This paper presents a study (experimentally) for strengthening reinforced concrete (RC) beams with Near-Surface-Mounted (NSM) technique. The use of this technique with CFRP strips or rebars is an efficient technology for increasing the strength for flexure and shear or for repairing damaged reinforced concrete (RC) members. The objective of this research is to study, experimentally, RC beams either repaired or strengthened with NSM CFRP strips and follow their flexural behavior and failure modes. NSM-CFRP strips were used to strengthen three RC beam specimens, one of them was initially strengthened and tested up to failure. Four beam specimens have been initially subjected to preloading to 50% and 80% of ultimate load. Two of the sp

In this study, nanocomposites have been prepared by adding
multiwall carbon nanotubes (MWCNTs) with weight ratios (0, 2, 3,
4, 5) wt% to epoxy resin. The samples were prepared by hand lay-up
method. Influence of an applied load before and after immersion in
sodium hydroxide (NaOH) of normality (0.3N) for (15 days) at
laboratory temperature on wear rate of Ep/MWCNTs
nanocomposites was studied. The results showed that wear rate
increases with increasing the applied load for the as prepared and
immersed samples and after immersion. It was also found that epoxy
resin reinforced with MWCNTs has wear rate less than neat epoxy.
The sample (Ep + 5wt% of MWCNTs) has lower wear rate. The
immersion effect in base so

In this study, the effect of construction joints on the performance of reinforced concrete beams was experimentally investigated. Seven beam specimens, with dimensions of 200×100×1000 mm, were fabricated. The variables were considered including; the location and configuration of the joints. One beam was cast without a joint (Reference specimen), two specimens were fabricated with a one horizontal joint located either at tension, or compression zone. The fourth
beam had two horizontal joints placed at tension, and compression area. The remaining specimens were with one or two inclined joints positioned at the shear span or beam’s mid-span. The specimens were subjected to a monotonic central concentrated loading until the failure. T

This paper is devoted to investigate the effect of burning by fire flame on the behavior and load carrying capacity of rectangular reinforced concrete rigid beams. Reduced scale beam models (which are believed to resemble as much as possible field conditions) were suggested. Five end restrained beam specimens were cast and tested. The specimens were subjected to fire flame temperatures ranging from (25-750) ºC at age of 60 days, two temperature levels of 400ºC and 750ºC were chosen with exposure duration of 1.5 hour. The cast rectangular reinforced concretebeam (2250×375×375 mm) (length× width× height respectively) were subjected to fire. Results indicate remarkable reduction in the ultrasonic pulse velocity and rebound number of

In this study, the mechanical properties of an epoxy and unidirectional woven carbon with fiberglass composite were experimentally investigated. When preparing the composite samples, American Society for Testing and Materials (ASTM)standard was used. Tensile, impact and flexural test were conducted to investigate the mechanical properties of the new produced epoxy Unidirectional Woven Carbon and Epoxy Fiberglass composites. The outcome showed that the strength of the produced samples increased with the increase in the number of unidirectional woven carbon layers added. Two methods were utilized: (1) woven carbon composite with glass fiber (2) woven carbon composite). The two methods of composite were compared with each other.  The resul

Carbon-fiber-reinforced polymer (CFRP) is widely acknowledged as a leading advanced material structure, offering superior properties compared to traditional materials, and has found diverse applications in several industrial sectors, such as that of automobiles, aircrafts, and power plants. However, the production of CFRP composites is prone to fabrication problems, leading to structural defects arising from cycling and aging processes. Identifying these defects at an early stage is crucial to prevent service issues that could result in catastrophic failures. Hence, routine inspection and maintenance are crucial to prevent system collapse. To achieve this objective, conventional nondestructive testing (NDT) methods are utilized to i

Many previous investigations have found quercetin to be a powerful antioxidant and antitumor flavonoid, but its poor bioavailability has limited its use. This current study investigated the effects of two newly synthesized Quercetin Schiff bases containing 2-amino thiadiazole-5-thiol (Q1), and its benzyl derivatives (Q2) on MCF-7 human breast cancer cells. Cell viability and apoptosis were assessed to determine the toxic effects of Q1 and Q2. Cytotoxicity valuation showed that both compounds inhibited MCF-7 cell growth, and lactate dehydrogenase (LDH) activity increased in a dose-dependent aspect compared to the control group. Comet assay results observed that Q1 and Q2 induce more serious DNA damage than the control (untreated cell

Schizophrenia (ZP) is a common devastating cognitive disorder; however, the etiology of its incidence remains largely unclear yet. Although some evidence blames both environ ment and genetic factor as main drivers of ZP, but the clear mechanism of their effect elusive till now. Of interest, severe anemia conditions can lead to hypoxia in CNS which disturbs the normal structures and functions of some area in the brain resulting in abnormalities in the neurons communications and decrease synaptic plasticity. Additionally, modulation of cytoskeleton constituents is thought to participate to ZP development. Recently, it has been revealed that iron deficiency, which is the main cause of anemia, has a significant impact on the cytoskeleton

In the leaves of Olea europaea L. Olive trees an endophytic fungus was discovered. Cladosporium sp. was identified to be the fungus based on its morphological characteristics and nuclear ribosomal DNA ITS sequence analysis and was registered in NCBI as the Cladosporium genus has been registered under the number (0P939922.1) The species was not specified, and it was considered of unknown species after comparing it to global isolates. In comparison to olive leaf extract, Cladosporium sp. including total flavonoid, total phenolic, total terpenoid, and total saponins, Which were 121.9%, 198.1%, 89.13%, and 29.87 % respectively compared to its content in olive leaf extract, which was 61.54 %, 67.88 % , 17.1