The thin films of SnO2,SnO2:TiO2 , SnO2:MoO3 , SnO2:WO3 , SnO2:Cr2O3 , and SnO2: Fe2O3 were prepared by pulsed laser deposition technique using (Nd:YAG) laser of λ=1064 nm average frequency (6) Hz and pulse duration (10 ns) under vacuum of 10 -2 mbar)deposited on glass, n-Si single crystals substrate room temperature with thickness of (100±10) nm. The structures of pure SnO2 and ,SnO2:TiO2 , SnO2:MoO3 , SnO2:WO3 , SnO2:Cr2O3 , SnO2:Co3O4 compounds were studied by X–ray diffraction .the results showed that there was red shift accompanied addition of MoO3 and TiO2 while a blue shift accompanied the addition of WoO3 , Cr2O3 , Fe2O3 to tin oxide . The gas sensing measurements of NO2 gas showed that S

The gas sensing properties of Co3O4and Co3O4:Y nano structures were investigated. The films were synthesized using the hydrothermal method on a seeded layer. The XRD, SEM analysis and gas sensing properties were investigated for Co3O4and Co3O4:Y thin films. XRD analysis shows that all films are polycrystalline in nature, having a cubic structure, and the crystallite size is (11.7)nm for cobalt oxide and (9.3)nm for the Co3O4:10%Y. The SEM analysis of thin films obviously indicates that Co3O4possesses a nanosphere-like structure and a flower-like structure for Co3O4:Y.The sensitivity, response time and recovery time to a H2S reducing gas were tested at different operating

Thin films of pure and doped nano titanium dioxide (TiO2) were prepared using a chemical pyrolysis technique (CPS), with different nanosize graphene oxide (GO) concentrations in the range (3-9)wt%. The structural, morphological andoptical characteristics of these films were investigated. X-ray diffraction (XRD) technique measurements revealed that the structure properties of TiO2have polycrystalline structure with anatase phase. AFM analysis showed the grain size of TiO2 films with different concentrations was decreased after doping with high concentration of GO ratio. Roughness of these films decreased too after adding of GO impurity for all films from (7.65-5.6)nm except 5wt% percentage where increased to 13.7nm. Optical

The preparation of composite metal oxide to attain high efficiency in removing phenol from wastewater has a great concern. In the present study, the focus would be on adopting antimony-tin oxide coating onto graphite substrates instead of titanium; besides the effect of SbCl3 concentration on the SnO2-Sb2O3 composite would be examined. The performance of this composite electrode as the working electrode in the removal of phenol by sonoelectrochemical oxidation will be studied. The antimony-tin dioxide composite electrode was prepared by cathodic deposition with SnCl2 . 2H2O solution in a mixture of HNO3 and NaNO3, with different concentrations of SbCl3. The SnO2-Sb2O3 deposit layer’s structure and morphology were examined and the 4 g/l Sb

Thin films of GexS1-x were fabricated by thermal evaporating under vacuum of 10-5Toor on glass substrate. The effect of increasing of germanium content (x) in sulfide films on the electrical properties like d.c conductivity (σDC), concentration of charge carriers (nH) and the activation energy (Ea) and Hall effect were investigated. The measurements show that (Ea) increases with the increasing of germanium content from 0.1to0.2 while it get to reduces with further addition, while charge carrier density (nH) is found to decrease and increase respectively with germanium content. The results were explained in terms of creating and eliminating of states in the band gap

Thin films of ZnSxSe1-x with different sulfide content(x)
(0, 0.02, 0.04, 0.06, 0.8, and 0.1), thickness (t) (0.3, 0.5, and 0.7 μm) and annealing temperature (Ta) (R.T 373 and 423K) were fabricated by thermal evaporating under vacuum of 10-5 Toor on glass substrate. The results show that the increasing of sulfide content (x)and annealing temperature lead to decrease the d.c conductivity σDC of and concentration of charge carriers (nH) but increases the activation energy (Ea1,Ea2), while the increasing of t increases σDC and nH but decrease (Ea1,Ea2). The results were explained in different terms

The current work concerns preparing cobalt manganese ferrite (Co0.2Mn0.8Fe2O4) and decorating it with polyaniline (PAni) for supercapacitor applications. The X-ray diffraction findings (XRD) manifested a broad peak of PAni and a cubic structure of cobalt manganese ferrite with crystal sizes between 21 nm. The pictures were taken with a field emission scanning electron microscope (FE-SEM), which evidenced that the PAni has nanofibers (NFs) structures, grain size 33 – 55 nm, according to the method of preparation, where the hydrothermal method was used. The magnetic measurements (VSM) that were conducted at room temperature showed that the samples had definite magnetic properties. Additionally, it was noted that the saturation magnetizatio