The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burn

       Nanometal oxides were extracted from cement factories wastes and were employed to proliferate skin cancer cells using MTT (Methyl Thiazolyl Tetraolium) assay. MTT assay results for skin cancer cell line A375,for CaO NPs the best concentration was 200 μg/mL,The viability was reduced to 57.28% while the IC₅₀ was (69.66) g/mL for A375 and normal cell WRL68 was significantly higher (231.2 g/mL). The cytotoxicity results of CaO: MgO: Fe₂O₃ NPs, at higher concentrations (200 and 400) μg/mL showed a significant difference. The IC₅₀ was (106.4) μg/mL for A375and normal cell WRL68 was significantly higher (173.3) μg/ml CaO:MgO:Fe₂O₃ NPs. The nanometal oxides, calci

The research included preparation of new iron(II) complexes with mixed ligands including benzilazine(BA) and semicarbazone ligands {benzilsemicarbazone- BSCH or benzilbis(semicarba-zone)- BBSCH2 or salicylaldehydesemicarbazone- SSCH2 or benzoinsemicarbazone- B'SCH2}.by classical and microwave methods. The resulted complexes have been characterized using chemical and physical methods. The study suggested that the above ligands form ionic complexes having formulae [Fe(SCHi)(BA)(Cl)m](Cl)2-m {where SCH, BSCH, BBSCH2, SSCH¬2 or B'SCH2 ligands; m=1 or 2}. Hexacoordinated mononuclear complexes have been investigated by this study and having octahedral geometries. The effect of laser ray type visible region have been studied on solid ligands and

         Certain cyclic amine derivatives of metronidazole via acetate spacer were prepared. Cyclic amines used are piperidine and piperazine to improve the physicochemical properties and reduce some of metronidazole side effects. This is believed to be done by modification of its structural features to get prodrugs with improved properties over that of metronidazole. The present work includes esterification of metronidazole with choroacetic acid, N-alkylation of the cyclic amines by the halogenated ester and characterization of their structures by spectral(UV and IR) and elemental(CHN)analysis.The melting points, degree of solubilities and partition coefficients were also determined. Both metronid

6-Amino-4-(4-hydroxyphenyl)-5-cyano-3-methyl-1-phenyl-1, 4-dihydropyrano [2,3-c] pyrazole (compound 2) was prepared by condensation of 2-(4-hydroxylbenzylidine) malononitrile (compound 1) [which was prepared by Knoevenagel condensation of malononitrile with 4-hydroxy benzaldehyde ] with 3-methyl-1-phenyl-2-pyrazolin-5-one. Reactions of compound 2 with different reagents formic acid, formamide, and ammonium thiocyanate under microwave irradiation leads to the synthesis of 4-(4-hydroxyphenyl)- 3-methyl-1-phenyl-4,6-dihydro- pyrazolo [3', 4':5,6] pyrano [2,3-d] pyrimidine-5-one (compound 3), 4-(4-hydroxyphenyl)- 3-methyl-1-phenyl-4, 6-dihydro- pyrazolo [3', 4':5,6]pyrano[2,3-d]pyrimidine-5-imine (compound 4) and N-[4-(4-hydroxyphenyl)- 3-me

Abstract

In this manuscript, a simple new method for the green synthesis of platinum nanoparticles (Pt NPs) utilizing F. carica Fig extract as reducing agent for antimicrobial activities was reported. Simultaneously, the microstructural and morphological features of the synthesized Pt NPs were thoroughly investigated. In particular, the attained Pt NPs exhibited spherical shape with diameter range of 5-30 nm and root mean square of 9.48 nm using Transmission Electron Microscopy (TEM) and Atomic Force Microscopy (AFM), respectively. Additionally, the final product (Pt NPs) was screened as antifungal and antibacterial agent against Candida and Aspergillus species as well as Gram-positive Staphyllococcus aureus and G

Aqueous root extract has been used to examine the green production of silver nanoparticles (AgNPs) by reducing the Ag+ ions in a silver nitrate solution. UV-Vis spectroscopy, X-ray diffraction, field emission scanning electron microscopy, and Fourier transform infrared spectroscopy (FTIR) were used to analyze the produced AgNPs. The AgNPs that were created had a maximum absorbance at 416 nm, were spherical in form, polydispersed in nature, and were 685 nm in size.The AgNPs demonstrated antibacterial efficacy against Escherichia coli and Staphylococcus. The dengue vector Aedes aegypti's second instar larvae were very susceptible to the AgNPs' powerful larvicidal action.

(Cu1-x,Agx)2ZnSnSe4 alloys have been fabricated with different Ag content(x=0, 0.1, and 0.2) successfully from their elements. Thin films of these alloys have been deposited on coring glass substrate at room temperature by thermal evaporation technique under vacuum of 10-5Torr with thickness of 800nm and deposition rate of 0.53 nm/sec. Later, films have been annealed in vacuum at (373, and 473)K, for one hour. The crystal structure of fabricated alloys and as deposited thin films had been examined by XRD analysis, which confirms the formation of tetragonal phase in [112] direction, and no secondary phases are founded. The shifting of main polycrystalline peak (112) to lower Bragg’s angle as compared to Cu2ZnSnSe4 angle refers to incorpora

    In this study the as-deposited and heat treated at 423K of conductive blend graphene oxide (GO)/ poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) thin films was prepared with different PEDOT:PSS concentration (0, 0.25, 0.5, 0.75 and 1)w/w on pre-cleaned glass substrate by spin coater. The XRD analysis indicate the existence of the preffered peak (001) of GO around 2θ=8.24° which is domain in all GO/ PEDOT:PSS films characterized for GO, this result approve the good quality of the PEDOT:PSS dispersion in GO, this peak shifted to the lower 2θ with increasing PEDOT:PSS concentration and after annealing process. The scanning electron microscopy (SEM) images and atomic force microscopy (AFM) clearly sh

In this research, we studied the structural properties of SnO2 films nanostructure which prepared by chemical spray pyrolysis method at room temperature on the rules of glass heated (400oC) with rate of spraying (2.5 ml/ min). The effect of annealing temperaturs (450,500,550,600 and 650oC) for two hours on those properties has been indicated. The results of x-ray diffraction showed that all of the prepared films were polycrystalline with tetragonal type and orientation was (110) for all models before and after annealing, and the annealing led to an increase in the grain size. The full width at half maximum (FWHM) values of the (110) peaks of the films decreased from 1.492o to 1.064o with increasing annealing temperature .The surface morp