Background: Computerized tomography scan can show the detailed anatomy of the nose and paranasal sinuses. The sphenoid sinus is a very important corridor for the skull base because of its central position. This sinus has a great range of variation and can put structures around at risk during surgery. This study aims to examine the variation of the sphenoid sinus, and its relation to other structures around it, in this sample of Iraqi patients. Materials and Methods: CT scans of 122 patients, were obtained, and submitted for examination and measurements, during the period between September 2020 and September 2021. Observation of The sphenoid sinus pneumatization pattern, clival extension, Onodi cell, and lateral pneumatization of SS.

The aim of this study is to understand the effect of addition carbon types on aluminum electrical conductivity which used three fillers of carbon reinforced aluminum at different weight fractions. The experimental results showed that electrical conductivity of aluminum was decreased by the addition all carbon types, also at low weight fraction of carbon black; it reached (4.53S/cm), whereas it was appeared highly increasing for each carbon fiber and synthetic graphite. At (45%) weight fraction the electrical conductivity was decreased to (4.36Scm) and (4.27Scm) for each carbon fiber and synthetic graphite, respectively. While it was reached to maximum value with carbon black. Hybrid composites were investigated also; the results exhibit tha

Superconducting thin films of Bi1.6Pb0.4Sr2Ca2Cu2.2Zn0.8O10 system were prepared by depositing the film onto silicon (111) substrate by pulsed laser deposition. Annealing treatment and superconducting properties were investigated by XRD and four probe resistivity measurement. The analysis reveals the evolution of the minor phase of the films 2212 phase to 2223 phase, when the film was annealed at 820 °C. Also the films have superconducting behavior with transition temperature ≥90K.

The purpose of the International Financial Reporting Standard (IFRS 15) is to determine the basis for reporting useful information to the users of financial reports on the nature, amount, timing and uncertainty about revenues and cash flows arising from a contract with a customer. It is based on specific conditions for recognizing revenue from the contract. When the two parties to the contract or one of them fulfil the performance obligations, specifically after the customer has the ability to exercise control over the product or service that is the subject of the contract. As a result of the failure of the revenue reporting requirements in the Iraqi environment to provide adequate and honestly representative information on the o

Where the accounting system in Iraq is still using many of these accounting practices according to the legal requirements to measure assets and liabilities away from the measurement that results in information representing the economic essence and represent honestly the financial situation and financial performance and future cash flows, and the needs of users of financial reports to useful accounting information adopted The International Accounting Standards Board (IASB) represents the true representation of accounting information in accordance with the concept of economic substance, which is the basis for the preparation and development of international accounting standards, and because accounting is part of the

In this study, composite materials were prepared using unsaturated polyester resin as binder with two types of fillers (sawdust and chopped reeds). The molding method is used to prepare sheets of UPE / sawdust composite and UPE / chopped reeds composite. The mechanical properties were studied including flexural strength and Young's modulus for the samples at normal conditions (N.C). The Commercial wood, UPE and its composite samples were immersed in water for about 30 days to find the weight gain (Mt%) of water for the samples, also to find the effect of water on their flexural strength and Young's modulus. The results showed that the samples of UPE / chopped reeds composite gained highest values of flexural strength (24.

Thin films samples of Bismuth sulfide Bi2S3 had deposited on
glass substrate using thermal evaporation method by chemical
method under vacuum of 10-5 Toor. XRD and AFM were used to
check the structure and morphology of the Bi2S3 thin films. The
results showed that the films with law thickness <700 nm were free
from any diffraction peaks refer to amorphous structure while films
with thickness≥700 nm was polycrystalline. The roughness decreases
while average grain size increases with the increase of thickness. The
A.C conductivity as function of frequency had studied in the
frequency range (50 to 5x106 Hz). The dielectric constant,
polarizability showed significant dependence upon the variation of
thic