This study involves adding nano materials and interaction with cement mortar behavior for several mortar samples under variable curing time with constant water to cement ratio (W/C = 0.5). The effects of adding nano materials on the microstructure of cement mortar were studied by (Scanning Electronic Microscopy (SEM) and X-Ray (for samples at different curing time 28 and 91 days. Small ratio replacements of nano particles (SiO₂ or Al₂O₃) were added to Ordinary Portland Cement (OPC) type (I). The percentage of nano materials additives replacement by weight of ordinary Portland cement includes (1, 2, 3, 4 and 5%) for both types of nano materials with constant (W/C) ratio, also the amount of the fin

A thin film of (SnSe) and SnSe:Cu with various Cu ratio (0,3,5 and 7)% have been prepared by thermal evaporation technique with thickness 400±20 nm on glass substrate at (R.T). The effect of Cu dopants concentration on the structural, morphological, optical and electrical properties of (SnSe) Nano crystalline thin films was explored by using X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), energy dispersive spectroscopy (EDS), UV–Vis absorption spectroscopy and Hall Effect measurement respectively. X-ray diffraction analysis reveal the polycrystalline nature of the all films deposited with orthorhombic structure which possess a preferred orientation along the (111) plane. The crystalline sizes o

The importance of economic and technical feasibility studies include all of the investor, the society, the banks, the project and the government. As it will assist in achieving the optimal use of the available economic incomes on the national level and arranging the projects in priority which participates in achieving the government benefit without wasting the amounts .This is the research goal So, the research covered its theoretical aspect, of SAIs and the economic and technical feasibility studies then the role of the auditors in auditing those studies Then a mechanism was proposed includes a guidebook that provides guidelines for organizing the process of preparing and auditi

Buffering of Local anaesthesia (LA) has been suggested as a mechanism to improve injection comfort and hasten the onset of anaesthesia. Aim This study aimed to evaluate the effectiveness of buffered LA in the extraction of maxillary premolars and molars. Materials and Methods This randomized controlled study included 100 patients who were indicated for extraction of maxillary posterior teeth, they were randomly divided into two groups; a study group that received infiltration of buffered 2% lidocaine hydrochloride with 1:80,000 epinephrine LA, and a control group that received non-buffered 2% lidocaine hydrochloride with 1:80,000 epinephrine LA. The buffering was performed using the Onset® LA buffering system (Onpharma®). The outcome va

   A new nano-sized NiMo/TiO₂-γ-Al₂O₃ was prepared as a Hydrodesulphurization catalyst for Iraqi gas oil with sulfur content of 8980 ppm, supplied from Al-Dura Refinery. Sol-gel method was used to prepare TiO₂- γ-Al₂O₃ nano catalyst support with 64% TiO_2, 32% Al₂O₃, Ni-Mo/TiO-γ-Al₂O₃ catalyst was prepared under vacuum impregnation conditions to loading metals with percentage 3.8 wt.% and 14 wt.% for nickel and molybdenum respectively while the percentage for alumina, and titanium became 21.7, and 58.61 respectively. The synthesized TiO₂- γ-Al₂O₃ nanocomposites and Ni-Mo /TiO₂

Effect of nano and micro SiO2 particles with different weight percent (2,4,6,8 and 10) %wt on the Interlaminar fracture toughness (GIc) of 16-plies of woven roving glass fiber /epoxy composites prepared by hand lay – up technique were investigated. The specimens were tested using DCB test (mode I).
Area method was used to compute the interlaminar fracture toughness. The results show that, GIc would increase with the increasing in the filler content, the main failure in microcomposites and nanocomposites was delamination in the layers, the delamination reduced with increasing in the filler content.