Chemical resistance ceramic tiles and mortar to alkali solution are prepared and characterized in this study due to the lack of this kind of publications in ceramic literature. Most of the utilized materials are readily available raw materials and the other materials are available commercially. Physical and mechanical properties are measured and indicate that the prepared ceramic tile and mortars are competitive to traditional building materials. Chemical resistance test against alkali solution is also performed by subjecting test specimens to 10%NaOH liquid for two weeks. The results give no indication of chemical attack to specimens of ceramic tile and mortar. The results are discussed and important conclusions are drawn to encourage c

The composites were manufactured and study the effect of addition of filler (nanoparticles SiO2 treated with silane) at different weight ratios (1, 2, 3, 4 and 5) %, on electrical, mechanical and thermal properties. Materials were mixed with each other using an ultrasound, and then pour the mixture into the molds to suit all measurements. The electrical characteristics were studied within a range of frequencies (50-1M) Hz at room temperature, where the best results were shown at the fill ratio (1%), and thermal properties at (X=3 %), the mechanical properties at the filler ratio (2%).

In this research, the effect of adding two different types of reinforcing particles was investigated, which included: nano-zirconia (nano-ZrO₂) particles and micro-lignin particles that were added with different volume fractions of 0.5%, 1%, 1.5% and 2% on the mechanical properties of polymer composite materials. They were prepared in this research, as a complete prosthesis and partial denture base materials was prepared, by using cold cure poly methyl methacrylate (PMMA) resin matrix. The composite specimens in this research consist of two groups according to the types of reinforced particles, were prepared by using casting methods, type (Hand Lay-Up) method. The first group consists of PMMA resin reinforced by (nano-ZrO

Abstract

     In this investigation, Al₂O₃ nano material of 50nm particles size were added to the 6061 Al aluminium alloy by using the stir casting technique to fabricate the nanocomposite of 10wt% Al₂O₃. The experimental results observed that the addition of 10wt% Al₂O₃ improved the fatigue life and strength of constant and cumulative fatigue. Comparison between the S-N curves behaviour of metal matrix (AA6061) and the nanocomposite 10wt% Al₂O₃ has been made. The comparison revealed that 12.8% enhancement in fatigue strength at 10⁷cycles due to 10wt% nano reinforcement. Also cumulative fatigue l

Magnesium aluminum silicate of glass ceramic having different amounts of magnesium fluoride in the range (0-13.2)%. Thermal expansion coefficient and micro hardness of the base glass and glass ceramic samples are seen to be interdependent but due to the multi – component system, the behaviour is seen to be somewhat complex, with an increase in Mg F2 content. The thermal expansion coefficient increase and micro harness decrease, numerical simulation of thermal expansion and hardness is useful in this study, L2 – regression is used to calculate the two parameters associated with each glass component, by comparing the measured parameters and the calculated parameters ,it is useful to use such a method to calculate the quantity

   This work was carried out to investigate the shrinkage properties of insulator ceramic body, and the effect of changing the ratio of concentration of electrolyte solution on these properties. The electrical insulator body was prepared by using Iraqi local materials. These are :- kaolin Duakhla, Arudhuma Sand glass, and potash feldspar with weight percentage (45%, 25%,and 30%) respectively. The processes of milling, classification, mixing, forming and firing, through the process of mixing electrolyte solution and mineralizer were added at different concentrations for electrolyte solution, (1%, 0.7%, 0.5%, 0.2%, and 0.1%).  The electrolyte solution was prepared by mixing sodium carbonate and sodium silicate by (2:1) ratio

   This study included preparation for the unsaturated polyester samples before and after reinforced by the Alumina oxide powder of different volume fraction amounting (2%,4%,6%).    And this research included the study of some of mechanical properties such as (Hardness,compressive,wear).     The results showed that the increase of the hardness and compressive strength after the reinforced and the increase with the volume fraction increase.   As the wear test shows that the wear rate increases with applied load increase(5,10,15) from  (10.6-18.6) gm/cm befor reninforced and from(5.4-15.2)gm/cm,(4.7-12.9)gm/cm,(48.1)gm/cm,after reinforced from the different volume fraction, and t

Refractories are mineral and chemical-, based, materials with excellent heat resistance, making them ideal for use in the construction of ovens, furnace walls industries. According to this our research is concerned to study the effect of addition of (4% CaO) and (5% graphite) on the silica brick properties. Different amounts of CaO and Graphite were included in the white sand (raw ingredients) of silica bricks as a binder to prepare the composition then the composition were sintered using Different sintering temperatures ranging from (1000–1400)𝛐C under static air. Density, thermal conductivity, porosity, and water absorption Compression there was power tested after sintering. XRD analysis was used to identify raw materials’