Thin films of (Cu2S)100-x( SnS2 )x at X=[ 30,40, &50)]% with thickness (0.9±0.03)µm , had been prepared by chemical spray pyrolysis method on glass substrates at 573 K. These films were then annealed under low pressure of(10-2) mbar ,373)423&473)K for one hour . This research includes , studying the the optical properties of (Cu2S)100-x-(SnS2)x at X=[ 30,40, &50)]% .Moreover studying the effect of annealing on their optical properties , in order to fabricate films with high stability and transmittance that can be used in solar cells. The transmittance and absorbance spectra had been recorded in the wavelength range (310 - 1100) nm in order to study the optical properties . It was found that these films had direct optical band

Background:The demand for esthetic orthodontic appliances is increasing so that the esthetic orthodontic archwires were introduced. This in vitro study was designed to evaluate the surface roughness offiber-reinforced polymer composite (FRPC) archwires compared to coated nickel-titanium (NiTi) archwires immersed in artificial saliva. Materials and Methods:Three types of esthetic orthodontic archwires were used: FRPC (Dentaurum), Teflon coated NiTi (Dentaurum) and epoxy coated NiTi (Orthotechnology). They were round (0.018 inch) in cross section and cut into pieces of 15 mm in length.Forty pieces from each type were divided into four groups; one group was left at a dry condition and the other three groups were immersed in artificial saliva (

Were collected three types of medicinal plants from their natural habitat after Astkhalasalziot volatile manner steam distillation and determine the quality and quantity of vehicles chemical for each of the oils obtained using a technique JC discouraged when you merge oily thyme and lemon grass against bacteria either when using oils in three did not have a different effect

Oil industry played a major role in delineating the course and type o development in both imported and exported Arabic countries alike where its revenues has perform an essential role in forming programs and plans of development on both national and international level in addition to anticipation of future consuming.

Iraq, as an oil producer country with a revenues –based economy depends on oil in building its economy totally including its infrastructure having a the greatest conformed reservoir which make the government budget depends largely on oil revenues where its strategic importance lies in funding all aspects of expenders as it is considered the prime source of foreign currency.  The chall

The assessment of a river water’ quality is an essential procedure of monitor programs and isused to collect basic environmental data. The management of integrated water resources in asustainable method is also necessary to allow future generations to meet their water needs. Themain objective of this research is to assess the effect of the Diyala River on Tigris River waterquality using Geographic Information System (GIS) technique. Water samples have beencollected monthly from November 2017 to April 2018 from four selected locations in Tigris andDiyala Rivers using the grab sampling method. Fourteen parameters were studied which areTurbidity, pH, Dissolved Oxygen, Biological Oxygen Demand, Electrical Conductivity, TotalDissolved Solids,

ABSTRACT:In this paper, Cd10–xZnxS (x = 0.1, 0.3, 0.5) films were deposited by using chemical spray pyrolysis technique, the molar concentration precursor solution was 0.15 M/L. Depositions were done at 350°C on cleaned glass substrates. X-ray dif- fraction technique (XRD) studies for all the prepared film; all the films are crystalline with hexagonal structure .The optical properties of the prepared films were studied using measurements from VIS-UV-IR spectrophotometer at wave- length with the range 300 - 900 nm; the average transmission of the minimum doping ratio (Zn at 0.1%) was about 55% in the VIS region, it was decrease at the increasing of Zn concentration in the CdS films, The band gap of the doped CdS films was varied as 3.7, 3

In this work dithine complexes prepared from dithiol benzil ligand and central ion to the Ni,Pd,Pt, element the ligand and complexes have been investigated using FTIR spectrophotometer and uv-vis-NIR spectral reigns show higher intensity represents the ?-?* transition in the chromopher cycle .These absorption which appear in visible and near IR spectral regions ,According to the complexes of one group ,the spectral shifting due to the change of central ion has been found to be related to atomic number of central ion .This shifting is increased while decreasing the central ion atom number These complexes have been implemented in Nd+2:YAG cavity because each posses resonant absorption band near Nd+2:YAG, Nd+2:Glass emitting at (106

Atmospheric residue fluid catalytic cracking was selected as a probe reaction to test the catalytic performance of modified NaY zeolites and prepared NaY zeolites. Modified NaY zeolites have been synthesized by simple ion exchange methods. Three samples of modified zeolite Y have been obtained by replacing the sodium ions in the original sample with lanthanum and the weight percent added are 0.28, 0.53, and 1.02 respectively. The effects of addition of lanthanum to zeolite Y in different weight percent on the cracking catalysts were investigated using an experimental laboratory plant scale of fluidized bed reactor.

The experiments have been performed with weight hourly space velocity (WHSV) range of 6 to 24 h