comprehensive concepts). The researcher designed a tool for the study, which is a content analysis card in the light of (NGSS) standards, based on the previous main dimensions. The descriptive analytical approach was adopted in analyzing the social studies curriculum for the primary stage to determine the degree to which the standards of the next generation are available, as well as to establish the theoretical framework related to the research variables. To develop the social studies curriculum in light o