The effects of reinforcing polymers with glass and graphite particles on enhancing their flexural properties are investigated.   Five composites were fabricated using the same polymer matrix material with different volume fractions of reinforcement particles. They comprise glass particles and graphite particles each  having volume fractions of 20% and 30% as well as a hybrid composite having 10% glass and 10% graphite. Three-point bending tests using a Universal Testing Machine were carried out on specimens of the above mentioned composites, as well as specimens of the polymer matrix material to determine their flexural properties. The experimental test results indicate that the flexural stiffness of all the composites wer

In this study, synthesis of polymer Nanocomposites through the blending of prepared polymers with polyvinyl alcohol (a synthetic polymer) or chitosan (a natural polymer) then mixed with nano oxide silica by many steps. The new compound [I] was obtained via reaction of 3,3’-dimethoxybiphenyl-4,4’-diamine as starting material with malic anhydride in DMF then treatment with ammonium persulfate (NH4 )2 S2 O8 (as the initiator) in order to produce polymer [II]. Also, we prepared new polymers [III-V] by using the same starting material (3,3’-dimethoxybiphenyl-4,4’-diamine) with glutaric acid or adipic acid or isophthalic acid in DMF and pyridine. In this study, new polymer blending [VI-IX] and [X-XIII] were synthesized from a prepared pol

    A new chelate polymer (2-5-hydroxy-3-methyl-2- (3-nonyl benzene) imino) methyl) benzyl) 4-6-dimethyphenol] (K4) was prepared by using the condensation reaction method and identified by several techniques, including FT-IR, NMR, and atomic absorption spectroscopy, as well as TG-DTA thermal analysis. The kinetic equilibrium for the sorption of lead and cadmium ions on the chelate polymer surface was also investigated. The results showed that the sorption of both ions followed the pseudo-first-order and pseudo-second-order kinetic equilibrium. The rate constant values of pseudo-first-order reaction  were equal to 0.062 and 0.057 min^-1  , while the values of pseudo-second-order were 0.0103 and 0.053 L.m

PVC/Kaolinite composites were prepared by the melt intercalation method. Mechanical properties, thermal properties, flammability and water absorption percentage of prepared samples were tested. Mechanical characteristic such as tensile strength, elongation at break; hardness and impact strength (charpy type) were measured for all samples. It was found that the tensile strength and elongation at break of PVC composites decreased with increasing kaolinite loading. Also, the hardness of the composites increases with increase in filler content .The impact strength of the composites at the beginning increases at lower kaolinite loadings is due to the lack of kaolin adhesion to the matrix. However, at higher kaolin loadings. This severe agglom

The polymeric hydrogels composed of poly vinyl alcohol (m.wt 72000) and glutaraldehyde(5%,8% and 10%) , have been thermally prepared for the purpose of studying their swelling and drug release behavior . The swelling ratio was measured for all the hydrogel samples at 37°C, in three different media pH (1.2, 4.7 and 6.8) as a function of time. The results show that the maximum swelling ratios were arranged as follows :pH =6.8 > pH =4.7 > pH =1.2 hydrogels cross linked PVA showed a typical pH responsive behavior such as high pH has maximum swelling while low pH shows minimum swelling.

Schiff base of chitosan with Para-Dimethyl aminobenzaldehyde /PVA-Ag Nanocomposite have been prepared as antimicrobial polymer. The prepared chitosan Schiff base and chitosan Schiff base / PVA-Ag nanocomposite were characterized by FT-IR, SEM analysis and biological activity. The nanocomposite showed good activity against different types of bacteria.

In this work, some mechanical properties of the polymer coating were improved by preparing a hybrid system containing Graphene (GR) of different weight percentages (0.25, 0.5, 1, and 2wt%) with 5wt% carbon fibres (CF) and added to a polymer coating by using casting method. The properties were improved as GR was added with further improvement on adding 5wt% of CF. The impact strength of acrylic polymer with GR increases with increasing weight ratio‏‏ of GR; maximum value was obtained when the polymer coating was incorporated with 1wt% GR and 5wt% CF. The impact strength of acrylic polymer with GR and GR/CF composites incorporated with GR at 1wt% and CF at 5wt%. Hardness increase with increasing weight ratio of Gr and a significant imp

     In this work, calcium ions were determined by the addition to the allyl chloride monomer resulting from bulk polymerization formation. To acquire the highest adsorption capacity, molar ratios of the template, monomer, and cross-linking agent, as well as solvents and multiple monomers were investigated. Scanning Electron Microscopy (SEM) and Fourier Transform Infrared Spectroscopy (FTIR) were used to analyze the calcium ion polymer. The elution of calcium had a small effect on the surfaces of the three-dimensional network structure. Calcium (II) ions were successfully eluted using a mixture of methanol and acetic acid. The calcium adsorption capacities were 3.8145 and 9.01773 mol/g (Q_max), respectively. A Langmuir isot

 In the present work polymer electrolytes were formulated using the solvent casting technique. Under special conditions, the electrolyte content was of fixed ratio of polyvinylpyrolidone (PVP): polyacrylonitrile (PAN) (25:75), ethylene carbonate (EC) and propylene carbonate (PC) (1:1) with 10% of potassium iodide (KI) and iodine I₂ = 10% by weight of KI. The conductivity was increased with the addition of ZnO nanoparticles. It is also increased with the temperature increase within the range (293 to 343 K). The conductivity reaches maximum value of about (0.0296 S.cm^-1) with (0.25 g) ZnO. The results of FTIR for blend electrolytes indicated a significant degree of interaction between the polymer blend (PVP and PAN)

     In the present study, pure Poly(viny1 alcohol) (PVA) and  pyromellitic dianhydride (PMDA) cross linked PVA with (0,5,10,15 and 20)wt.% and doped with different molarity (5,9)M of sulfuric acid (H₂SO₄) were prepared by the solution casting method and were characterized as a function of  frequency in the range (1-100) KHz.

     The FT-IR results showed that the strong broad band observed at 3738.05 and 3857.63 cm^-1 may be assigned to O-H stretching due to the strong hydrogen bond of intramolecular and intermolecular type in PVA film.  When PVA is doped with 5M and 9M H₂SO₄,  a new peak was noticed at 813 cm^-1, this peak may be due to the fo