In this research, experimental and numerical studies were carried out to investigate the performance of encased glass-fiber-reinforced polymer (GFRP) beams under fire. The test specimens were divided into two peer groups to be tested under the effect of ambient and elevated temperatures. The first group was statically tested to investigate the monotonic behavior of the specimens. The second group was exposed to fire loading first and then statically tested to explore the residual behavior of the burned specimens. Adding shear connectors and web stiffeners to the GFRP beam was the main parameter in this investigation. Moreover, service loads were applied to the tested beams during the fire. Utilizing shear connectors, web stiffeners,

In this research, experimental and numerical studies were carried out to investigate the performance of encased glass-fiber-reinforced polymer (GFRP) beams under fire. The test specimens were divided into two peer groups to be tested under the effect of ambient and elevated temperatures. The first group was statically tested to investigate the monotonic behavior of the specimens. The second group was exposed to fire loading first and then statically tested to explore the residual behavior of the burned specimens. Adding shear connectors and web stiffeners to the GFRP beam was the main parameter in this investigation. Moreover, service loads were applied to the tested beams during the fire. Utilizing shear connectors, web stiffeners,

Carbon Fiber-Reinforced Polymer (CFRP) bars have several advantages over traditional steel reinforcement, including low density, erosion resistance, and higher tensile strength. The ACI 440.11-22 code permits CFRP as reinforcement; however, there are limited experimental studies on its application in Reinforced Concrete (RC) columns under combined loads. This study utilized theoretical analysis and Finite Element Analysis (FEA) to investigate 25 square slender concrete columns (kL/r = 17) affected by concentric and eccentric loads, examining variables, like CFRP bar contribution, eccentricity-to-depth ratio, and reinforcement arrangement. The results demonstrated CFRP's effectiveness in these columns, with failure modes varying from

Carbon Fiber-Reinforced Polymer (CFRP) bars have several advantages over traditional steel reinforcement, including low density, erosion resistance, and higher tensile strength. The ACI 440.11-22 code permits CFRP as reinforcement; however, there are limited experimental studies on its application in Reinforced Concrete (RC) columns under combined loads. This study utilized theoretical analysis and Finite Element Analysis (FEA) to investigate 25 square slender concrete columns (kL/r = 17) affected by concentric and eccentric loads, examining variables, like CFRP bar contribution, eccentricity-to-depth ratio, and reinforcement arrangement. The results demonstrated CFRP's effectiveness in these columns, with failure modes varying from

Taguchi experimental design (TED) is applied to find the optimum effectiveness of aqueous Red Pomegranate Peel (RPP) extract as a green inhibitor for the corrosion of mild steel in 2M H₃PO₄ solution. The Taguchi methodology has been used to study the effects of changing, temperature, RPP concentration and contact period, at three levels. Weight-loss measurements were designed by construction a L₉ orthogonal arrangement of experiments.   Results of the efficiencies of inhibition were embraced for the signal to noise proportion & investigation of variance (ANOVA).  The results were further processed with a MINITAB-17 software package to find the optimal condition

In this research we prepared shiff bases unilateral claw( benzyl imine aniline ) and Bilateral claw ( benzayal-2-imine phenol ) in high purity reach to 98% , which it's prepared from aromatic amine with aldehydes, it's solid,thermosetting, not dissolved in water in general. Diagnosed prepared article by using infra red spectroscopy (IR) which shows azomethen grop at 1640cm-1 At this diagnosis we suggest tetra headral mechanism in this Circumstances For a reaction.