This paper investigated the fatigue life behavior of two composite materials subjected to different times of shot peening (2, 4 and 6 min).The first material prepared from unsaturated polyester with E-glass reinforcement by 33% volume fraction. While, the second one was prepared from unsaturated polyester with aluminum powder by2.5% volume fraction. The experimental results showed that the improvement in endurance limit was obtained (for the first material) at 2, 4 and 6 min shot peening times where the percentage of maximum improvement was 25% at shot peening time of 6 min. While, the endurance limit of the second material decreased at shot peening times of 2, 4 and 6 min where the percentage of maximum reduction was 29 % at shot peenin

In this study, an experimental investigation had conducted for six high strength laced reinforced concrete one-way slabs to discover the behavior of laced structural members after being exposed to fire flame (high temperature). Self-compacted concrete (SCC) had used to achieve easy casting and high strength concrete. All the adopted specimens were identical in their compressive strength of ( , geometric layout 2000 750 150 mm and reinforcement specifics except those of lacing steel content, three ratios of laced steel reinforcement of (0.0021, 0.0040 and 0.0060) were adopted. Three specimens were fired with a steady state temperature of  for two hours duration and then after the specimens were cooled suddenly by spraying water. The

The use of composite materials has vastly increased in recent years. Great interest is therefore developed in the damage detection of composites using non- destructive test methods. Several approaches have been applied to obtain information about the existence and location of the faults. This paper used the vibration response of a composite plate to detect and localize delamination defect based on the modal analysis. Experiments are conducted to validate the developed model. A two-dimensional finite element model for multi-layered composites with internal delamination is established. FEM program are built for plates under different boundary conditions. Natural frequencies and modal displacements of the intact and damaged

Background: With the increase in composite material use in posterior teeth, the concerns about the polymerization shrinkage has increased with the concerns about the formation of marginal gaps in the oral cavity environment. New generation of adhesives called universal adhesive have been introduced to the market in order to reduce the technique sensitive bonding procedures to give the advantage of using the bonding system in any etching protocol without compromising the bonding strength. The aim of the study was to study marginal adaptation of two universal adhesives (Single bondâ„¢ Universal and Prime and Bond elect) using 3 etching techniques under thermal cycling aging. Materials and Methods: Forty-eight sound maxillary first premola

The inhibitive action of polyvinyl alcohol –sodium nitrite (PVASN) composite on the corrosion of mild steel in simulated cooling water (SCW) has been investigated by weight loss and potentiodynamic polarization. The effect of composite concentration (PVA/SN) , pH, and exposure time on corrosion rate of mild steel were verified using 2 levels factorial design and surface response analysis through weight loss approach, while the electrochemical measurements were used to study the behavior of mild steel in (SCW) with pH between 6 and 8 and in absence and presence of (PVA) in solution containing different concentration of NaNO2. It was verified that all three main variables studied were statistically significant while their interaction is

Cubosomes are nanosized structures self-assembled nanostructured materials used for controlling the release of the entrapped drug molecule. Lornoxicam (LXM) is a potent analgesic nonsteroidal anti-inflammatory (NSAID) drug with a short half-life (3-4) hours. The present study aims to prepare LXM-loaded cubosomes with well-defined morphology, particle size, PDI, high entrapment efficiency, sustained drug release, and high zeta potential value, as a transdermal drug delivery system.

      Twelve formulas of LXM-loaded cubosomal dispersions were prepared by a solvent dilution method using Glyceryl monooleate ( GMO) as polar lipid with different stabilizers as Pluronic® F127 or tween 80 and different types o

Anastrozole (ANZ) is considered constitute of the fourth –generation of Non–steroidal aromatase blockage, ANZ has use for hormone receptor positive breast cancer in postmenopausal women. The serious side effects of ANZ including, vaginal dryness, hot flashes, irritability, breast tenderness and un–stability in circulation.

Nanostructured lipid carriers (NLCs) have recently emerged as a multifunctional platform for drug delivery in cancer therapy.

Five formula were composed of (200 mg of glyceryl monostearate, 40 mg of oleic acid , 1% (w/w) Tween 80, 1% (w/w) Poloxamer 407, 1% (w/w) soy lecithin and Vitamin E Polyethylene Glycol Succinate.

The mean particle size, polydispersity index, zeta potential, entrapme