The present study evaluates the effects of Ginkgo biloba extract as monotherapy on the glycemic status, insulin resistance (IR), body mass index (BMI), and visceral adiposity index (VAI), in addition to the inflammatory markers, oxidative status and leptin level in patients with metabolic syndrome in comparison with metformin.

The study is a randomized, double-blind pilot study conducted during the period May to September, 2020. Fifty patients were recruited in the study and they were allocated into two groups (25 per each group): Ginkgo biloba and Metformin groups, they received (120 mg Ginkgo biloba extract/ capsule) and (500 mg Metformin/ capsule) respectively; orally as a single dose for 90 days. Blood samples were taken at z

جريت التجربة في اصص فخارية سعة كل اصيص 4 كغم تربة في البيت الزجاجي التابع لقسم علوم الحياة/كلية التربية ابن الهيثـــــــــم/جـامعــة بـغداد لموســم النمـو 2008-2009 لدراســة تأثيــر اربعـــة مستويـــــات من سمــــاد اليوريـــا وهي (0, 0.1, 0.2, 0.4) غم/اصيص والتي تعادل (0, 100, 200, 400) كغم/هكتار وثلاث مستويات من سماد السوبر فوسفات وهي (0, 0.1, 0.2) غم/اصيص والتي تعادل (0, 100, 200) كغم/هكتارفي مكونـات الحاصـــل لنبــات الحلبـــة Trigonella foe

Exposing the dorsal superficial skin of rats to partial-depth burn leads to bacterial and microbes Invasion. Topical treatment is required in most superficial burn cases Moist exposed burn ointment (MEBO) protects wounds from infection and enhances healing without any harmful effects of purified chemicals is caused. The topical using of HA gel in rat models with full and partial thickness surgical wounds shows enhancement in wound repair. In this study, we compared the healing efficacy of topical use of hyaluronic acid gel products with MEBO as standard management in rats that were exposed to a partial-thickness burn. The experiment included twenty-four (24) adult albino rats of male sex with weight (150-220 gm) of 3 months’ age divided i

Study was made on the optical properties of Ge2oSe8othinfilms prepared by vac-uum evaporation as radiated by (0,34,69) Gy of 13 ray.The optical band gab Eg and tailing band A.Et were studied in the photon energy range ( 1 to 3)eV. The a-Ge20Se8o film was found to be indirect gap with energy gap of (1.965,1.9 , 1.82) eV at radiated by B ray with absorption doses of (0,34,69)Gy respectively.The Ea and AEt of Ge20Se80 films showed adecrease in E8 and an increase in AEt with radiation. This be-havior may be related to structural defects and dangling bonds.

ZnS thin films were grown onto glass substrates by flash evaporation technique, the effects of ? – rays on the optical constants of ZnS these films were studied. It was found that ? – rays affected all the parameters under investigation.

Reflection cracking in asphalt concrete (AC) overlays is a common form of pavement deterioration that occurs when underlying cracks and joints in the pavement structure propagate through an overlay due to thermal and traffic-induced movement, ultimately degrading the pavement’s lifespan and performance. This study aims to determine how alterations in overlay thickness and temperature conditions, the incorporation of chopped fibers, and the use of geotextiles influence the overlay’s capacity to postpone the occurrence of reflection cracking. To achieve the above objective, a total of 36 prism specimens were prepared and tested using an overlay testing machine (OTM). The variables considered in this study were the thickness of the

Reflection cracking in asphalt concrete (AC) overlays is a common form of pavement deterioration that occurs when underlying cracks and joints in the pavement structure propagate through an overlay due to thermal and traffic-induced movement, ultimately degrading the pavement’s lifespan and performance. This study aims to determine how alterations in overlay thickness and temperature conditions, the incorporation of chopped fibers, and the use of geotextiles influence the overlay’s capacity to postpone the occurrence of reflection cracking. To achieve the above objective, a total of 36 prism specimens were prepared and tested using an overlay testing machine (OTM). The variables considered in this study were the thickness of the

Conventional flexible pavements are released to different types of failure in the initial phases of their service life due to high traffic density, high speeds, heavy loads, and harsh climates. To eliminate pavement damage and failure early, the present search investigates the impact of adding glass, steel, and basalt fibers in the asphalt mixtures. Also, the study evaluates these materials characteristics compared to the mixtures without fibers. The Marshall test and tensile strength ratio test (TSR) were utilized to evaluate the asphalt mixture's performance. A set of specimens were produced by incorporating glass fiber (GF), steel fiber (SF), and basalt fiber (BF) at (0.10%, 0.15%, 0.20%), (0.25%, 0.35%, 0.45%), and (0.15%, 0.35%