New types of hydrodesulfurization (HDS) catalyst Re-Ni-Mo/ γ-Al₂O₃ was prepared and tested separately with two prepared conventional HDS catalysts (Ni-Mo/ γ-Al₂O₃ and Co-Mo//γ-Al₂O₃) by using a pilot plant hydrotreatment unit. Activities of three prepared hydrodesulfurization catalysts were examined in hydrodesulfurization (HDS) of atmospheric gas oil at different temperatures 275 to 350 °C and LHSV 1 to 4 h^-1, the reactions conducted under constant pressure 40 bar and H₂/HC ratio 500 ml/ml .Moreover, the hydrogenation of aromatic (HAD) in gas oil has been studied. HDS was much improved by adding promoter Re to the Ni-Mo/Al₂O₃

New types of hydrodesulfurization (HDS) catalyst Re-Ni-Mo/ γ-Al2O3 was prepared and tested separately with two prepared conventional HDS catalysts (Ni-Mo/ γ-Al2O3 and Co-Mo//γ-Al2O3) by using a pilot plant hydrotreatment unit. Activities of three prepared hydrodesulfurization catalysts were examined in hydrodesulfurization (HDS) of atmospheric gas oil at different temperatures 275 to 350 °C and LHSV 1 to 4 h-1, the reactions conducted under constant pressure 40 bar and H2/HC ratio 500 ml/ml .Moreover, the hydrogenation of aromatic (HAD) in gas oil has been studied. HDS was much improved by adding promoter Re to the Ni-Mo/Al2O3 catalyst. The results showed that Re-Ni-Mo/ γ-Al2O3 have more activity in desulfurization than Ni-Mo//γ-Al2O3

New types of hydrodesulfurization (HDS) catalyst Re-Ni-Mo/ γ-Al2O3 was prepared and tested separately with two prepared conventional HDS catalysts (Ni-Mo/ γ-Al2O3 and Co-Mo//γ-Al2O3) by using a pilot plant hydrotreatment unit. Activities of three prepared hydrodesulfurization catalysts were examined in hydrodesulfurization (HDS) of atmospheric gas oil at different temperatures 275 to 350 °C and LHSV 1 to 4 h-1, the reactions conducted under constant pressure 40 bar and H2/HC ratio 500 ml/ml .Moreover, the hydrogenation of aromatic (HAD) in gas oil has been studied. HDS was much improved by adding promoter Re to the Ni-Mo/Al2O3 catalyst. The results showed that Re-Ni-Mo/ γ-Al2O3 have more activity in desulfurization than Ni-Mo//

In this study, gold nanoparticle samples were prepared by the chemical reduction method (seed-growth) with 4 ratios (10, 12, 15 and 18) ml of seed, and the growth was stationary at 40 ml. The optical and structural properties of these samples were studied. The 18 ml seed sample showed the highest absorbance. The X- ray diffraction (XRD) patterns of these samples showed clear peaks at (38.25^o, 44.5^o, 64.4^o, and 77.95^o). The UV-visible showed that the absorbance of all the samples was in the same range as the standard AuNPs. The field emission-scanning electron microscope (FE-SEM) showed the shape of AuNPs as nanorods and the particle size between 30-50 nm. Rhodamine-610 (RhB) was prepared at 10<

Preparation and Characterization of Maleate, Tartarate,and Phthalate Modified Pectin

In this study we examine variations in the structure of perovskite compounds of LaBa2Cu2O9, LaBa2CaCu3O12 and LaBa2Ca2Cu5O15 synthesized using the solid state reaction method. The samples’ compositions were assessed using X-ray fluorescence (XRF) analysis. The La: Ba: Ca: Cu ratios for samples LaBa2Cu2O9, LaBa2CaCu3O12 and LaBa2Ca2Cu5O15 were found by XRF analysis to be around 1:2:0:2, 1:2:1:3, and 1:2:2:5, respectively. The samples’ well-known structures were then analyzed using X-ray diffraction. The three samples largely consist of phases 1202, 1213, and 1225, with a trace quantity of an unknown secondary phase, based on the intensities and locations of the diffraction peaks. According to the measured parameters a, b, and c, every sa

In this work, Pure and Cu: doped titanium dioxide nano-powder was prepared through a solid-state method. the dopant concentration [Cu/TiO₂ in atomic percentage (wt%)] is derived from 0 to 7 wt.%. structural properties of the samples performed with XRD revealed all nanopowders are of titanium dioxide having polycrystalline nature. Physical and Morphological studies were conducted using a scanning electronic microscope SEM test instrument to confirm the grain size and texture. The other properties of samples were examined using an optical microscope, Lee's Disc, Shore D hardness instrument, Fourier-transform infrared spectroscopy (FTIR), and Energy-dispersive X-ray spectroscopy (EDX). Results showed that the thermal conductivity