Copper doped Zinc oxide and (n-ZnO / p-Si and n-ZnO: Cu / p-Si) thin films thru thickness (400±20) nm were deposited by thermal evaporation technique onto two substrates. The influence of different Cu percentages (1%,3% and 5%) on ZnO thin film besides hetero junction (ZnO / Si) characteristics were investigated, with X-ray diffractions examination supports ZnO films were poly crystal then hexagonal structural per crystallite size increase from (22.34 to 28.09) nm with increasing Cu ratio. The optical properties display exceptional optically absorptive for 5% Cu dopant with reduced for optically gaps since 3.1 toward 2.7 eV. Hall Effect measurements presented with all films prepared pure and doped have n-types conductive, with a ma

There is a real problem when adding micro elements to the soil as a result of fixation, sedimentation, washing or toxicity, and thus economic loss. The plant needs micro elements in very small quantities that do not burn the leaves or cause poisoning to plants, including iron, zinc and boron, as they are essential elements for growth and completing the plant's life cycle, and increase the plant's resistance to diseases and insects, activate enzymes, and form the chlorophyll molecule, in addition to their role in oxidation and reduction processes and vital processes. The use of fertilizers with their modern technology has made the process of activating seeds or foliar nutrition a matter of interest to researchers as a complementary process t

Mycotoxins are secondary by-products of mold metabolism and are accountable for human and animal mycotoxicosis. The most serious trichothecenic mycotoxin is the fungal T-2 mycotoxin. T-2 mycotoxin impaired nutrient absorption, metabolism, and then, eliciting severe oxidoreductive stress. Diet plays a key role beyond the supply of nutrients in order to promote animal and human health. Organic acids have been commonly used to exert antioxidative stress capacity in the liver and gut ecosystem. This study is planned to explore, the competence of using (X-MoldCid®) during chronic T-2 mycotoxicosis course in rat. Rats were allocated into 4 main groups, (CN-Gr), negative control and was allowed for the free access to the normal rats chow and the

This mini review provides an overview of methods for manufacturing expanded graphite (EGT) and the use of its composites with metal oxides in the field of photodegradation of dyes. Dyes from textile manufacturing represent a significant environmental pollution problem in waterways worldwide, highlighting the need for environmentally friendly and efficient technologies to remove dyes from industrial and local wastewater. Photodegradation technologies offer a low-cost, sustainable solution with minimal secondary pollution. Carbon-based materials, such as expanded graphite, are advantageous in enhancing catalytic activity. Accordingly, this review will explore the different fabrication techniques of expanded graphite and summarize the recent d

The physical and morphological characteristics of porous silicon (PS) synthesized via gas sensor was assessed by electrochemical etching for a Si wafer in diluted HF acid in water (1:4) at different etching times and different currents. The morphology for PS wafers by AFM show that the average pore diameter varies from 48.63 to 72.54 nm with increasing etching time from 5 to 15min and from 72.54 to 51.37nm with increasing current from 10 to 30 mA. From the study, it was found that the gas sensitivity of In2O3: CdO semiconductor, against NO2 gas, directly correlated to the nanoparticles size, and its sensitivity increases with increasing operating temperature.

Tin Oxide (SnO2) films have been deposited by spray pyrolysis technique at different substrate temperatures. The effects of substrate temperature on the structural, optical and electrical properties of SnO2 films have been investigated. The XRD result shows a polycrystalline structure for SnO2 films at substrate temperature of 673K. The thickness of the deposited film was of the order of 200 nm measured by Toulansky method. The energy gap increases from 2.58eV to 3.59 eV when substrate temperature increases from 473K to 673K .Electrical conductivity is 4.8*10-7(.cm)-1 for sample deposited at 473K while it increases to 8.7*10-3 when the film is deposited at 673K

Overall enthalpy and entropy of complex formation were calculated from stability constant measurements at different tempreture also experimental results